RESUMEN
Organic conducting polymers are promising electrode materials for printable organic electronics. One of the most studied conducting polymers is PEDOT: PSS, which is sufficiently conductive and transparent, but which shows some drawbacks, such as hygroscopicity and acidity. A new approach to stabilize PEDOT in aqueous dispersions involves the replacement of PSS with a basic polyanion based on a polystyrene backbone with (trifluoromethylsulfonyl)imide (TSFI) side groups. The PEDOT: PSTFSIK dispersions were obtained by oxidative polymerization of EDOT in an aqueous PSTFSIK solution and were characterized with regard to their composition, morphology, doping, rheological behavior, and optoelectronic performance. The PEDOT: PSTFSIK dispersions showed excellent printability and good optoelectronic performance (238â Ohm sq(-1) at 91% transmittance, σ>260â S cm(-1)) and were successfully integrated as flexible electrodes in OLED and OPV devices.
RESUMEN
A novel approach to obtaining nanocomposite materials using anionic sequential polymerization and post-synthetic esterification reactions with chemically modified graphene sheets (CMGs) is reported. The anionically synthesized diblock copolymer precursors of the PS-b-PI-OH type were grafted to the chemically modified -COOH groups of the CMGs, giving rise to the final composite materials, namely polystyrene-b-poly(isoprene)-g-CMGs, which exhibited enhanced physicochemical properties. The successful synthesis was determined through multiple molecular characterization techniques together with thermogravimetric analysis for the verification of increased thermal stability, and the structure/properties relationship was justified through transmission electron microscopy. Furthermore, the arrangement of CMGs utilizing lamellar and cylindrical morphologies was studied in order to determine the effect of the loaded CMGs in the adopted topologies.