RESUMEN
Nanoselective area growth (NSAG) by metal organic vapor phase epitaxy of high-quality InGaN nanopyramids on GaN-coated ZnO/c-sapphire is reported. Nanopyramids grown on epitaxial low-temperature GaN-on-ZnO are uniform and appear to be single crystalline, as well as free of dislocations and V-pits. They are also indium-rich (with homogeneous 22% indium incorporation) and relatively thick (100 nm). These properties make them comparable to nanostructures grown on GaN and AlN/Si templates, in terms of crystallinity, quality, morphology, chemical composition and thickness. Moreover, the ability to selectively etch away the ZnO allows for the potential lift-off and transfer of the InGaN/GaN nanopyramids onto alternative substrates, e.g. cheaper and/or flexible. This technology offers an attractive alternative to NSAG on AlN/Si as a platform for the fabrication of high quality, thick and indium-rich InGaN monocrystals suitable for cheap, flexible and tunable light-emitting diodes.
RESUMEN
We investigate the optical signature of the interface in a single MgZnO/ZnO heterojunction, which exhibits two orders of magnitude lower resistivity and 10 times higher electron mobility compared with the MgZnO/Al2O3 film grown under the same conditions. These impressive transport properties are attributed to increased mobility of electrons at the MgZnO/ZnO heterojunction interface. Depth-resolved cathodoluminescence and photoluminescence studies reveal a 3.2 eV H-band optical emission from the heterointerface, which exhibits excitonic properties and a localization energy of 19.6 meV. The emission is attributed to band-bending due to the polarization discontinuity at the interface, which leads to formation of a triangular quantum well and localized excitons by electrostatic coupling.
RESUMEN
A correction to this article has been published and is linked from the HTML version of this paper. The error has been fixed in the paper.