RESUMEN
Organic thioethers play an important role in the discovery of drugs and natural products. However, the green synthesis of organic sulfide compounds remains a challenging task. The convenient and efficient synthesis of 5-alkoxy-3-halo-4-methylthio-2(5H)-furanones from DMSO is performed via the mediation of 1,3-dibromo-5,5-dimethylhydantoin (DBDMH), affording a facile route for the sulfur-functionalization of 3,4-dihalo-2(5H)-furanones under transition metal-free conditions. This new approach has demonstrated the functionalization of non-aromatic Csp2-X-type halides with unique structures containing C-X, C-O, C=O and C=C bonds. Compared with traditional synthesis methods using transition metal catalysts with ligands, this reaction has many advantages, such as the lower temperature, the shorter reaction time, the wide substrate range and good functional group tolerance. Notably, DMSO plays multiple roles, and is simultaneously used as an odorless methylthiolating reagent and safe solvent.
RESUMEN
How to effectively improve the poor interfacial adhesion between polylactic acid/poly(butylene adipate-co-terephthalate) (PLA/PBAT) matrix and thermoplastic starch (TPS) is still a challenge. Therefore, this work aims to introduce a convenient method to enhance the performance of PLA/PBAT/TPS blend by melt reactive extrusion. Here, using 4,4'-methylene-bis(N,N-diglycidyl-aniline) (MBDG) containing four epoxy groups as a reactive compatibilizer, and respectively using 1-methylimidazole (MI) or triethylenediamine (TD) as a catalyzer, serial PLA/PBAT/TPS ternary bio-composites are successfully prepared via melt reactive extrusion. The results showed that, under the catalysis of organic base, especially MI, the epoxy groups of MBDG can effectively react with hydroxyl and carboxyl groups of PLA/PBAT and hydroxyl groups in TPS to form chain-expanded and cross-linked structures. The tensile strength of the composites is increased by 20.0 % from 21.1 MPa, and the elongation at break is increased by 182.4 % from 17.6 % owing to the chain extension and the forming of cross-linked structures. The molecular weight, thermal stability, crystallinity, and surface hydrophobicity of the materials are gradually improved with the increase of MBDG content. The melt fluidity of the composites is also improved due to the enhancement of compatibility. The obtained PLA/PBAT/TPS materials have the potential to be green plastic products with good properties.
Asunto(s)
Alquenos , Resinas Epoxi , Ácidos Ftálicos , Poliésteres , Adipatos , AlmidónRESUMEN
The bio-based lactic acid (LA) and the common metal ion chelating agent iminodiacetic acid (IDA) are used to design and prepare a polymeric sustained-release Pb2+ chelating agent by a brief one-step reaction. After the analysis on theoretical calculation for this reaction, poly(lactic acid-iminodiacetic acid) [P(LA-co-IDA)] with different monomer molar feed ratios is synthesized via direct melt polycondensation. P(LA-co-IDA) mainly has star-shaped structure, and some of them have two-core or three-core structure. Thus, a possible mechanism of the polymerization is proposed. The degradation rate of P(LA-co-IDA)s can reach 70% in 4 weeks. The change of IDA release rate is consistent with the trend of the degradation rate, and the good Pb2+ chelating performance is confirmed. P(LA-co-IDA) is expected to be developed as a lead poisoning treatment drug or Pb2+ adsorbent in the environment with long-lasting effect, and this research provides a new strategy for the development of such drugs.