An Intensity-Demodulated Fiber-Optic Magnetometer Based on Nanostructured Magnetic Fluid-Filled Fluidic Photonic Crystal Fibers.

An intensity-demodulated fiber-optic magnetometer is proposed and experimentally investigated, which is fabricated via fusion splicing a segment of photonic crystal fiber (PCF) between single-mode fibers (SMFs), with the cladding air holes of PCF filled with magnetic fluid. Using the magneto-optical properties of the magnetic fluid, the transmission spectrum is changed with an external magnetic field. Based on the intensity variations in the transmission spectrum, the magnetic field is detected, and a sensitivity of 0.238 dB/mT is obtained at 1550.03 nm with the length of PCF 5.5 cm. By converting light signals into electrical signals, a sensitivity of 0.003 V/mT is achieved. The fiber-optic magnetometer possesses the advantages of simple fabrication, compact/robust structure, and low cost.

A Co-Sputtering Process Optimization for the Preparation of FeGaB Alloy Magnetostrictive Thin Films.

A co-sputtering process for the deposition of Fe0.8Ga0.2B alloy magnetostrictive thin films is studied in this paper. The soft magnetic performance of Fe0.8Ga0.2B thin films is modulated by the direct-current (DC) sputtering power of an FeGa target and the radio-frequency (RF) sputtering power of a B target. Characterization results show that the prepared Fe0.8Ga0.2B films are amorphous with uniform thickness and low coercivity. With increasing FeGa DC sputtering power, coercivity raises, resulting from the enhancement of magnetism and grain growth. On the other hand, when the RF sputtering power of the B target increases, the coercivity decreases first and then increases because of the conversion of the films from a crystalline to an amorphous state. The lowest coercivity of 7.51 Oe is finally obtained with the sputtering power of 20 W for the FeGa target and 60 W for the B target. Potentially, this optimization provides a simple way for improving the magnetoelectric coefficient of magnetoelectric composite materials and the sensitivity of magnetoelectric sensors.

Highly sensitive flexible heat flux sensor based on a microhole array for ultralow to high temperatures.

With the growing demand for thermal management of electronic devices, cooling of high-precision instruments, and biological cryopreservation, heat flux measurement of complex surfaces and at ultralow temperatures has become highly imperative. However, current heat flux sensors (HFSs) are commonly used in high-temperature scenarios and have problems when applied in low-temperature conditions, such as low sensitivity and embrittlement. In this study, we developed a flexible and highly sensitive HFS that can operate at ultralow to high temperatures, ranging from -196 °C to 273 °C. The sensitivities of HFSs with thicknesses of 0.2 mm and 0.3 mm, which are efficiently manufactured by the screen-printing method, reach 11.21 µV/(W/m2) and 13.43 µV/(W/m2), respectively. The experimental results show that there is a less than 3% resistance change from bending to stretching. Additionally, the HFS can measure heat flux in both exothermic and absorptive cases and can measure heat flux up to 25 kW/m2. Additionally, we demonstrate the application of the HFS to the measurement of minuscule heat flux, such as heat dissipation of human skin and cold water. This technology is expected to be used in heat flux measurements at ultralow temperatures or on complex surfaces, which has great importance in the superconductor and cryobiology field.

Design of High-Precision Parallel AWG Demodulation System.

Here, we present a high-precision demodulation method that supports the arrayed waveguide grating (AWG) system, which includes a 1 × 8 AWG as the primary filter with a 0.5 nm channel spacing and a 1 × 4 AWG as the auxiliary filter with a 1 nm channel spacing. The high precision is achieved through an innovative method of decoupling three channels, involving two adjacent channels of the primary filter and one channel of the secondary auxiliary filter. Simulation results show that the AWGs have a good transmission spectrum with crosstalk below -24.8 dB, non-uniformities below 0.8 dB, insertion loss below -3.7 dB, 3 dB bandwidth of 0.25 nm, and 10 dB bandwidth of 0.43 nm. The interrogation precision can reach 8 pm, with a dynamic range of 0.4 nm, corresponding to a single FBG.

High-Linearity Wireless Passive Temperature Sensor Based on Metamaterial Structure with Rotation-Insensitive Distance-Based Warning Ability.

