Trans-Endodontic Zirconium Oxide Implants: A Clinical Alternative / Implantes trans-endodónticos de óxido de zirconia: Una alternativa clínica

Abstract 24. Dental trauma, mainly from the anterior area of the mouth in the incisor teeth at the level of the radicular third, has the extraction of the dental organ as an elective treatment, depending on the severity of the lesion and the site where it presented. This paper reports two cases: one in a young 13-year-old male patient with dental trauma in central incisors, and another in an 18-year-old female patient with radicular reabsorption in central incisors. Both were treated using trans-endodontic implants on teeth 2.1 and 1.1-2.2 each case, respectively. The treatment approach proposed for each case provided good functional and esthetic outcomes. Clinical and radiographic results after 1 year were successful.

Resumen 28. El traumatismo dental del área anterior de la boca en los dientes incisivos a nivel del tercio radicular, indica la extracción del órgano dental como un tratamiento electivo dependiendo de la gravedad de la lesión y el sitio donde se presentó. Este artículo reporta dos casos: uno en un paciente masculino joven de 13 años con trauma dental en los incisivos centrales y otro en una paciente de 18 años con reabsorción radicular en los incisivos centrales. Ambos fueron tratados con implantes trans-endodónticos en los dientes 2.1 y 1.1-2.2 en cada caso, respectivamente. El enfoque de tratamiento propuesto para cada caso proporcionó buenos resultados funcionales y estéticos. Los resultados clínicos y radiográficos después de 1 año fueron exitosos.

Chemical and Microscopy Characterization of Trans-Endodontic Implants / Caracterización química y microscópica de implantes trans-endodónticos

Abstract Trans-endodontic implants are an artificial extension through root apex anchored in periradicular bone tissue. The aim is to improve the crown-root ratio and to provide stability to dental organ present. Zirconium oxide (ZrO2) is a material of great technological importance, having good natural color, high strength, high toughness, high chemical stability, does not suffer any corrosion, chemical and microbial resistance and excellent esthetic properties. Objective: The aim of this study was to evaluate chemical and microscopy of surface conditions of ZrO2 trans-endodontic implant. Materials and Methods: A blocks of ZrO2 were manufactured for produce trans-endodontic implants and divided in two groups: monoclinic and tetragonal phase. They were evaluated using Scanning Electroning Microscope (SEM), EnergyDispersive X-ray Spectroscopy (EDS), and Atomic Force Microscope (AFM) and Vickers Micro hardness. Results: The Monoclinic phase through AFM analysis showed roughness Ra = 0.320μm, whereas in the Tetragonal phase was 0.126μm, SEM/EDX indicated that the phases are not properly uniform and the addition of the Yttrium to favor the stabilization of the Tetragonal phase. The Vickers hardness analysis showed a value of 1500HV. Conclusion: The characterization of the surface of trans-endodontic zirconium oxide implants provides a guideline to know the surface characteristics of the material, since a greater roughness on the surface of the implant will favor the Osseo-integration capacity.

Resumen Los implantes trans-endodónticos son una extensión artificial a través del ápice radicular anclado en el tejido óseo periradicular. El objetivo es mejorar la relación corona-raíz y proporcionar estabilidad al órgano dental presente. El óxido de zirconio (ZrO2) es un material de gran importancia tecnológica, con buen color natural, alta resistencia, alta tenacidad, alta estabilidad química, no sufre corrosión, resistencia química y microbiana y excelentes propiedades estéticas. Objetivo: El objetivo de este estudio fue evaluar las condiciones superficiales de ZrO2 para su aplicación clínica a los implantes transendodónticos. Materiales y Métodos: se trituraron bloques de ZrO2 en implantes trans-endodónticos y se dividieron en: monoclínico y tetragonal. Luego se evaluaron mediante microscopía electrónica de barrido (SEM), espectroscopia de rayos X de energía dispersiva (EDS) y microscopio de fuerza atómica (AFM) y microdureza vickers. Resultados: La fase monoclínica a través del análisis AFM presenta Ra = 0.320 μm, mientras que en la fase Tetragonal es 0.126 μm, SEM / EDS muestra que las fases no son adecuadamente uniformes y la adición del Ytrio para favorecer la estabilización de la fase tetragonal. El análisis de microdureza mostro un valor de 1500HV. Conclusión: La caracterización de la superficie de los implantes trans-endodónticos de óxido de zirconio, brinda una pauta para conocer las características superficiales del material, ya que al haber una mayor rugosidad en la superficie del implante se verá favorecida la capacidad de oseointegración.