A method for characterizing the topological fluctuations in liquids is proposed. This approach exploits the concept of the weighted gyration tensor of a collection of particles and permits the definition of a local configurational unit (LCU). The first principal axis of the gyration tensor serves as the director of the LCU, which can be tracked and analyzed by molecular dynamics simulations. Analysis of moderately supercooled Kob-Andersen mixtures suggests that orientational relaxation of the LCU closely follows viscoelastic relaxation and exhibits a two-stage behavior. The slow relaxing component of the LCU corresponds to the structural, Maxwellian mechanical relaxation. Additionally, it is found that the mean curvature of the LCUs is approximately zero at the Maxwell relaxation time with the Gaussian curvature being negative. This observation implies that structural relaxation occurs when the configurationally stable and destabilized regions interpenetrate each other in a bicontinuous manner. Finally, the mean and Gaussian curvatures of the LCUs can serve as reduced variables for the shear stress correlation, providing a compelling proof of the close connection between viscoelastic relaxation and topological fluctuations in glass-forming liquids.
RESUMEN
Cu with nanotwin (NT) possesses great electrical, mechanical, and thermal properties and has potential for electronic applications. Various studies have reported the effect of NT orientation on Cu mechanical properties. However, its effect on Cu stress-relaxation behavior has not been clarified, particularly in nano-scale. In this study, Cu nanopillars with various orientations were examined by a picoindenter under constant strain and observed byin situTEM. The angles between the twin plane and the loading direction in the examined nanopillars were 0°, 60°, to 90°, and a benchmark pillar of single-crystal Cu without NT was examined. The stress drops were respectively 10%, 80%, 4%, and 50%. Owing to the interaction by NT, the dislocation behavior in nanopillars was different from that in bulk or in thin film samples. Especially, the rapid slip path of dislocations to go to the free surface of the nanopillar induced a dislocation-free zone in the 0° nanopillar, which led to work-softening. On the contrary, a high dislocation density was observed in the 90° nanopillar, which was generated by dislocation interaction and obstruction of dislocation slip by twin planes, and it led to work-hardening. The findings reveal the NT orientation in Cu nanopillars affected stress relaxation significantly.
RESUMEN
We outline a machine learning strategy for quantitively determining the conformation of AB-type diblock copolymers with excluded volume effects using small angle scattering. Complemented by computer simulations, a correlation matrix connecting conformations of different copolymers according to their scattering features is established on the mathematical framework of a Gaussian process, a multivariate extension of the familiar univariate Gaussian distribution. We show that the relevant conformational characteristics of copolymers can be probabilistically inferred from their coherent scattering cross sections without any restriction imposed by model assumptions. This work not only facilitates the quantitative structural analysis of copolymer solutions but also provides the reliable benchmarking for the related theoretical development of scattering functions.
RESUMEN
Herein, we aim to develop a facile method for the fabrication of mechanical metamaterials from templated polymerization of thermosets including phenolic and epoxy resins using self-assembled block copolymer, polystyrene-polydimethylsiloxane with tripod network (gyroid), and tetrapod network (diamond) structures, as templates. Nanoindentation studies on the nanonetwork thermosets fabricated reveal enhanced energy dissipation from intrinsic brittle thermosets due to the deliberate structuring; the calculated energy dissipation for gyroid phenolic resins is 0.23 nJ whereas the one with diamond structure gives a value of 0.33 nJ. Consistently, the gyroid-structured epoxy gives a high energy dissipation value of 0.57 nJ, and the one with diamond structure could reach 0.78 nJ. These enhanced properties are attributed to the isotropic periodicity of the nanonetwork texture with plastic deformation, and the higher number of struts in the tetrapod diamond network in contrast to tripod gyroid, as confirmed by the finite element analysis.
RESUMEN
Band structure by design in 2D layered semiconductors is highly desirable, with the goal to acquire the electronic properties of interest through the engineering of chemical composition, structure, defect, stacking, or doping. For atomically thin transition metal dichalcogenides, substitutional doping with more than one single type of transition metals is the task for which no feasible approach is proposed. Here, the growth of WS2 monolayer is shown codoped with multiple kinds of transition metal impurities via chemical vapor deposition controlled in a diffusion-limited mode. Multielement embedment of Cr, Fe, Nb, and Mo into the host lattice is exemplified. Abundant impurity states thus generate in the bandgap of the resultant WS2 and provide a robust switch of charging/discharging states upon sweep of an electric filed. A profound memory window exists in the transfer curves of doped WS2 field-effect transistors, forming the basis of binary states for robust nonvolatile memory. The doping technique presented in this work brings one step closer to the rational design of 2D semiconductors with desired electronic properties.