A wireless passive temperature sensor based on a metamaterial structure is proposed that is capable of measuring the temperature of moving parts. The sensor structure consists of an alumina ceramic substrate with a square metal double split-ring resonator fixed centrally on the ceramic substrate. Since the dielectric constant of the alumina ceramic substrate is temperature sensitive, the resonant frequency of the sensor is altered due to changes in temperature. A wireless antenna is used to detect the change in the resonant frequency of the sensor using a wireless antenna, thereby realizing temperature sensing operation of the sensor. The temperature sensitivity of the sensor is determined to be 205.22 kHz/°C with a strong linear response when tested over the temperature range of 25-135 °C, which is evident from the R2 being 0.995. Additionally, the frequency variation in this sensor is insensitive to the angle of rotation and can be used for temperature measurement of rotating parts. The sensor also has a distance warning functionality, which offers additional safety for the user by providing early warning signals when the heating equipment overheats after operating for extended durations.

Evolution of Thermoelectric Generators: From Application to Hybridization.

Considerable thermal energy is emitted into the environment from human activities and equipment operation in the course of daily production. Accordingly, the use of thermoelectric generators (TEGs) can attract wide interest, and it shows high potential in reducing energy waste and increasing energy recovery rates. Notably, TEGs have aroused rising attention and been significantly boosted over the past few years, as the energy crisis has worsened. The reason for their progress is that thermoelectric generators can be easily attached to the surface of a heat source, converting heat energy directly into electricity in a stable and continuous manner. In this review, applications in wearable devices, and everyday life are reviewed according to the type of structure of TEGs. Meanwhile, the latest progress of TEGs' hybridization with triboelectric nanogenerator (TENG), piezoelectric nanogenerator (PENG), and photovoltaic effect is introduced. Moreover, prospects and suggestions for subsequent research work are proposed. This review suggests that hybridization of energy harvesting, and flexible high-temperature thermoelectric generators are the future trends.

Flexible thin film thermocouples: From structure, material, fabrication to application.

Flexible thin-film thermocouples (TFTCs) have been garnering interest as temperature sensors due to the advantages of being flexible, ultrathin, and ultralight. Additionally, they have fast response times and enable detection of temperature. These properties have made them suitable for applications such as wearable electronics, healthcare, portable personal devices, and smart detection systems. This review presents the progress in the development of flexible TFTCs. The mechanism, structural design, materials, fabrication methods, and related applications of flexible TFTCs are also elaborated. Finally, future development directions of flexible TFTCs are discussed such as wide-range temperature measurement, multiple sensor integration, and achieving reliable cold-end compensation systems.

Ag Nanoparticle-Thiolated Chitosan Composite Coating Reinforced by Ag-S Covalent Bonds with Excellent Electromagnetic Interference Shielding and Joule Heating Performances.

Conductive composite coatings are an important element in flexible electronics research and are widely used in energy transformation, artificial intelligence, and electronic skins. However, the comparatively low electrical conductivity limits their performance in many specific applications, such as electromagnetic interference (EMI) shielding and Joule heating devices. Therefore, the preparation of ultrahigh-electrical conductivity composite coatings with good flexibility and durability remains a great challenge. Herein, we fabricated multifunctional conductive composite coatings based on thiolated chitosan (TCS) and Ag nanoparticles (AgNPs) by an eco-friendly drop-coating method. The three-dimensional conductive network constructed by thermal sintering imparted the coating with an ultrahigh electrical conductivity of up to 67079.4 S/m. Moreover, the coating reinforced by Ag-S covalent bonding exhibits good stability, including heat resistance, chemical resistance, and mechanical stability. In addition, based on the ultrahigh electrical conductivity, the coating exhibits superior EMI shielding effectiveness and Joule heating capability. With 30 wt % of AgNPs in the coating, the EMI shielding effectiveness of the coating reaches 70.2 dB, far exceeding commercial standards. Additionally, the coating can quickly reach a saturation temperature (Ts) of 195.9 °C at a safe drive voltage of 3 V. These excellent performances demonstrate that the robust and flexible highly conductive composite coatings prepared by this method have attractive potential for EMI shielding and thermal management applications as well as in wearable electronics.

Exploring the nonlinear piezoresistive effect of 4H-SiC and developing MEMS pressure sensors for extreme environments.

