RESUMEN
AlGaN-based vertical type high power ultraviolet-C light emitting diodes (UV-C LEDs), which have a Ga-face n-contact structure, were fabricated on a LED epilayer transferred to a carrier wafer through a laser lift-off (LLO) process. A significant light extraction enhancement of the vertical chip by using a highly reflective ITO/Al p-type electrode is demonstrated, along with surface roughening. A GaN-free LED epi structure is employed to prevent light absorption in the UV-C wavelength region. The vertical chip with the ITO/Al reflector and n-AlGaN surface roughening exhibited a high light output power of 104.4mW with a peak wavelength of 277.6nm at an injection current of 350mA. Comparing the device characteristics of the vertical chip and the flip chip showed that the light output power of the vertical chip was 1.31 times higher than that of the flip chip at 350mA. In particular, with the high power vertical type UV-C LED, a maximum light output power of 630mW could be achieved at a current of 3.5A, and this is mainly attributed to efficient heat dissipation through a metal substrate and the resulting relatively lower junction temperature of the vertical chip.
RESUMEN
We investigated the effect of phosphor deposition methods on the correlated color temperature (CCT), luminous flux and thermal characteristics of packaged white light-emitting diodes (WLEDs) for use in mobile display products. For both the samples, the CCT decreased with increasing viewing angle. Phosphor sedimentation samples displayed much better angular color uniformity than phosphor dispersion samples. The phosphor sedimentation sample had higher luminous flux and luminous efficacy at 20 mA than the phosphor dispersion sample. The phosphor sedimentation sample displayed much better high-temperature/humidity (85 °C/85%) reliability and lower package temperatures compared with the phosphor dispersion sample.
RESUMEN
We demonstrated the growth of crack-free high-quality GaN-based UV vertical LEDs (VLEDs) (λ = 365 nm) on 6-inch sapphire substrates by using an ex-situ sputtered AlN nucleation layer (NL) and compared their performance with that of UV VLEDs with an in situ low temperature (LT) AlGaN NL. The X-ray diffraction (XRD) results showed that the ex-situ AlN sample contained lower densities of screw-type and edge-type threading dislocations than the in situ AlGaN NL sample. The micro-Raman results revealed that the ex-situ AlN sample was under more compressive stress than the in situ AlGaN sample. As the current was increased, the electroluminescence peaks of both of the samples blue-shifted, reached a minimum wavelength at 1000 mA, and then slightly red-shifted. Packaged VLEDs with the ex-situ AlN NL yielded 6.5% higher light output power at 500 mA than that with the in situ AlGaN NL. The maximum EQEs of the VLED with the in situ AlGaN and ex-situ AlN NLs were 43.7% and 48.2%, respectively. Based on the XRD and Raman results, the improved light output power of the ex-situ AlN sample is attributed to the lower density of TDs.
RESUMEN
We investigated the optical and electrical properties of red AlGaInP light-emitting diodes (LEDs) as functions of chip size, p-cladding layer thickness, and the number of multi-quantum wells (MQWs). External quantum efficiency (EQE) decreased with decreasing chip size. The ideality factor gradually increased from 1.47 to 1.95 as the chip size decreased from 350 µm to 15 µm. This indicates that the smaller LEDs experienced larger carrier loss due to Shockley-Read-Hall nonradiative recombination at sidewall defects. S parameter, defined as ∂lnL/∂lnI, increased with decreasing chip size. Simulations and experimental results showed that smaller LEDs with 5 pairs of MQWs had over 30% higher IQE at 5 A/cm2 than the LED with 20 pairs of MQWs. These results show that the optimization of the number of QWs is needed to obtain maximum EQE of micro-LEDs.