RESUMEN
Self-assembly of amphiphilic polymers in water is of fundamental and practical importance. Significant amounts of free unimers and associated micellar aggregates often coexist over a wide range of phase regions. The thermodynamic and kinetic properties of the microphase separation are closely related to the relative population density of unimers and micelles. Although the scattering technique has been employed to identify the structure of micellar aggregates as well as their time-evolution, the determination of the population ratio of micelles to unimers remains a challenging problem due to their difference in scattering power. Here, using small-angle neutron scattering (SANS), we present a comprehensive structural study of amphiphilic n-dodecyl-PNIPAm polymers, which shows a bimodal size distribution in water. By adjusting the deuterium/hydrogen ratio of water, the intra-micellar polymer and water distributions are obtained from the SANS spectra. The micellar size and number density are further determined, and the population densities of micelles and unimers are calculated to quantitatively address the degree of micellization at different temperatures. Our method can be used to provide an in-depth insight into the solution properties of microphase separation, which are present in many amphiphilic systems.
RESUMEN
We observed the small-size-induced hardening and plasticity of brittle ionic MgO as a result of abnormally triggered dislocation gliding on a non-charge-balanced slip system. The indentation tests of ⟨111⟩ MgO pillars revealed an increased hardness with decreasing pillar size, and the tips of the pillars that were ≤200 nm were plastically deformed. The in situ compression tests of ⟨111⟩ MgO nanopillars in transmission electron microscopy verified aligned dislocation-mediated plasticity on the {111}⟨110⟩ and {100}⟨110⟩ systems rather than the charge-balanced {110}⟨110⟩ slip system.
RESUMEN
BACKGROUND: Changes over time in preferences for life-sustaining treatments (LSTs) at end of life (EOL) in different patient cohorts are not well established, nor is the concept that LST preferences represent more than 2 groups (uniformly prefer/not prefer). PURPOSE: The purpose of this study was to explore heterogeneity and changes in patterns of LST preferences among 2 independent cohorts of terminally ill patients with cancer recruited a decade apart. METHODS: Preferences for cardiopulmonary resuscitation, intensive care unit care, cardiac massage, intubation with mechanical ventilation, intravenous nutritional support, nasogastric tube feeding, and dialysis were surveyed among 2,187 and 2,166 patients in 2003-2004 and 2011-2012, respectively. Patterns and changes in LST preferences were examined by multigroup latent class analysis. RESULTS: We identified 7 preference classes: uniformly preferring, uniformly rejecting, uniformly uncertain, favoring nutritional support but rejecting other treatments, favoring nutritional support but uncertain about other treatments, favoring intravenous nutritional support with mixed rejection of or uncertainty about other treatments, and preferring LSTs except intubation with mechanical ventilation. Probability of class membership decreased significantly over time for the uniformly preferring class (15.26%-8.71%); remained largely unchanged for the classes of uniformly rejecting (41.71%-40.54%) and uniformly uncertain (9.10%-10.47%), and favoring nutritional support but rejecting (20.68%-21.91%) or uncertain about (7.02%-5.47%) other treatments, and increased significantly for the other 2 classes. The LST preferences of Taiwanese terminally ill patients with cancer are not a homogeneous construct and shifted toward less-aggressive treatments over the past decade. CONCLUSIONS: Identifying LST preference patterns and tailoring interventions to the unique needs of patients in each LST preference class may lead to the provision of less-aggressive EOL care.
Asunto(s)
Cuidados para Prolongación de la Vida , Neoplasias/epidemiología , Neoplasias/terapia , Prioridad del Paciente , Cuidado Terminal , Enfermo Terminal , Estudios Transversales , Humanos , Cuidados para Prolongación de la Vida/métodos , Cuidados para Prolongación de la Vida/tendencias , Taiwán/epidemiología , Cuidado Terminal/métodos , Cuidado Terminal/tendenciasRESUMEN
In situ nanoscopic observations of healthy and osteoporotic bone nanopillars under compression were performed. The structural-mechanical property relationship at the atomic scale suggests that cortical bone performance is correlated to the feature, arrangement, movement, distortion, and fracture of hydroxyapatite nanocrystals. Healthy bone comprising tightly bound mineral nanocrystals shows high structural stability with nanoscopic lattice distortions and dislocation activities. On the other hand, osteoporotic bone exhibits brittleness owing to the movements of dispersed minerals in and intergranular fracture along a weak organic matrix.
