RESUMEN
In this study, we conduct extensive high-pressure experiments to investigate phase stability in the cobalt-nitrogen system. Through a combination of synthesis in a laser-heated diamond anvil cell, first-principles calculations, Raman spectroscopy, and single-crystal X-ray diffraction, we establish the stability fields of known high-pressure phases, hexagonal NiAs-type CoN, and marcasite-type CoN2 within the pressure range of 50-90â GPa. We synthesize and characterize previously unknown nitrides, Co3N2, Pnma-CoN and two polynitrides, CoN3 and CoN5, within the pressure range of 90-120â GPa. Both polynitrides exhibit novel types of polymeric nitrogen chains and networks. CoN3 feature branched-type nitrogen trimers (N3) and CoN5 show π-bonded nitrogen chain. As the nitrogen content in the cobalt nitride increases, the CoN6 polyhedral frameworks transit from face-sharing (in CoN) to edge-sharing (in CoN2 and CoN3), and finally to isolated (in CoN5). Our study provides insights into the intricate interplay between structure evolution, bonding arrangements, and high-pressure synthesis in polynitrides, expanding the knowledge for the development of advanced energy materials.
RESUMEN
Nitridophosphates and nitridogermanates attract high interest in current research due to their structural versatility. Herein, the elastic properties of GeP2N4 were investigated by single-crystal X-ray diffraction (XRD) upon compression to 44.4(1) GPa in a diamond anvil cell. Its isothermal bulk modulus was determined to be 82(6) GPa. At 44.4(1) GPa, laser heating resulted in the formation of multiple crystalline phases, one of which was identified as unprecedented germanium nitridophosphate GePN3. Its structure was elucidated from single-crystal XRD data (C2/c (no. 15), a = 8.666(5), b = 8.076(4), c = 4.691(2) Å, ß = 101.00(7)°) and is built up from layers of GeN6 octahedra and PN4 tetrahedra. The GeN6 octahedra form double zigzag chains, while the PN4 tetrahedra are found in single zigzag chains. GePN3 can be recovered to ambient conditions with a unit cell volume increase of about 12%. It combines PV and GeIV in a condensed nitridic network for the first time.
RESUMEN
The reaction between PrO2 and SiO2 was investigated at various pressure points up to 29 GPa in a diamond anvil cell using laser heating and in situ single-crystal structure analysis. The pressure points at 5 and 10 GPa produced Pr2III(Si2O7), whereas Pr4IIISi3O12 and Pr2IV(O2)O3 were obtained at 15 GPa. Pr4IIISi3O12 can be interpreted as a high-pressure modification of the still unknown orthosilicate Pr4III(SiO4)3. PrIVSi3O8 and Pr2IVSi7O18 that contain praseodymium in its rare + IV oxidation state were identified at 29 GPa. After the pressure was released from the reaction chamber, the Pr(IV) silicates could be recovered, indicating that they are metastable at ambient pressure. Density functional theory calculations of the electronic structure corroborate the oxidation state of praseodymium in both PrIVSi3O8 and Pr2IVSi7O18. Both silicates are the first structurally characterized representatives of Pr4+-containing salts with oxoanions. All three silicates contain condensed networks of [SiO6] octahedra which is unprecedented in the rich chemistry of lanthanoid silicates.
RESUMEN
The study of the structural stability of carbonates under different pressure and temperature conditions is important for modeling the carbon budget in the Earth's interior and the stability of carbonation products of carbon capture and storage (CCS) solutions. In this work, we confirm the existence of the two dense polymorphs of the hydrated magnesium carbonate MgCO3·3H2O nesquehonite mineral previously reported, and we characterize their structures using synchrotron single-crystal X-ray diffraction at 3.1 and 11.6 GPa. Phase transitions entail the distortion and atomic rearrangement of the Mg-centered polyhedra and the tilting of the [CO3] carbonate units. In particular, the Mg coordination number increases from 6 in nesquehonite to 7 in the second high-pressure phase, while maintaining a topology based on complex MgCO3(H2O)2 chains. We also studied their vibrational behavior upon compression using Raman spectroscopy and complemented the experimental results with density-functional theory (DFT) calculations. The role played by hydrogen bonds in the compressibility and the polymorphism of this hydrated carbonate is also discussed.