Microelectromechanical system (MEMS) pressure sensors based on silicon are widely used and offer the benefits of miniaturization and high precision. However, they cannot easily withstand high temperatures exceeding 150 °C because of intrinsic material limits. Herein, we proposed and executed a systematic and full-process study of SiC-based MEMS pressure sensors that operate stably from -50 to 300 °C. First, to explore the nonlinear piezoresistive effect, the temperature coefficient of resistance (TCR) values of 4H-SiC piezoresistors were obtained from -50 to 500 °C. A conductivity variation model based on scattering theory was established to reveal the nonlinear variation mechanism. Then, a piezoresistive pressure sensor based on 4H-SiC was designed and fabricated. The sensor shows good output sensitivity (3.38 mV/V/MPa), accuracy (0.56% FS) and low temperature coefficient of sensitivity (TCS) (-0.067% FS/°C) in the range of -50 to 300 °C. In addition, the survivability of the sensor chip in extreme environments was demonstrated by its anti-corrosion capability in H2SO4 and NaOH solutions and its radiation tolerance under 5 W X-rays. Accordingly, the sensor developed in this work has high potential to measure pressure in high-temperature and extreme environments such as are faced in geothermal energy extraction, deep well drilling, aeroengines and gas turbines.

Numerical Investigation of GaN HEMT Terahertz Detection Model Considering Multiple Scattering Mechanisms.

GaN high-electron-mobility transistor (HEMT) terahertz (THz) detectors have been widely studied and applied in the past few decades. However, there are few reports about the influence of GaN/AlGaN heterostructure material properties on the detection model at present. In this paper, a response voltage model for a GaN HEMT THz detector that considers the carrier scattering in a GaN/AlGaN heterostructure is proposed. The phonon scattering, dislocation scattering, and interface roughness scattering mechanisms are taken into account in the classic THz response voltage model; furthermore, the influence of various material parameters on the response voltage is studied. In a low-temperature region, acoustic scattering plays an important role, and the response voltage drops with an increase in temperature. In a high temperature range, optical phonon scattering is the main scattering mechanism, and the detector operates in a non-resonant detection mode. With an increase in carrier surface density, the response voltage decreases and then increases due to piezoelectric scattering and optical phonon scattering. For dislocation and interface roughness scattering, the response voltage is inversely proportional to the dislocation density and root mean square roughness (RMS) but is positively related to lateral correlation length. Finally, a comparison between our model and the reported models shows that our proposed model is more accurate.

An ultrasensitive and stretchable strain sensor based on a microcrack structure for motion monitoring.

Flexible strain sensors are promising candidates for intelligent wearable devices. Among previous studies, although crack-based sensors have attracted a lot of attention due to their ultrahigh sensitivity, large strain usually causes fractures in the conductive paths. Because of the unstable crack structure, the tradeoff between sensitivity and workable strain range is still a challenge. As carbon nanotubes (CNTs) and silver nanowires (AgNWs) can form a strong interface with the thermoplastic substrate and strengthen the conductive network by capillary force during water evaporation, CNTs and AgNWs were deposited on electrospun TPU fiber mats via vacuum-assisted filtration in this work. The prestretching treatment constructed a microcrack structure that endowed the sensor with the combined characteristics of a wide working range (0~171% strain), ultrahigh sensitivity (a gauge factor of 691 within 0~102% strain, ~2 × 104 within 102~135% strain, and >11 × 104 within 135~171% strain), a fast response time (~65 ms), small hysteresis, and superior durability (>2000 cycles). Subsequently, the sensing mechanism of the sensor was studied. Distributed microcrack propagation based on the "island-bridge" structure was explained in detail, and its influence on the strain-sensing behavior of the sensor was analyzed. Finally, the sensor was assembled to monitor various vibration signals and human motions, demonstrating its potential applications in the fields of electronic skin and human health monitoring.

A flexible and wearable NO2 gas detection and early warning device based on a spraying process and an interdigital electrode at room temperature.

Flexible sensors used to detect NO2 gas generally have problems such as poor repeatability, high operating temperature, poor selectivity, and small detection range. In this work, a new spraying platform with a simple structure, low cost, and good film-forming consistency was designed and built to make a sensitive film (rGO/SnO2) for NO2 gas sensors. The relationship between the solid content of rGO and SnO2 nanoparticles, annealing temperature, and sensor performance was studied. The results show that the interdigital electrode-sensitive film formed by spraying 0.25 ml of a 0.4 wt% rGO/SnO2 mixture and annealing at 250 °C exhibited the best comprehensive performance for NO2 detection. The sensor's response value for 100 ppm NO2 gas was 0.2640 at room temperature (25 °C), and the response time and recovery time were 412.4 s and 587.3 s, respectively. In the range of 20-100 ppm, the relationship between the response and NO2 concentration was linear, and the correlation coefficient was 0.9851. In addition, a soft-monitoring node module with an overlimit warning function for NO2 gas was designed and manufactured based on flexible electronics. Finally, the flexible sensor and node module were embedded into woven fabric that could be used to make a mask or a watch that could detect NO2 gas, realizing the practical application of flexible NO2 gas sensors in the field of wearable electronics.