Asunto(s)
Huesos/fisiopatología , Nanotecnología , Osteoporosis/fisiopatología , Animales , Fenómenos Biomecánicos , Ratones , Microscopía Electrónica de TransmisiónRESUMEN
Medium-entropy alloys (MEAs) have attracted considerable attention in recent decades due to their exceptional material properties and design flexibility. In this study, lightweight and non-equiatomic MEAs with low density (~5 g/cm3), high strength (yield strength: 1200 MPa), and high ductility (plastic deformation: â§10%) were explored. We fine-tuned a previously developed Ti-rich MEA by microalloying it with small amounts of Ni (reducing the atomic radius and increasing the elastic modulus) through solid solution strengthening to achieve a series of MEAs with enhanced mechanical properties. Among the prepared MEAs, Ti65Ni1 and Ti65Ni3 exhibited optimal properties in terms of the balance between strength and ductility. Furthermore, the Ti65Ni3 MEA was subjected to thermo-mechanical treatment (TMT) followed by cold rolling 70% (CR70) and cold rolling 85% (CR85). Subsequently, the processed samples were rapidly annealed at 743 °C, 770 °C, 817 °C, and 889 °C at a heating rate of 15 °C/s. X-ray diffraction analysis revealed that the MEA could retain its single-body-centered cubic solid solution structure after TMT. Additionally, the tensile testing results revealed that increasing the annealing temperature led to a decrease in yield strength and an increase in ductility. Notably, the Ti65Ni3 MEA sample that was subjected to CR70 and CR85 processing and annealed for 30 s exhibited high yield strength (>1250 MPa) and ductility (>13%). In particular, the Ti65Ni3 MEA subjected to CR85 exhibited a specific yield strength of 264 MPa·cm3/g, specific tensile strength of 300 MPa·cm3/g, and ductility of >13%.
RESUMEN
In this study, we investigated the thermal stabilities of butylphosphonic acid (BPA) and aminopropyltriethoxysilane (APTES) self-assembled monolayers (SAM) on a Si substrate. The thermal desorption and the thermal cleavage of the BPA and APTES SAM film on the Si substrate were studied by X-ray photoelectron spectroscopy (XPS) upon thermal treatment from 50 to 550 °C. XPS analyses show that the onset of the thermal desorption of the APTES monolayer occurs at 250 °C and the APTES SAM completely decomposed at 400 °C. Conversely, BPA SAM on Si shows that the onset of thermal desorption occurs at 350 °C, and the BPA SAM completely desorbed at approximately 500 °C. Our study revealed that the organophosphonate SAM is a more stable SAM in modifying the dielectric sidewalls of a Cu interconnect when compared to organosilane SAM. To overcome the spontaneous reaction of the organophosphonate film on the metal substrate, a simple orthogonal functionalization method using thiolate SAM as a sacrificial layer was also demonstrated in this study.
RESUMEN
The nanoscopic deformation of ⟨111⟩ nanotwinned copper nanopillars under strain rates between 10-5/s and 5 × 10-4/s was studied by using in situ transmission electron microscopy. The correlation among dislocation activity, twin boundary instability due to incoherent twin boundary migration and corresponding mechanical responses was investigated. Dislocations piled up in the nanotwinned copper, giving rise to significant hardening at relatively high strain rates of 3-5 × 10-4/s. Lower strain rates resulted in detwinning and reduced hardening, while corresponding deformation mechanisms are proposed based on experimental results. At low/ultralow strain rates below 6 × 10-5/s, dislocation activity almost ceased operating, but the migration of twin boundaries via the 1/4 ⟨101¯ ⟩ kink-like motion of atoms is suggested as the detwinning mechanism. At medium strain rates of 1-2 × 10-4/s, detwinning was decelerated likely due to the interfered kink-like motion of atoms by activated partial dislocations, while dislocation climb may alternatively dominate detwinning. These results indicate that, even for the same nanoscale twin boundary spacing, different nanomechanical deformation mechanisms can operate at different strain rates.
