RESUMEN
The locally defined growth of carbon nanofibers with lambda shape in an open flame process is demonstrated. Via the growth time, the geometry of the structures can be tailored to a Λ- or λ-type shape. Microchannel cantilever spotting and dip-pen nanolithography are utilized for the deposition of catalytic salt NiCl2 · 6H2 O for locally controlled growth of lambda-shaped carbon nanofibers. Rigorous downscaling reveals a critical catalytic salt volume of 0.033 µm³, resulting in exactly one lambda-shaped carbon nanofiber at a highly predefined position. An empirical model explains the observed growth process.
RESUMEN
Peptide microarrays are a fast-developing field enabling the mapping of linear epitopes in the immune response to vaccinations or diseases and high throughput studying of protein-protein interactions. In this respect, a rapid label-free measurement of protein layer topographies in the array format is of great interest but is also a great challenge due to the extremely low aspect ratios of the peptide spots. We have demonstrated the potential of vertical scanning interferometry (VSI) for a detailed morphological analysis of peptide arrays and binding antibodies. The VSI technique is shown to scan an array area of 5.1 square millimeters within 3â»4 min at a resolution of 1.4 µm lateral and 0.1 nm vertical in the full automation mode. Topographies obtained by VSI do match the one obtained by AFM measurements, demonstrating the accuracy of the technique. A detailed topology of peptide-antibody layers on single spots was measured. Two different measurement regions are distinguished according to the antibody concentration. In the case of weakly diluted serum, the thickness of the antibody layer is independent of the serum dilution and corresponds to the physical thickness of the accumulated antibody layer. In strongly diluted serum, the thickness measured via VSI is linearly proportional to the serum dilution.
RESUMEN
Background: Inspired by structural hierarchies and the related excellent mechanical properties of biological materials, we created a smoothly graded micro- to nanoporous structure from a thermoplastic polymer. Results: The viscoelastic properties for the different pore sizes were investigated in the glassy regime by dynamic flat-punch indentation. Interestingly, the storage modulus was observed to increase with increasing pore-area fraction. Conclusion: This outcome appears counterintuitive at first sight, but can be rationalized by an increase of the pore wall thickness as determined by our quantitative analysis of the pore structure. Therefore, our approach represents a non-chemical way to tune the elastic properties and their local variation for a broad range of polymers by adjusting the pore size gradient.
RESUMEN
Inspired by the white beetle of the genus Cyphochilus, we fabricate ultra-thin, porous PMMA films by foaming with CO2 saturation. Optimising pore diameter and fraction in terms of broad-band reflectance results in very thin films with exceptional whiteness. Already films with 60 µm-thick scattering layer feature a whiteness with a reflectance of 90%. Even 9 µm thin scattering layers appear white with a reflectance above 57%. The transport mean free path in the artificial films is between 3.5 µm and 4 µm being close to the evolutionary optimised natural prototype. The bio-inspired white films do not lose their whiteness during further shaping, allowing for various applications.
RESUMEN
Based on magnetic-field-assisted growth of carbon nanofibers in an open ethanol flame we fabricated arrays of carbon nanofibers with different degrees of orientation. Inspired by the dry adhesive system of geckos we investigated the adhesive properties of such carbon nanofiber arrays with ordered and random orientation. AFM-based force spectroscopy revealed that adhesion force and energy rise linear with preload force. Carbon nanofibers oriented by a magnetic field show a 68% higher adhesion (0.66 N/cm2) than the randomly oriented fibers. Endurance tests revealed that the carbon nanofiber arrays withstand 50.000 attachment/detachment cycles without observable wear.