Rietveld Refinement, Morphology, and Optical and Photoluminescence Properties of a ß-Ag1.94Cu0.06MoO4 Solid Solution.

Corner-truncated cubic ß-Ag1.94Cu0.06MoO4 microcrystals were synthesized using the hydrothermal method. These were investigated by X-ray diffraction, confirming obtention of the spinel structure Fd3̅m. Through Raman spectroscopy are confirmed all modes for the point group of Oh7. The Egap shows a decrease of the band gap from 3.20 to 3.07 eV, with reduction of the conduction band occurring from -0.20 eV (ß-Ag2MoO4) to -0.13 eV (ß-Ag1.94Cu0.06MoO4), suggesting a p-type behavior for the Cu2+ ion. The field-emission scanning electron microscopy images confirm the morphological changes for ß-Ag2MoO4, where potato-like microcrystals were found. Meanwhile, corner-truncated cubic microcrystals for ß-Ag1.94Cu0.06MoO4. The photoluminescence (PL) spectrum confirms the increase in the PL emission for ß-Ag1.94Cu0.06MoO4, with suppression of the deep defects occurring in the structure caused by oxygen and silver atoms. In contrast, the green region is intensified because of distortions of the Ag-O and Mo-O bonds. Therefore, the ß-Ag1.94Cu0.06MoO4 solid solution has PL emission with CCT (4510 K) and CIE coordinates (x = 0.372 and y = 0.433), which could be interesting properties for applications as light-emitting diodes.