RESUMEN
OBJECTIVE: This study aimed to evaluate the color stability (ΔE00 ) of bis-acryl resins after different immersion solutions and storage time by different evaluation methods. MATERIALS AND METHODS: Sixty specimens (n = 30) were prepared from Protemp 4 and Structur 3. The specimens were divided into three groups (n = 10), according to the immersion solution (artificial saliva, cola beverage, and yerba mate tea) and evaluated at two storage times (7 and 14 days). The ΔE00 of each group was calculated using color coordinates obtained by a spectrophotometer and by a digital method, using the CIEDE2000 color difference formula. Data were analyzed by three-way ANOVA and Tukey test (α = 0.05). RESULTS: The 7-day period presented the lowest ΔE00 values, regardless of the material and solution evaluated for both evaluation methods (ΔE00 < 0.93; ΔE00 < 3.12). The immersion solution with the highest color change was yerba mate tea after 14 days (ΔE00 > 2.11). For digital analyses, all materials and solutions at both times presented ΔE00 values higher than the clinically acceptable (ΔE00 > 1.8), while in spectrophotometer only in yerba mate tea (14 days) Structur was above the clinical acceptability level. CONCLUSIONS: Yerba mate tea was the immersion solution with a higher color change in both materials and assessment methods. The highest values were found after 14 days of immersion, regardless of the solution. The ΔE00 for the digital method was higher than the spectrophotometer analysis. CLINICAL SIGNIFICANCE: It is important to identify the influence of staining beverages on interim materials used in patients requiring temporary rehabilitation. The use of a spectrophotometer seems to be more accurate than the digital method for the evaluation of color parameters of the tested materials.
Asunto(s)
Resinas Compuestas , Materiales Dentales , Bebidas , Color , Humanos , Ensayo de Materiales , Propiedades de SuperficieRESUMEN
The quality of the micromechanical retention between the enamel prisms exposed through acid etching and adhesive system can be influenced by the relationship between the angle of the exposed enamel prisms and the external surface/restorative material. Therefore, the aim of the present study was to determine the influence of the enamel cavosurface beveling in different cavity sizes on the angle relation between enamel prisms and the restorative material. For this research, 30 human permanent molars were used and divided into three groups according the isthmus aperture of class I cavities (1/4, 1/3, and 1/2 of the intercuspal distance). Cavosurface angle beveling was performed in each tooth buccal or palatal/lingual side, and a resin composite restoration was placed. Each restored tooth was sectioned in buccal/palatal direction followed by analysis in scanning electron microscope. Means of the angles observed between enamel prisms and the restorative material were registered and statistically analyzed by Kruskal-Wallis test. Results showed higher mean angle values for beveled groups when comparing with the values observed in the unbeveled margins (p < .05) regardless of the isthmus aperture, being 1/4 (beveled = 48.36°; unbeveled = 20.71°), 1/3 (beveled = 39.75°; unbeveled = 29.15°), and 1/2 (beveled = 37.02°; unbeveled = 26.34°). It was also observed that in some unbeveled cavities, there were the presence of laterally exposed enamel prisms (0°), mainly in more conservative cavities. It was concluded that the presence of higher angles values occurred in the samples with beveled margins, without presence of laterally exposed enamel prisms.
RESUMEN
OBJECTIVES: In this study hybrid nanofibers embedded with niobium pentoxide (Nb2O5) were synthesized, incorporated in self-adhesive resin cement, and their influence on physical-properties was evaluated. METHODS: Poly(D,L-lactide), PDLLA cotton-wool-like nanofibers with and without silica-based sol-gel precursors were formulated and spun into submicron fibers via solution blow spinning, a rapid fiber forming technology. The morphology, chemical composition and thermal properties of the spun fibers were characterized by field emission scanning electron microscopy (FE-SEM), energy dispersive X-ray spectroscopy (EDS) and Fourier-transform infrared spectroscopy (FTIR), and differential scanning calorimetry (DSC), respectively. Produced fibers were combined with a self-adhesive resin cement (RelyX U200, 3M ESPE) in four formulations: (1) U200 resin cement (control); (2) U200+1wt.% PDLLA fibers; (3) U200+1wt.% Nb2O5-filled PDLLA composite fibers and (4) U200+1wt.% Nb2O5/SiO2-filled PDLLA inorganic-organic hybrid fibers. Physical properties were assessed in flexure by 3-point bending (n=10), Knoop microhardness (n=5) and degree of conversion (n=3). Data were analyzed with One-way ANOVA and Tukey's HSD (α=5%). RESULTS: Composite fibers formed of PDLLA-Nb2O5 exhibited an average diameter of â¼250nm, and hybrid PDLLA+Nb2O5/SiO2 fibers were slightly larger, â¼300nm in diameter. There were significant differences among formulations for hardness and flexural strength (p<0.05). Degree of conversion of resin cement was not affected for all groups, except for Group 4 (p<0.05). SIGNIFICANCE: Hybrid reinforcement nanofibers are promising as fillers for dental materials. The self-adhesive resin cement with PDLLA+Nb2O5 and PDLLA+Nb2O5/SiO2 presented superior mechanical performance than the control group.