Finger Bending Sensing Based on Series-Connected Fiber Bragg Gratings.

Smart wearable devices are occupying an increasingly important position in scientific research and people's life fields. As an indispensable component of smart wearable devices, sensors play a crucial role in their sensing and feedback capabilities. In this paper, we investigate the bending gesture sensing for the most dexterous part of human anatomy, the finger. Based on series-connected fiber Bragg gratings (FBGs), recognition of finger bending posture is achieved by MATLAB modeling and the cubic spline interpolation.

Simultaneous Measurement of Temperature and Refractive Index Using Michelson Interferometer Based on Waist-Enlarged Fiber Bitaper.

An all-fiber temperature and refractive dual-parameter-sensing Michelson interferometer is designed based on the waist-enlarged bitaper. At 5 mm from the fiber end, the waist-enlarged bitaper is manually spliced and the probe is formed. Since the input light encounters the waist-enlarged bitaper, it will excite high-order modes to transmit in the fiber cladding, and there will be an optical path difference between the basic mode and the higher-order mode. The light transmitted in the core and cladding is reflected upon encountering the fiber end face and the interference occurs due to the optical path difference between basic mode and higher-order mode. Changes in temperature and refractive index at the fiber probe can be detected by monitoring the interference fringes. The refractive response sensitivity is -191.06 dBm/RIU from 1.351 RIU to 1.4027 RIU, and the temperature response sensitivity is 0.12 nm/°C from 11 °C to 98 °C. Through the sensitivity matrix equation, the superimposed refractive index and temperature signals can be effectively demodulated. The sensor has the advantages of multi-parameter measurement, compact structure, low cost, easy fabrication and high reliability.

High Sensitivity Optical Fiber Mach-Zehnder Refractive Index Sensor Based on Waist-Enlarged Bitaper.

A Mach-Zehnder fiber optic sensor with high refractive index response sensitivity was developed. By fabricating a waist-enlarged bitaper structure on the interference arm of a single mode-multimode-single mode (SMS) Mach-Zehnder interferometer (MZI), the spectral contrast and response sensitivity were improved. Subsequently, the response sensitivity was further improved by etching the interference arm. When a beam of light was introduced into the sensor, due to the structural mismatch between the multimode fiber and the normal transmission light, the difference between the low-order mode and the high-order mode was generated in the fiber core and the fiber cladding. In the process of transmission in the sensing arm, due to the different refractive indices of the core and cladding, the optical path difference of the high-order mode and the low-order mode was different, which eventually generated interference fringes. The experimentally measured response sensitivity of SMS MZI in the range of 1.351 RIU to 1.402 RIU is 57.623 nm/RIU; the response sensitivity of a single mode-multimode-bitaper-multimode-single mode (SMBMS) MZI is 61.607 nm/RIU; and the response sensitivity of the etched SMBMS (ESMBMS) MZI is 287.65 nm/RIU. The response sensitivity of the new ESMBMS MZI is three times higher than that of the original SMS MZI. The sensor has the characteristics of compact structure, high sensitivity, easy manufacture, and a wide range of refractive index measurements, and can be used in food processing, pharmaceutical manufacturing and other fields.

Influences of RF Magnetron Sputtering Power and Gas Flow Rate on a High Conductivity and Low Drift Rate of Tungsten-Rhenium Thin-Film Thermocouples.

Thin-Film Thermocouples (TFTCs) are characterized by their high spatial resolutions, low cost, high efficiency and low interference on the air flow. However, the thermal stability of TFTCs should be further improved for application since their accuracy is influenced by joule heat and temperature time drift. In this paper, 3D molecular dynamics and finite element analysis are used for structural design. The effects of RF magnetron sputtering power and gas flow rate on conductivity and temperature time drift rate (DT) of high thermal stability tungsten-rhenium (95% W/5% Re vs. 74% W/26% Re) TFTCs were analyzed. According to the experimental results, the average Seebeck coefficient reached 31.1 µV/°C at 900 °C temperature difference (hot junction 1040 °C) with a repeatability error at ±1.37% in 33 h. The conductivity is 17.1 S/m, which is approximately 15.2 times larger than the compared tungsten-rhenium sample we presented, and the DT is 0.92 °C/h (1040 °C for 5 h), which is 9.5% of the old type we presented and 4.5% of compared ITO sample. The lumped capacity method test shows that the response time is 11.5 ms at 300 °C. This indicated an important significance in real-time temperature measurement for narrow spaces, such as the aero-engine combustion chamber.

Research on the High Temperature and High Pressure Gold-Plated Fiber Grating Dual-Parameter Sensing Measurement System.

