Zincophilic Electrode Interphase with Appended Proton Reservoir Ability Stabilizes Zn Metal Anodes.

The rampant dendrites and hydrogen evolution reaction (HER) resulting from the turbulent interfacial evolution at the anode/electrolyte are the main culprits of short lifespan and low Coulombic efficiency of Zn metal batteries. In this work, a versatile protective coating with excellent zincophilic and amphoteric features is constructed on the surface of Zn metal (ZP@Zn) as dendrite-free anodes. This kind of protective coating possesses the advantages of reversible proton storage and rapid desolvation kinetics, thereby mitigating the HER and facilitating homogeneous nucleation concomitantly. Furthermore, the space charge polarization effect promotes charge redistribution to achieve uniform Zn deposition. Accordingly, the ZP@Zn symmetric cell manifests excellent reversibility at an ultrahigh cumulative plating capacity of 4700 mAh cm-2 and stable cycling at 80 % depth of discharge (DOD). The ZP@Zn//V6 O13 pouch cell also reveals superior cycling stability with a high capacity of 326.6 mAh g-1 .

A smelting-rolling strategy for ZnIn bulk phase alloy anodes.

Reversibility and stability are considered as the key indicators for Zn metal anodes in aqueous Zn-ion batteries, yet they are severely hindered by uncontrolled Zn stripping/plating and side reactions. Herein, we fabricate a bulk phase ZnIn alloy anode containing trace indium by a typical smelting-rolling process. A uniformly dispersed bulk phase of the whole Zn anode is constructed rather than only a protective layer on the surface. The Zn deposition can be regarded as instantaneous nucleation due to the adsorption of the evenly dispersed indium, and formation of the exclusion zone for further nucleation can be prevented at the same time. Owing to the bulk phase structure of ZnIn alloy, the indium not only plays a crucial role in Zn deposition, but also improves the Zn stripping. Consequently, the as-designed ZnIn alloy anode can sustain stable Zn stripping/plating for over 2500 h at 4.4 mA cm-2 with nearly 6 times smaller voltage hysteresis than that of pure Zn. Moreover, it enables a substantially stable ZnIn//NH4V4O10 battery with 96.44% capacity retention after 1000 cycles at 5 A g-1. This method of regulating the Zn nucleation by preparing a Zn-based alloy provides a potential solution to the critical problem of Zn dendrite growth and by-product generation fundamentally.