RESUMEN
The research for wurtzite-type ternary nitride semiconductors containing earth abundant elements with a stoichiometry of 1:1:2 was focused on metals like Mg or Zn, so far. The vast majority of these Grimm-Sommerfeld analogous compounds crystallize in the ß-NaFeO2 structure, although a second arrangement in space group Pmc21 is predicted to be a viable alternative. Despite extensive theoretical and experimental studies, this structure has so far remained undiscovered. Herein, we report on BeGeN2 in a Pmc21 structure, synthesized from Be3N2 and Ge3N4 using a high-pressure high-temperature approach at 6 GPa and 800 °C. The compound was characterized by powder X-ray diffraction (PXRD), solid state nuclear magnetic resonance (NMR), Raman and energy dispersive X-ray (EDX) spectroscopy, temperature-dependent PXRD, second harmonic generation (SHG) and UV/VIS measurements and in addition also compared to its lighter homologue BeSiN2 in all mentioned analytic techniques. The synthesis and investigation of both the first beryllium germanium nitride and the first ternary wurtzite-type nitride crystallizing in space group Pmc21 open the door to a new field of research on wurtzite-type related structures.
RESUMEN
The stabilization of nitrogen-rich phases presents a significant chemical challenge due to the inherent stability of the dinitrogen molecule. This stabilization can be achieved by utilizing strong covalent bonds in complex anions with carbon, such as cyanide CN- and NCN2- carbodiimide, while more nitrogen-rich carbonitrides are hitherto unknown. Following a rational chemical design approach, we synthesized antimony guanidinate SbCN3 at pressures of 32-38â GPa using various synthetic routes in laser-heated diamond anvil cells. SbCN3 , which is isostructural to calcite CaCO3 , can be recovered under ambient conditions. Its structure contains the previously elusive guanidinate anion [CN3 ]5- , marking a fundamental milestone in carbonitride chemistry. The crystal structure of SbCN3 was solved and refined from synchrotron single-crystal X-ray diffraction data and was fully corroborated by theoretical calculations, which also predict that SbCN3 has a direct band gap with the value of 2.20â eV. This study opens a straightforward route to the entire new family of inorganic nitridocarbonates.
RESUMEN
The metal-insulator transition driven by electronic correlations is one of the most fundamental concepts in condensed matter. In mixed-valence compounds, this transition is often accompanied by charge ordering (CO), resulting in the emergence of complex phases and unusual behaviors. The famous example is the archetypal mixed-valence mineral magnetite, Fe3O4, exhibiting a complex charge-ordering below the Verwey transition, whose nature has been a subject of long-time debates. In our study, using high-resolution X-ray diffraction supplemented by resistance measurements and DFT+DMFT calculations, the electronic, magnetic, and structural properties of recently synthesized mixed-valence Fe4O5 are investigated under pressure to â¼100 GPa. Our calculations, consistent with experiment, reveal that at ambient conditions Fe4O5 is a narrow-gap insulator characterized by the original Verwey-type CO. Under pressure Fe4O5 undergoes a series of electronic and magnetic-state transitions with an unusual compressional behavior above â¼50 GPa. A site-dependent collapse of local magnetic moments is followed by the site-selective insulator-to-metal transition at â¼84 GPa, occurring at the octahedral Fe sites. This phase transition is accompanied by a 2+ to 3+ valence change of the prismatic Fe ions and collapse of CO. We provide a microscopic explanation of the complex charge ordering in Fe4O5 which "unifies" it with the behavior of two archetypal examples of charge- or bond-ordered materials, magnetite and rare-earth nickelates (RNiO3). We find that at low temperatures the Verwey-type CO competes with the "trimeron"/"dimeron" charge ordered states, allowing for pressure/temperature tuning of charge ordering. Summing up the available data, we present the pressure-temperature phase diagram of Fe4O5.
RESUMEN
Magnetite, Fe3O4, is the oldest known magnetic mineral and archetypal mixed-valence oxide. Despite its recognized role in deep Earth processes, the behavior of magnetite at extreme high-pressure high-temperature (HPHT) conditions remains insufficiently studied. Here, we report on single-crystal synchrotron X-ray diffraction experiments up to â¼80 GPa and 5000 K in diamond anvil cells, which reveal two previously unknown Fe3O4 polymorphs, γ-Fe3O4 with the orthorhombic Yb3S4-type structure and δ-Fe3O4 with the modified Th3P4-type structure. The latter has never been predicted for iron compounds. The decomposition of Fe3O4 at HPHT conditions was found to result in the formation of exotic phases, Fe5O7 and Fe25O32, with complex structures. Crystal-chemical analysis of iron oxides suggests the high-spin to low-spin crossover in octahedrally coordinated Fe3+ in the pressure interval between 43 and 51 GPa. Our experiments demonstrate that HPHT conditions promote the formation of ferric-rich Fe-O compounds, thus arguing for the possible involvement of magnetite in the deep oxygen cycle.
