RESUMEN
The synthesis of a new benzocyclobutene based polymer, PSBBB, designed as a dielectric material for use in organic thin film transistors was reported. Compared to conventional benzocyclobutene-based materials, the introduction of a butoxide substituent at the 7-position of the benzocyclobutene pendant unit on the polymer allowed PSBBB to be cross-linked at temperatures of 120 °C, thus rendering it compatible with the processing requirements of flexible plastic substrates. The cross-linking behavior of PSBBB was investigated by Fourier transform infrared spectroscopy and differential scanning calorimetry, demonstrating cross-linking of the polymer after curing at 120 °C. Bottom-gate bottom-contact organic thin film transistors were fabricated using PSBBB as dielectric, affording a performance comparable to that of other dielectric polymeric materials.
RESUMEN
A well-defined series of long and soluble isoindigo thienoacene oligomers have been synthesized from a novel electron deficient building block: benzo[1,2-b:4,5-b']bis[b]benzothiophene bislactams. Extension of the π-conjugated systems facilitates control of the optical, electronic and device characteristics.
RESUMEN
The molecular dynamics of organic semiconductor blend layers are likely to affect the optoelectronic properties and the performance of devices such as solar cells. We study the dynamics (5-50 ps) of the poly(3-hexylthiophene) (P3HT): phenyl-C61-butyric acid methyl ester (PCBM) blend by time-of-flight quasi-elastic neutron scattering, at temperatures in the range 250-360 K, thus spanning the glass transition temperature region of the polymer and the operation temperature of an OPV device. The behavior of the QENS signal provides evidence for the vitrification of P3HT upon blending, especially above the glass transition temperature, and the plasticization of PCBM by P3HT, both dynamics occurring on the picosecond time scale.