Variable-Wavelength Quick Scanning Nanofocused X-Ray Microscopy for In Situ Strain and Tilt Mapping.

Compression of micropillars is followed in situ by a quick nanofocused X-ray scanning microscopy technique combined with 3D reciprocal space mapping. Compared to other attempts using X-ray nanobeams, it avoids any motion or vibration that would lead to a destruction of the sample. The technique consists of scanning both the energy of the incident nanofocused X-ray beam and the in-plane translations of the focusing optics along the X-ray beam. Here, the approach by imaging the strain and lattice orientation of Si micropillars and their pedestals during in situ compression is demonstrated. Varying the energy of the incident beam instead of rocking the sample and mapping the focusing optics instead of moving the sample supplies a vibration-free measurement of the reciprocal space maps without removal of the mechanical load. The maps of strain and lattice orientation are in good agreement with the ones recorded by ordinary rocking-curve scans. Variable-wavelength quick scanning X-ray microscopy opens the route for in situ strain and tilt mapping toward more diverse and complex materials environments, especially where sample manipulation is difficult.

In situ compression of micropillars under coherent X-ray diffraction: a case study of experimental and data-analysis constraints.

Micropillar compression is a method of choice to understand mechanics at small scale. It is mainly studied with electron microscopy or white-beam micro-Laue X-ray diffraction. The aim of the present article is to show the possibilities of the use of diffraction with a coherent X-ray beam. InSb micropillars in epitaxy with their pedestals (i.e. their support) are studied in situ during compression. Firstly, an experiment using a collimated beam matching the pillar size allows determination of when the sample enters the plastic regime, independently of small defects induced by experimental artefacts. A second experiment deals with scanning X-ray diffraction maps with a nano-focused beam; despite the coherence of the beam, the contributions from the pedestal and from the micropillar in the diffraction patterns can be separated, making possible a spatially resolved study of the plastic strain fields. A quantitative measurement of the elastic strain field is nevertheless hampered by the fact that the pillar diffracts at the same angles as the pedestal. Finally, no image reconstructions were possible in these experiments, either in situ due to a blurring of the fringes during loading or post-mortem because the defect density after yielding was too high. However, it is shown how to determine the elastic bending of the pillar in the elastic regime. Bending angles of around 0.3° are found, and a method to estimate the sample's radius of curvature is suggested.

Size-induced twinning in InSb semiconductor during room temperature deformation.

Room-temperature deformation mechanism of InSb micro-pillars has been investigated via a multi-scale experimental approach, where micro-pillars of 2 µm and 5 µm in diameter were first fabricated by focused ion beam (FIB) milling and in situ deformed in the FIB-SEM by micro-compression using a nano-indenter equipped with a flat tip. Strain rate jumps have been performed to determine the strain rate sensitivity coefficient and the related activation volume. The activation volume is found to be of the order of 3-5 b3, considering that plasticity is mediated by Shockley partial dislocations. Transmission electron microscopy (TEM) thin foils were extracted from deformed micro-pillars via the FIB lift-out technique: TEM analysis reveals the presence of nano-twins as major mechanism of plastic deformation, involving Shockley partial dislocations. The presence of twins was never reported in previous studies on the plasticity of bulk InSb: this deformation mechanism is discussed in the context of the plasticity of small-scale samples.

Revealing the role of microstructure architecture on strength and ductility of Ni microwires by in-situ synchrotron X-ray diffraction.

Deformation mechanisms of cold drawn and electropolished nickel microwires are studied by performing in-situ monotonous and cyclic tensile tests under synchrotron radiation. X-ray diffraction tests allow probing elastic strains in the different grain families and establishing a link with the deformation mechanisms taking place within the microwires. The measurements were carried out on several microwires with diameters ranging from as-drawn 100 µm down to 40 µm thinned down by electropolishing. The as-drawn wires exhibit a core-shell microstructure with <111> fiber texture dominant in core and heterogeneous dual fiber texture <111> and <100> in the shell. Reduction of specimen size by electropolishing results in a higher yield stress and tensile strength along with reduced ductility. In-situ XRD analysis revealed that these differences are linked to the global variation in microstructure induced by shell removal with electropolishing, which in turn affects the load sharing abilities of grain families. This study thus proposes a new way to increase ductility and retain strength in nickel microwires across different diameters by tuning the microstructure architecture.

Evidence of dislocation cross-slip in MAX phase deformed at high temperature.

Ti2AlN nanolayered ternary alloy has been plastically deformed under confining pressure at 900°C. The dislocation configurations of the deformed material have been analyzed by transmission electron microscopy. The results show a drastic evolution compared to the dislocation configurations observed in the Ti2AlN samples deformed at room temperature. In particular, they evidence out-of-basal-plane dislocations and interactions. Moreover numerous cross-slip events from basal plane to prismatic or pyramidal planes are observed. These original results are discussed in the context of the Brittle-to-Ductile Transition of the nanolayered ternary alloys.