RESUMEN
Nitrogen and water are very abundant in nature; however, the way they chemically react at extreme pressure-temperature conditions is unknown. Below 6 GPa, they have been reported to form clathrate compounds. Here, we present Raman spectroscopy and x-ray diffraction studies in the H2O-N2 system at high pressures up to 140 GPa. We find that clathrates, which form locally in our diamond cell experiments above 0.3 GPa, transform into a fine grained state above 6 GPa, while there is no sign of formation of mixed compounds. We point out size effects in fine grained crystallites, which result in peculiar Raman spectra in the molecular regime, but x-ray diffraction shows no additional phase or deviation from the bulk behavior of familiar solid phases. Moreover, we find no sign of ice doping by nitrogen, even in the regimes of stability of nonmolecular nitrogen.
RESUMEN
The synthesis of polynitrogen compounds is of great importance due to their potential as high-energy-density materials (HEDM), but because of the intrinsic instability of these compounds, their synthesis and stabilization is a fundamental challenge. Polymeric nitrogen units which may be stabilized in compounds with metals at high pressure are now restricted to non-branched chains with an average N-N bond order of 1.25, limiting their HEDM performances. Herein, we demonstrate the synthesis of a novel polynitrogen compound TaN5 via a direct reaction between tantalum and nitrogen in a diamond anvil cell at circa 100â GPa. TaN5 is the first example of a material containing branched all-single-bonded nitrogen chains [N5 5- ]∞ . Apart from that we discover two novel Ta-N compounds: TaN4 with finite N4 4- chains and the incommensurately modulated compound TaN2-x , which is recoverable at ambient conditions.
RESUMEN
Owing to its outstanding elastic properties, the nitride spinel γ-Si3 N4 is of considered interest for materials scientists and chemists. DFT calculations suggest that Si3 N4 -analog beryllium phosphorus nitride BeP2 N4 adopts the spinel structure at elevated pressures as well and shows outstanding elastic properties. Herein, we investigate phenakite-type BeP2 N4 by single-crystal synchrotron X-ray diffraction and report the phase transition into the spinel-type phase at 47â GPa and 1800â K in a laser-heated diamond anvil cell. The structure of spinel-type BeP2 N4 was refined from pressure-dependent in situ synchrotron powder X-ray diffraction measurements down to ambient pressure, which proves spinel-type BeP2 N4 a quenchable and metastable phase at ambient conditions. Its isothermal bulk modulus was determined to 325(8)â GPa from equation of state, which indicates that spinel-type BeP2 N4 is an ultraincompressible material.
RESUMEN
Functional oxides whose physicochemical properties may be reversibly changed at standard conditions are potential candidates for the use in next-generation nanoelectronic devices. To date, vanadium dioxide (VO2 ) is the only known simple transition-metal oxide that demonstrates a near-room-temperature metal-insulator transition that may be used in such appliances. In this work, we synthesized and investigated the crystals of a novel mixed-valent iron oxide with an unconventional Fe5 O6 stoichiometry. Near 275â K, Fe5 O6 undergoes a Verwey-type charge-ordering transition that is concurrent with a dimerization in the iron chains and a following formation of new Fe-Fe chemical bonds. This unique feature highlights Fe5 O6 as a promising candidate for the use in innovative applications. We established that the minimal Fe-Fe distance in the octahedral chains is a key parameter that determines the type and temperature of charge ordering. This model provides new insights into charge-ordering phenomena in transition-metal oxides in general.
RESUMEN
Polynitrides are intrinsically thermodynamically unstable at ambient conditions and require peculiar synthetic approaches. Now, a one-step synthesis of metal-inorganic frameworks Hf4 N20 â N2 , WN8 â N2 , and Os5 N28 â 3 N2 via direct reactions between elements in a diamond anvil cell at pressures exceeding 100â GPa is reported. The porous frameworks (Hf4 N20 , WN8 , and Os5 N28 ) are built from transition-metal atoms linked either by polymeric polydiazenediyl (polyacetylene-like) nitrogen chains or through dinitrogen units. Triply bound dinitrogen molecules occupy channels of these frameworks. Owing to conjugated polydiazenediyl chains, these compounds exhibit metallic properties. The high-pressure reaction between Hf and N2 also leads to a non-centrosymmetric polynitride Hf2 N11 that features double-helix catena-poly[tetraz-1-ene-1,4-diyl] nitrogen chains [-N-N-N=N-]∞ .