RESUMEN
This study presents the utilization of MoS2 as a diffusion barrier for metal interconnects, in situ transmission electron microscopy (TEM) observations are employed for comprehensive understanding. The diffusion-blocking ability of MoS2 is discussed by the diffusion and phase transformation between Ru and Si via TEM diffraction and imaging. When the sample is heated to a high temperature such that MoS2 loses the ability to block the diffusion, Si diffuses through the MoS2 into the Ru layer, leading to the formation of Ru2Si3. Both multilayer and monolayer (1L) MoS2 exhibit exceptional diffusion-blocking ability up to 800 °C. Furthermore, plasma-treated 1L-MoS2 shows a slightly low diffusion-blocking temperature of 750 °C, while the dangling bonds in MoS2 improve the interfacial adhesion. These findings suggest that MoS2 holds great potential as a diffusion barrier for metal interconnects.
RESUMEN
To develop strong refractory high-entropy alloys for use at elevated temperatures as well as to overcome grain-boundary brittleness, an equimolar HfMoNbTaTiZr alloy was prepared, and a minor amount of boron (0.1 at.%) was added into the alloy. The microstructures of the alloys were characterized, and their macro-to-microscale mechanical properties were measured. The microstructural observations indicated that the matrices of both the alloys were composed of a body-centered cubic solid-solution structure, and the added boron induced the precipitation of hexagonal close-packed borides (most likely the (Hf, Zr)B2) at the grain boundaries. The modulus and hardness of differently oriented grains were about equivalent, suggesting a diminished anisotropy, and many small slips occurred on multiple {110} planes. While the hardness of the matrix was not increased, the intergranular precipitation of the borides markedly raised the hardness of the grain boundaries. Owing to the enhanced grain boundary cohesion, the work hardenability and ductility were effectively improved with the addition of boron.
RESUMEN
The authors would like to make corrections to a recently published paper [...].
RESUMEN
Inspired by Mantis shrimp, this work aims to suggest a bottom-up approach for the fabrication of nanonetwork hydroxyapatite (HAp) thin film using self-assembled polystyrene-block-polydimethylsiloxane (PS-b-PDMS) block copolymer (BCP) with a diamond nanostructure as a template for templated sol-gel reaction. By introducing poly(vinylpyrrolidone) (PVP) into precursors of calcium nitrate tetrahydrate and triethyl phosphite, which limits the growth of forming HAp nanoparticles, well-ordered nanonetwork HAp thin film can be fabricated. Based on nanoindentation results, the well-ordered nanonetwork HAp shows high energy dissipation compared to the intrinsic HAp. Moreover, the uniaxial microcompression test for the nanonetwork HAp shows high energy absorption per volume and high compression strength, outperforming many cellular materials due to the topologic effect of the well-ordered network at the nanoscale. This work highlights the potential of exploiting BCP templated synthesis to fabricate ionic solid materials with a well-ordered nanonetwork monolith, giving rise to the brittle-to-ductile transition, and thus appealing mechanical properties with the character of mechanical metamaterials.
Asunto(s)
Nanopartículas , Nanoestructuras , Durapatita/química , Polímeros/química , Nanoestructuras/química , Poliestirenos/químicaRESUMEN
Herein, this work aims to fabricate well-ordered nanonetwork epoxy resin modified with poly(butyl acrylate)-b-poly(methyl methacrylate) (PBA-b-PMMA) block copolymer (BCP) for enhanced energy dissipation using a self-assembled diblock copolymer of polystyrene-b-poly(dimethylsiloxane) (PS-b-PDMS) with gyroid and diamond structures as templates. A systematic study of mechanical properties using nanoindentation of epoxy resin with gyroid- and diamond-structures after modification revealed significant enhancement in energy dissipation, with the values of 0.36 ± 0.02 nJ (gyroid) and 0.43 ± 0.03 nJ (diamond), respectively, when compared to intrinsic epoxy resin (approximately 0.02 ± 0.002 nJ) with brittle characteristics. This enhanced property is attributed to the synergic effect of the deliberate structure with well-ordered nanonetwork texture and the toughening of BCP-based modifiers at the molecular level. In addition to the deliberate structural effect from the nanonetwork texture, the BCP modifier composed of epoxy-philic hard segment and epoxy-phobic soft segment led to dispersed soft-segment domains in the nanonetwork-structured epoxy matrix with superior interfacial strength for the enhancement of applied energy dissipation.
