Phosphoric acid containing proanthocyanidin enhances bond stability of resin/dentin interface.

Proanthocyanidin (PA) is a promising dentin biomodifier due to its ability to stabilize collagen fibrils against degradation by matrix metalloproteinases (MMPs); however, the most effective protocol to incorporate PA into bonding procedures is still unclear. This study evaluated the effect of dentin biomodification with a PA acid etchant on MMP activity, adhesive interface morphology and resin-dentin microtensile bond strength. Sound extracted human molars were flattened to expose dentin and acid-etched for 15 s according to the groups: EXP - experimental phosphoric acid; EXP+PA - experimental phosphoric acid 10% PA; TE - total-etching system; SE - self-etching system. Samples were restored with composite resin and stored in distilled water (37ºC). MMP activity and interface morphology were analyzed after 24 h by in situ zymography (n=6) and scanning electron microscopy (n=3), respectively. The resin-dentin microtensile bond strength (µTBS) was evaluated after 24 h and 6 months storage (n=6). Significantly higher MMP activity was detected in etched dentin compared with untreated dentin (p<0.05), but no difference among acid groups was found. Resin tags and microtags, indicative of proper adhesive system penetration in dentinal tubules and microtubules, were observed along the hybrid layer in all groups. There was no difference in µTBS between 24 h and 6 months for EXP+PA; moreover, it showed higher long-term µTBS compared with TE and EXP (p<0.05). The results suggest that 15 s of biomodification was not sufficient to significantly reduce MMP activity; nonetheless, EXP+PA was still able to improve resin-dentin bond stability compared with total- and self-etching commercial systems.

Phosphoric acid containing proanthocyanidin enhances bond stability of resin/dentin interface

Abstract Proanthocyanidin (PA) is a promising dentin biomodifier due to its ability to stabilize collagen fibrils against degradation by matrix metalloproteinases (MMPs); however, the most effective protocol to incorporate PA into bonding procedures is still unclear. This study evaluated the effect of dentin biomodification with a PA acid etchant on MMP activity, adhesive interface morphology and resin-dentin microtensile bond strength. Sound extracted human molars were flattened to expose dentin and acid-etched for 15 s according to the groups: EXP - experimental phosphoric acid; EXP+PA - experimental phosphoric acid 10% PA; TE - total-etching system; SE - self-etching system. Samples were restored with composite resin and stored in distilled water (37ºC). MMP activity and interface morphology were analyzed after 24 h by in situ zymography (n=6) and scanning electron microscopy (n=3), respectively. The resin-dentin microtensile bond strength (μTBS) was evaluated after 24 h and 6 months storage (n=6). Significantly higher MMP activity was detected in etched dentin compared with untreated dentin (p<0.05), but no difference among acid groups was found. Resin tags and microtags, indicative of proper adhesive system penetration in dentinal tubules and microtubules, were observed along the hybrid layer in all groups. There was no difference in μTBS between 24 h and 6 months for EXP+PA; moreover, it showed higher long-term μTBS compared with TE and EXP (p<0.05). The results suggest that 15 s of biomodification was not sufficient to significantly reduce MMP activity; nonetheless, EXP+PA was still able to improve resin-dentin bond stability compared with total- and self-etching commercial systems.

Resumo A proantocianidina (PA) é um biomodificador dentinário promissor devido a sua capacidade de estabilizar as fibrilas colágenas contra a degradação por metaloproteinases da matriz (MMPs); no entanto, o protocolo mais eficaz para a incorporação de PA em procedimentos adesivos ainda não está claro. Este estudo avaliou o efeito da biomodificação da dentina com um condicionador ácido contendo PA na atividade de MMPs, morfologia da interface adesiva e resistência à microtração resina-dentina. Molares humanos extraídos foram lixados para exposição da dentina e condicionados com ácido por 15 s de acordo com os grupos: EXP - ácido fosfórico experimental; EXP+PA - ácido fosfórico experimental com 10% PA; TE - sistema total-etch; SE - sistema self-etch. As amostras foram restauradas com resina composta e armazenadas em água destilada (37ºC). A atividade de MMP e morfologia da interface foram analisadas após 24 h por zimografia in situ (n=6) e microscopia eletrônica de varredura (n=3), respectivamente. A resistência à microtração resina-dentina (μTBS) foi avaliada após 24 horas e 6 meses de armazenamento (n=6). Atividade de MMP detectada na dentina condicionada foi significativamente maior em comparação com a dentina não tratada (p <0,05), mas não houve diferenças entre os diferentes ácidos. Tags e microtags de resina, indicativos de uma penetração adequada do sistema adesivo nos túbulos e microtúbulos dentinários, foram observadas ao longo da camada híbrida em todos os grupos. Não houve diferença entre os valores de μTBS de 24 h e 6 meses para EXP+PA; além disso, EXP+PA apresentou maiores valores de μTBS após 6 meses em comparação com TE e EXP (p <0,05). Os resultados sugerem que a biomodificação por 15 s não foi suficiente para reduzir significativamente a atividade de MMP; apesar disso, EXP + PA foi capaz de melhorar a estabilidade da interface resina-dentina em comparação com sistemas total- e self-etch comerciais.