RESUMEN
The high-pressure behavior of non-metal nitrides is of special interest for inorganic and theoretical chemistry as well as materials science, as these compounds feature intriguing elastic properties. The double nitride α-BP3 N6 was investigated by inâ situ single-crystal X-ray diffraction (XRD) upon cold compression to a maximum pressure of about 42â GPa, and its isothermal bulk modulus at ambient conditions was determined to be 146(6)â GPa. At maximum pressure the sample was laser-heated, which resulted in the formation of an unprecedented high-pressure polymorph, ß-BP3 N6 . Its structure was elucidated by single-crystal XRD, and can be described as a decoration of a distorted hexagonal close packing of N with B in tetrahedral and P in octahedral voids. Hence, ß-BP3 N6 is the first nitride to contain PN6 octahedra, representing the much sought-after proof of principle for sixfold N-coordinated P that has been predicted for numerous high-pressure phases of nitrides.
RESUMEN
High-pressure single-crystal X-ray diffraction at ambient temperature and high-pressure SQUID measurements down to 2 K were performed up to â¼2.5 GPa on ammonium metal formates, [NH4][M(HCOO)3] where M = Mn2+, Fe2+, and Ni2+, in order to correlate structural variations to magnetic behaviour. Similar structural distortions and phase transitions were observed for all compounds, although the transition pressures varied with the size of the metal cation. The antiferromagnetic ordering in [NH4][M(HCOO)3] compounds was maintained as a function of pressure, and the magnetic ordering transition temperature changed within a few kelvins depending on the structural distortion and the metal cation involved. These compounds, in particular [NH4][Fe(HCOO)3], showed greatest sensitivity to the degree of spin canting upon compression, clearly visible from the twenty-fold increase in the low-temperature magnetisation for [NH4][Fe(HCOO)3] at 1.4 GPa, and the change from purely antiferromagnetic to weakly ferromagnetic ordering in [NH4][Mn(HCOO)3] at 1 GPa. The variation in the exchange couplings and spin canting was checked with density-functional calculations that reproduce well the increase in canted moment within [NH4][Fe(HCOO)3] upon compression, and suggest that the Dzyaloshinskii-Moriya (DM) interaction is evolving as a function of pressure. The pressure dependence of spin canting is found to be highly dependent on the metal cation, as magnetisation magnitudes did not change significantly for when M = Ni2+ or Mn2+. These results demonstrate that the overall magnetic behaviour of each phase upon compression was not only dependent on the structural distortions but also on the electronic configuration of the metal cation.
RESUMEN
Phosphorus oxonitride (PON) is isoelectronic with SiO2 and may exhibit a similar broad spectrum of intriguing properties as silica. However, PON has only been sparsely investigated under high-pressure conditions and there has been no evidence on a PON polymorph with a coordination number of P greater thanâ 4. Herein, we report a post-coesite (pc) PON polymorph exhibiting a stishovite-related structure with P in a (5+1) coordination. The pc-PON was synthesized using the multianvil technique and characterized by powder X-ray diffraction, solid-state NMR spectroscopy, TEM measurements and inâ situ synchrotron X-ray diffraction in diamond anvil cells. The structure model was verified by single-crystal X-ray diffraction at 1.8â GPa and the isothermal bulk modulus of pc-PON was determined to K0 =163(2)â GPa. Moreover, an orthorhombic PON polymorph (o-PON) was observed under high-pressure conditions and corroborated as the stable modification at pressures above 17â GPa by DFT calculations.
RESUMEN
A nitrogen-rich compound, ReN8 â x N2 , was synthesized by a direct reaction between rhenium and nitrogen at high pressure and high temperature in a laser-heated diamond anvil cell. Single-crystal X-ray diffraction revealed that the crystal structure, which is based on the ReN8 framework, has rectangular-shaped channels that accommodate nitrogen molecules. Thus, despite a very high synthesis pressure, exceeding 100â GPa, ReN8 â x N2 is an inclusion compound. The amount of trapped nitrogen (x) depends on the synthesis conditions. The polydiazenediyl chains [-N=N-]∞ that constitute the framework have not been previously observed in any compound. Abâ initio calculations on ReN8 â x N2 provide strong support for the experimental results and conclusions.