RESUMEN
To lower the charge leakage of a floating gate device and improve the operation performance of memory devices toward a smaller structure size and a higher component capability, two new types of floating gates composed of pn-type polysilicon or np-type polysilicon were developed in this study. Their microstructure and elemental compositions were investigated, and the sheet resistance, threshold voltages and erasing voltages were measured. The experimental results and charge simulation indicated that, by forming an n-p junction in the floating gate, the sheet resistance was increased, and the charge leakage was reduced because of the formation of a carrier depletion zone at the junction interface serving as an intrinsic potential barrier. Additionally, the threshold voltage and erasing voltage of the np-type floating gate were elevated, suggesting that the performance of the floating gate in the operation of memory devices can be effectively improved without the application of new materials or changes to the physical structure.
RESUMEN
Most medium entropy alloys (MEAs) exhibit excellent mechanical properties, but their applications are limited because of their high density. This study explores a series of lightweight nonequiatomic Ti65(AlCrNbV)35-xZrx (x = 3, 5, 7, and 10) MEAs with a low density, high strength, and high ductility. To achieve solid solution strengthening, Zr with a large atomic radius was used. In addition, various thermomechanical treatment parameters were adopted to further improve the MEAs' mechanical properties. The density of the MEAs was revealed to be approximately 5 g/cm3, indicating that they were lightweight. Through an X-ray diffraction analysis, the MEAs were revealed to have a single body-centered cubic structure not only in the as-cast state but also after thermomechanical treatment. In terms of mechanical properties, all the as-cast MEAs with Zr additions achieved excellent performance (>1000 MPa tensile yield strength and 20% tensile ductility). In addition, hot rolling effectively eliminated the defects of the MEAs; under a given yield strength, hot-rolled MEAs exhibited superior ductility relative to non-hot-rolled MEAs. Overall, the Ti65(AlCrNbV)28Zr7 MEAs exhibited an optimum combination of mechanical properties (yield strength > 1200 MPa, plastic strain > 15%) after undergoing hot rolling 50%, cold rolling 70%, and rapid annealing for 30 to 50 s (at a temperature of approximately 850 °C) with a heating rate of 15 K/s. With their extremely high specific yield strength (264 MPa·g/cm3) and high ductility (22%), the Ti65(AlCrNbV)28Zr7 MEAs demonstrate considerable potential for energy and transportation applications.
RESUMEN
OBJECTIVE: This study aimed to evaluate whether adjuvant radiotherapy (RT) can improve the treatment outcome of patients with locally advanced gastric cancer who underwent extensive lymph node dissection (ELND). MATERIALS AND METHODS: This retrospective study included patients with gastric cancer pathological stages IIA-IIIC at Taipei Tzu Chi Hospital between 2008 and 2015. Patients (a) aged >80 years, (b) with distant metastasis at diagnosis, (c) with coexisting malignancies, (d) who did not complete the prescribed RT course, and (e) who died 1 month after surgery were excluded. Among 420 patients diagnosed with gastric cancer, 98 were included. RESULTS: The median follow-up was 24.5 months. Of 39 patients who underwent adjuvant RT, 38 also received adjuvant chemotherapy (CT). Of 59 patients who did not receive adjuvant RT, only 34 received adjuvant CT. ELND was performed in 67.3% of the patients. The 5-year overall survival (OS) rate was 40%. In the univariate analyses, adjuvant CT regimen, 5-fluorouracil + leucovorin, was associated with worst outcome, while TS-1 was associated with better survival outcome (P = 0.018). The number of involved lymph nodes was strongly related to the OS and disease-free survival (DFS) (P < 0.001). We tried using different numbers of involved lymph nodes as a cutoff point and found that adjuvant RT significantly improved both OS and DFS in patients whose involved lymph nodes were ≥4 (OS, P = 0.017; DFS, P = 0.015). In multivariate analyses, better DFS was associated with negative surgical margin (P = 0.04), earlier disease stage (P = 0.001), adjuvant radiotherapy (P = 0.045), and adjuvant CT regimen TS-1 (P = 0.001). CONCLUSION: Adjuvant RT could improve DFS of patients with locally advanced gastric cancer with or without ELND. When the number of involved lymph nodes is ≥4, adjuvant RT is strongly suggested.