Urea incorporated into ordered mesoporous silica for potential cosmetic application
Braz. J. Pharm. Sci. (Online)
; 56: e17560, 2020. tab, graf
Article
in En
| LILACS
| ID: biblio-1285514
Responsible library:
BR40.1
Localization: BR40.1
ABSTRACT
Urea's thermal instability and burning on sensitive skin can cause problems for cosmetic formulations. To overcome these drawbacks, urea was incorporated into ordered mesoporous silica (SBA-15). SBA-15 was synthesized using tetraethyl orthosilicate and Pluronic® P123 in an acid medium. Urea (20 wt.%) was incorporated into calcined SBA-15 by the incipient wetness impregnation method. Several techniques were used to characterize the samples. Skin hydration and transepidermal water loss were measured using Corneometer® CM 825 PC and Tewameter® 300 TM. Results showed that the structural properties of SBA-15Urea were similar to pure SBA-15, indicating that SBA-15 remained structured even after urea incorporation. Nitrogen physisorption data showed the volume and surface area of the pores in SBA-15Urea were much lower than those in SBA-15, demonstrating that urea was deposited inside the mesopores. In vivo moisturization studies revealed that SBA-15Urea was not able to reduce transepidermal water loss compared to the other products and control, while forming a non-occlusive surface film on the skin. We conclude that incorporation of urea in the pores of the inorganic SBA-15 matrix is a promising approach to enhancing its stability and providing a prolonged moisturizing effect.
Key words
Full text:
1
Index:
LILACS
Main subject:
Urea
/
Silicon Dioxide
Language:
En
Journal:
Braz. J. Pharm. Sci. (Online)
Journal subject:
Farmacologia
/
Teraputica
/
Toxicologia
Year:
2020
Type:
Article