RESUMEN
Green approaches for nanoparticle synthesis have emerged as biocompatible, economical, and environment-friendly alternatives to counteract the menace of microbial drug resistance. Recently, the utilization of honey as a green source to synthesize Fe2O3-NPs has been introduced, but its antibacterial activity against one of the opportunistic MDR pathogens, Klebsiella pneumoniae, has not been explored. Therefore, this study employed Apis mellifera honey as a reducing and capping agent for the synthesis of iron oxide nanoparticles (Fe2O3-NPs). Subsequent to the characterization of nanoparticles, their antibacterial, antioxidant, and anti-inflammatory properties were appraised. In UV-Vis spectroscopic analysis, the absorption band ascribed to the SPR peak was observed at 350 nm. XRD analysis confirmed the crystalline nature of Fe2O3-NPs, and the crystal size was deduced to be 36.2 nm. Elemental analysis by EDX validated the presence of iron coupled with oxygen in the nanoparticle composition. In ICP-MS, the highest concentration was of iron (87.15 ppm), followed by sodium (1.49 ppm) and other trace elements (<1 ppm). VSM analysis revealed weak magnetic properties of Fe2O3-NPs. Morphological properties of Fe2O3-NPs revealed by SEM demonstrated that their average size range was 100-150 nm with a non-uniform spherical shape. The antibacterial activity of Fe2O3-NPs was ascertained against 30 clinical isolates of Klebsiella pneumoniae, with the largest inhibition zone recorded being 10 mm. The MIC value for Fe2O3-NPs was 30 µg/mL. However, when mingled with three selected antibiotics, Fe2O3-NPs did not affect any antibacterial activity. Momentous antioxidant (IC50 = 22 µg/mL) and anti-inflammatory (IC50 = 70 µg/mL) activities of Fe2O3-NPs were discerned in comparison with the standard at various concentrations. Consequently, honey-mediated Fe2O3-NP synthesis may serve as a substitute for orthodox antimicrobial drugs and may be explored for prospective biomedical applications.
Asunto(s)
Miel , Abejas , Animales , Antioxidantes/farmacología , Estudios Prospectivos , Antibacterianos/farmacología , Hierro , Klebsiella pneumoniae , Nanopartículas Magnéticas de Óxido de HierroRESUMEN
Herein, polymeric cryogels containing poly(N-isopropylacrylamide) were synthesized by cryo-polymerization at subzero temperature. The synthesized cryogels were loaded with silver and palladium nanoparticles by the chemical reduction method at room temperature using the reducing agent NaBH4. Moreover, for comparison with cryogels, pure poly(N-isopropylacrylamide) hydrogel and its silver hybrid were also prepared by the conventional method at room temperature. The chemical structure and functional group analysis of the pure cryogels was confirmed by Fourier transform infrared spectroscopy. The synthesis of hybrid cryogels was confirmed by the X-ray diffraction technique and energy dispersive X-ray. The pore size and surface morphology of the pure cryogels, their respective hybrid cryogels and of conventional hydrogels were studied by using the scanning electron microscopy technique. The hybrid cryogels were successfully used as a catalyst for the degradation of methyl orange dye. The degradation performance of the hybrid cryogels was much better than its counterpart hybrid hydrogel for methyl orange dye. The effect of temperature and amount of catalyst on catalytic performance was studied by UV-visible spectroscopy. The reduction follows pseudo-first-order reaction kinetics. In addition, the antibacterial activities of these cryogels were evaluated against Gram-positive bacteria (Staphylococcus aureus, ATCC: 2593) and Gram-negative bacteria (Escherichia coli, ATCC: 25922). Both hybrid cryogels have shown much better antibacterial activity for these two strains of bacteria compared to pure cryogels. The results indicate that these cryogels are potential candidates for water purification systems as well as biomedical applications.
RESUMEN
In this study, we synthesized hybrid systems based on manganese oxide@zinc oxide (Mn3O4@ZnO), using sol gel and hydrothermal methods. The hybrid materials exhibited hierarchical morphologies and structures characterized by the hexagonal phase of ZnO and the tetragonal phase of Mn3O4. The hybrid materials were tested for degradation of methylene blue (MB), methyl orange (MO), and malachite green (MG) under ultraviolet (UV) light illumination. The aim of this work was to observe the effect of various amounts of Mn3O4 in enhancing the photocatalytic properties of ZnO-based hybrid structures towards the degradation of MB, MO and MG. The ZnO photocatalyst showed better performance with an increasing amount of Mn3O4, and the degradation efficiency for the hybrid material containing the maximum amount of Mn3O4 was found to be 94.59%, 89.99%, and 97.40% for MB, MO and MG, respectively. The improvement in the performance of hybrid materials can be attributed to the high charge separation rate of electron-hole pairs, the co-catalytic role, the large number of catalytic sites, and the synergy for the production of high quantities of oxidizing radicals. The performance obtained from the various Mn3O4@ZnO hybrid materials suggest that Mn3O4 can be considered an effective co-catalyst for a wide range of photocatalytic materials such as titanium dioxide, tin oxide, and carbon-based materials, in developing practical hybrid photocatalysts for the degradation of dyes and for wastewater treatment.