RESUMEN
Al-based composites incorporating multilayered graphene sheets were developed via a facile approach. The multilayered graphene sheets were fabricated from the expanded graphite via a simple mechanical exfoliation process. The facile extrusion molding process with Al powder and graphene sheets exfoliated from expended graphite afforded Al-based graphene composite rods. These composites showed enhanced thermal conductivity compared to the pristine Al rods. Moreover, the Al-based multilayered graphene sheet composites exhibited lower interfacial contact resistance between graphene-based electrodes than the pristine Al. With increasing degrees of dispersion, the number of exposed graphene sheets increases, thereby significantly decreasing the interfacial contact resistance between the composite and external graphite electrode.
RESUMEN
The organic high-energy material pentaerythritol tetranitrate (PETN) was incorporated at low concentrations into Al (100 nm)/Fe(2)O(3) metastable intersitital composites (MIC) to form a hybrid organic/inorganic high-energy material. Studies of the dynamics of energy release were carried out by initiating the reaction photothermally with a single 8 ns pulse of the 1064 nm fundamental of a Nd:YAG laser. The reaction dynamics were measured using time-resolved spectroscopy of the light emitted from the deflagrating material. Two parameters were measured: the time to initiation and the duration of the deflagration. The presence of small amounts of PETN (16 mg/g of MIC) results in a dramatic decrease in the initiation time. This is attributed to a contribution to the temperature of the reacting system from the combustion of the PETN that, at lower loadings, appears to follow an Arrhenius dependence. The presence of PETN was also found to reduce the energy density required for single-pulse photothermal initiation by an order of magnitude, suggesting that hybrid materials such as this may be engineered to optimize their use as an efficient photodetonation medium.
RESUMEN
A carbon nanotube yarn core graphitic shell hybrid fiber was fabricated via facile heat treatment of epoxy-based negative photoresist (SU-8) on carbon nanotube yarn. The effective encapsulation of carbon nanotube yarn in carbon fiber and a glassy carbon outer shell determines their physical properties. The higher electrical conductivity (than carbon fiber) of the carbon nanotube yarn overcomes the drawbacks of carbon fiber/glassy carbon, and the better properties (than carbon nanotubes) of the carbon fiber/glassy carbon make up for the lower thermal and mechanical properties of the carbon nanotube yarn via synergistic hybridization without any chemical doping and additional processes.
RESUMEN
Uniform high-quality iron oxide thin films can be formed from the spin coating of iron oxide/hydroxide sol-gels on a silicon substrate. Thermal processing of the films at temperatures of approximately 300 degrees C results in the transformation of films into a ternary layered structure with iron oxide, Fe(2)O(3), at the surface, characterized by Mossbauer spectroscopy, and reduced, metallic iron characterized by depth profiling of the surface by X-ray photoelectron spectroscopy as a function of Ar(+) etching. Imaging of the etched surface by scanning electron microscopy reveals two distinct regions at the interface, nanoparticles that are very iron-rich separated by an unstructured region that is somewhat less iron-rich. The results demonstrate a synthetic protocol for the spontaneous formaton of a ternary layered structure from a simple one-step preparation.