Experimental and Theoretical Studies on Acid Corrosion Inhibition of API 5L X70 Steel with Novel 1-N-α-d-Glucopyranosyl-1H-1,2,3-Triazole Xanthines.

A series of novel 1-N-α-d-glucopyranosyl-1H-1,2,3-triazole xanthines was synthesized from azido sugars (glucose, galactose, and lactose) and propargyl xanthines (theophylline and theobromine) using a typical copper (I)-catalyzed azide-alkyne 1,3-dipolar cycloaddition. The corrosion inhibition activities of these new carbohydrate-xanthine compounds were evaluated by studying the corrosion of API 5 L X70 steel in a 1 M HCl medium. The results showed that, at 10 ppm, a 90% inhibition efficiency was reached by electrochemical impedance spectroscopy. The inhibitory efficiency of these molecules is explained by means of quantum chemical calculations of the protonated species with the solvent effect, which seems to better represent the actual situation of the experimental conditions. Some quantum chemical parameters were analyzed to characterize the inhibition performance of the tested molecules.

A General Use QSAR-ARX Model to Predict the Corrosion Inhibition Efficiency of Drugs in Terms of Quantum Mechanical Descriptors and Experimental Comparison for Lidocaine.

A study of 250 commercial drugs to act as corrosion inhibitors on steel has been developed by applying the quantitative structure-activity relationship (QSAR) paradigm. Hard-soft acid-base (HSAB) descriptors were used to establish a mathematical model to predict the corrosion inhibition efficiency (IE%) of several commercial drugs on steel surfaces. These descriptors were calculated through third-order density-functional tight binding (DFTB) methods. The mathematical modeling was carried out through autoregressive with exogenous inputs (ARX) framework and tested by fivefold cross-validation. Another set of drugs was used as an external validation, obtaining SD, RMSE, and MSE, obtaining 6.76%, 3.89%, 7.03%, and 49.47%, respectively. With a predicted value of IE% = 87.51%, lidocaine was selected to perform a final comparison with experimental results. By the first time, this drug obtained a maximum IE%, determined experimentally by electrochemical impedance spectroscopy measurements at 100 ppm concentration, of about 92.5%, which stands within limits of 1 SD from the predicted ARX model value. From the qualitative perspective, several potential trends have emerged from the estimated values. Among them, macrolides, alkaloids from Rauwolfia species, cephalosporin, and rifamycin antibiotics are expected to exhibit high IE% on steel surfaces. Additionally, IE% increases as the energy of HOMO decreases. The highest efficiency is obtained in case of the molecules with the highest ω and ΔN values. The most efficient drugs are found with pKa ranging from 1.70 to 9.46. The drugs recurrently exhibit aromatic rings, carbonyl, and hydroxyl groups with the highest IE% values.

4-Phenylcoumarin (4-PC) Glucoside from Exostema caribaeum as Corrosion Inhibitor in 3% NaCl Saturated with CO2 in AISI 1018 Steel: Experimental and Theoretical Study.

The corrosion inhibition of 5-O-ß-D-glucopyranosyl-7-methoxy-3',4'-dihydroxy-4-phenylcoumarin (4-PC) in AISI 1018 steel immersed in 3% NaCl + CO2 was studied by electrochemical impedance spectroscopy (EIS). The results showed that, at just 10 ppm, 4-PC exerted protection against corrosion with Õ² = 90% and 97% at 100 rpm. At static conditions, the polarization curves indicated that, at 5 ppm, the inhibitor presented anodic behavior, while at 10 and 50 ppm, there was a cathodic-type inhibitor. The inhibitor adsorption was demonstrated to be chemisorption, according to the Langmuir isotherm for 100 and 500 rpm. By means of SEM-EDS, the corrosion inhibition was demonstrated, as well as the fact that the organic compound was effective for up to 72 h of immersion. At static conditions, dispersion-corrected density functional theory results reveal that the chemical bonds established by the phenyl group of 4-PC are responsible of the chemisorption on the steel surface. According with Fukui reactivity indices, the molecules adsorbed on the metal surface provide a protective cover against nucleophilic and electrophilic attacks, pointing to the corrosion inhibition properties of 4-PC.

Study of SCC of X70 Steel Immersed in Simulated Soil Solution at Different pH by EIS.

An electrochemical study of stress corrosion cracking (SCC) of API X70 steel in a simulated soil solution at different pH values (3, 8 and 10) was carried out. The stress conditions were implemented by slow strain rate stress test (SSRT) and the SCC process was simultaneously monitored by electrochemical impedance spectroscopy (EIS). Fracture surface analysis and corrosion product analysis were performed by scanning electron microscopy (SEM) and X-ray diffraction (XRD), respectively. The results show that the susceptibility to SCC was higher as the pH decreases. In the acid solution, hydrogen evolution can occur by H+ and H2CO3 reduction, and more atomic hydrogen can diffuse into the steel, producing embrittlement. EIS results indicated that the anodic dissolution contributed to SCC process by reducing the charge transfer resistances during the SSRT test. While SEM micrographs shown a general corrosion morphology on the longitudinal surface of samples. At higher pH (pH 8 and pH 10), the SCC susceptibility was lower, which it is attributed to the presence of corrosion products film, which could have limited the process. Using the angle phase (φ) value it was determined that the cracking process started at a point close to the yield strength (YS).