In electrohydrostatic drive actuators, there is a demand for temperature and pressure monitoring in complex environments. Fiber Bragg grating (FBG) has become a promising sensor for measuring temperature and pressure. However, there is a cross-sensitivity between temperature and pressure. A gold-plated FBG is proposed and manufactured, and an FBG is used as a reference grating to form a parallel all-fiber sensing system, which can realize the simultaneous measurement of pressure and temperature. Based on the simulation software, the mechanical distribution of the pressure diaphragm is analyzed, and the fixation scheme of the sensor is determined. Using the demodulator to monitor the changes in the reflectance spectrum in real-time, the pressure and ambient temperature applied to the sensor are measured. The experimental results show that the temperature sensitivity of gold-plated FBG is 3 times that of quartz FBG, which can effectively distinguish the temperature changes. The pressure response sensitivity of gold-plated FBG is 0.3 nm/MPa, which is same as the quartz FBG. Through the sensitivity matrix equation, the temperature and pressure dual-parameter sensing measurement is realized. The accuracy of the temperature and pressure measurement is 97.7% and 99.0%, and the corresponding response rates are 2.7 ms/°C and 2 ms/MPa, respectively. The sensor has a simple structure and high sensitivity, and it is promising to be applied in health monitoring in complex environments with a high temperature and high pressure.

Compact Tri-FFPI sensor for measurement of ultrahigh temperature, vibration acceleration, and strain.

As a high-precision fiber optic sensor, a single optical fiber Fabry Pérot interferometer (FFPI) sensor is often used to measure parameters such as temperature or strain. However, the use of combined FFPIs to measure multiple parameters simultaneously has rarely been reported. In this paper, a compact Tri-FFPI sensor consisting of three series-connected FFPIs is proposed to measure high temperature, high acceleration, and large strain. The total length and diameter of the sensing part are only 2558.9 µm and 250 µm, respectively. One of the FFPIs, FFPI-1, contains a cantilever beam structure to measure vibration acceleration. FFPI-2 is used to measure temperature and the temperature compensation of the strain measurement. FFPI-3 is used to measure strain. To ensure that the sensor has high measurement sensitivity, two demodulation methods are used: the light intensity demodulation method for vibration acceleration and the wavelength demodulation method for temperature and strain. The sensor is capable of withstanding ultrahigh temperatures up to 1000°C.

Dislocation Defect Layer-Induced Magnetic Bi-states Phenomenon in Epitaxial La0.7Sr0.3MnO3(111) Thin Films.

La0.7Sr0.3MnO3 (LSMO) is one of the most fascinating strongly correlated oxides in which the spin polarization and magnetic property are sensitive to strain, especially in the (111)-oriented LSMO. In the paper, epitaxial LSMO(111) thin films with different thicknesses were prepared, and they showed continuous dislocation defect arrays with thickness greater than 45 nm. Then, the thick LSMO(111) films were divided into a double-layer structure with two slightly different oriented cells. The LSMO(111) films present a stronger lattice-spin coupling, thus the double-layer structure triggers an obvious magnetic heterogeneity phenomenon (magnetic bi-states) by the way of creating a double-mode ferromagnetic resonance (FMR) spectrum. Therefore, the nanostructures, especially the ordered structure defects, may trigger enriched physical phenomena and offer new forms of spin coupling and device functionality in strain-sensitive strongly correlated oxide systems.

Optimization on thermoelectric characteristics of indium tin oxide/indium oxide thin film thermocouples based on screen printing technology.

In this work, indium tin oxide (ITO)/indium oxide (In2O3) thin film thermocouples (TFTCs) were prepared based on screen printing technology for high temperature measurement. With terpilenol as solvent, epoxy resin and polyether amine as binders and glass powders as additives, the ITO and In2O3 slurries were printed onto the Al2O3 substrate to form thermocouples. The effect on thermoelectric properties of the TFTCs with heat treatment and different contents of additives was investigated through microstructure observation and thermal cycle test. The static calibration experiment shows that the annealed TFTCs with 7.5 wt. % glass powders additives have the maximum Seebeck coefficient. The thermoelectric voltage output of the TFTCs can reach 126.5 mV at 1275 °C while the temperature difference is 1160 °C and the sensitivity of the TFTCs was 109.1 µV/°C. The drift rate of the TFTCs was 8.34 °C/h at a measuring time of 20 min at 1275 °C. The TFTCs prepared via screen printing technology with excellent thermoelectric properties and thermal stability are aimed to be a viable replacement for practical applications.