RESUMEN
We investigated the structural, vibrational, magnetic, and electronic properties of the recently synthesized CaCo3V4O12 double perovskite with the high-spin (HS) Co2+ ions in a square-planar oxygen coordination at extreme conditions of high pressures and low temperatures. The single-crystal X-ray diffraction and Raman spectroscopy studies up to 60 GPa showed a conservation of its cubic crystal structure but indicated a crossover near 30 GPa. Above 30 GPa, we observed both an abnormally high "compressibility" of the Co-O bonds in the square-planar oxygen coordination and a huge anisotropic displacement of HS-Co2+ ions in the direction perpendicular to the oxygen planes. Although this effect is reminiscent of a continuous HS â LS transformation of the Co2+ ions, it did not result in the anticipated shrinkage of the cell volume because of a certain "stiffing" of the bonds of the Ca and V cations. We verified that the oxidation states of all the cations did not change across this crossover, and hence, no charge-transfer effects were involved. Consequently, we proposed that CaCo3V4O12 could undergo a phase transition at which the large HS-Co2+ ions were pushed out of the oxygen planes because of lattice compression. The antiferromagnetic transition in CaCo3V4O12 at 100 K was investigated by neutron powder diffraction at ambient pressure. We established that the magnetic moments of the Co2+ ions were aligned along one of the cubic axes, and the magnetic structure had a 2-fold periodicity along this axis, compared to the crystallographic one.
RESUMEN
CD3ζ has emerged as a clinically important immunological marker in head and neck squamous cell carcinoma (HNSCC) with reduced level of expression reported in both tumor infiltrating lymphocytes and peripheral blood lymphocytes. In this prospective study (power = 0.99, α = 0.05), CD3ζ expression was compared in 47 HNSCC patients and 53 controls using standardized flow cytometric method. There was no statistical difference in the percentages of the CD3 ε+ T-cell subset present in the peripheral blood mononuclear cells of the HNSCC patients and the healthy controls; however, T cells from the HNSCC patients produced a significantly weaker IFN-γ response in comparison to the healthy controls, when they were stimulated by the recall viral CEF peptide antigen. All patients were followed up for at least 3 years with a median follow-up of 45 months. Levels of CD3ζ-chain expression were measured at 117 follow-up visits at six-month intervals. Receiver operating characteristic curve identified the optimal cut off as a 12% increase in post treatment CD3ζ-chain expression from the baseline levels to confirm absence of HNSCC with the area under curve of 0.81 (95% CI = 0.68-0.94) for predicting absence of HNSCC. The specificity, sensitivity and positive predictive value were 81.25% 79.21% and 97.56%, respectively. Three-year disease specific survival (DSS) was significantly lower (p = 0.007) at 63.2% for patients who showed <12% increase in CD3ζ-chain level as compared to 96.2% for patients who had ≥12% increase. Our results indicate that the change in CD3ζ-chain expression from the baseline is an independent predictor of residual and recurrent HNSCC.
Asunto(s)
Biomarcadores de Tumor/biosíntesis , Complejo CD3/biosíntesis , Carcinoma de Células Escamosas/genética , Neoplasias de Cabeza y Cuello/genética , Adulto , Anciano , Biomarcadores de Tumor/genética , Complejo CD3/genética , Carcinoma de Células Escamosas/patología , Supervivencia sin Enfermedad , Femenino , Regulación Neoplásica de la Expresión Génica , Neoplasias de Cabeza y Cuello/patología , Humanos , Leucocitos Mononucleares/metabolismo , Leucocitos Mononucleares/patología , Masculino , Persona de Mediana Edad , Carcinoma de Células Escamosas de Cabeza y CuelloRESUMEN
The incorporation of noble gas atoms, in particular neon, into the pores of network structures is very challenging due to the weak interactions they experience with the network solid. Using high-pressure single-crystal X-ray diffraction, we demonstrate that neon atoms enter into the extended network of ammonium metal formates, thus forming compounds Nex [NH4 ][M(HCOO)3 ]. This phenomenon modifies the compressional and structural behaviours of the ammonium metal formates under pressure. The neon atoms can be clearly localised within the centre of [M(HCOO)3 ]5 cages and the total saturation of this site is achieved after â¼1.5â GPa. We find that by using argon as the pressure-transmitting medium, the inclusion inside [NH4 ][M(HCOO)3 ] is inhibited due to the larger size of the argon. This study illustrates the size selectivity of [NH4 ][M(HCOO)3 ] compounds between neon and argon insertion under pressure, and the effect of inclusion on the high-pressure behaviour of neon-bearing ammonium metal formates.