RESUMEN
The pre-sintered preform (PSP) is an advanced technology for repairing the Ni-based superalloy blade in a turbine. In general, boron is added to the Ni-based superalloys in small quantities (<0.1 wt.%) to increase boundary strength and cohesivity. Despite this, the effect of high B content (>1.0 wt.%) on the microstructure evolution and mechanical properties in Ni-based superalloys for the PSP application is rarely studied. The variety, composition and evolution of the precipitates during solution heat treatment in the alloy with high B content were determined by EBSD, EPMA and SEM. The results indicate that Cr, W and Mo-rich M5B3 type borides precipitate from the matrix and its area fraction reaches up to about 8%. The area fraction of boride decreases with the prolonging of solution time and the increase of temperature higher than 1120 °C. The borides nearly disappear after solution treatment at 1160 °C for 2 h. The redissolution of boride and eutectic results in the formation of B-rich area with low incipient melting (about 1189 °C). It can bond metallurgically with the blade under the melting point of the blade, which decreases the precipitation of harmful phases of the blade after PSP repairing. The microhardness within the grain in the PSP work-blank first decreases (lower than 1160 °C) and then increases (higher than 1185 °C) with the increase of solution heat treatment temperature due to the dissolving and precipitation of borides. The tensile strength of the combination of PSP work-blank and Mar-M247 matrix at room temperature after solution treatment is related to the area fraction of boride, incipient melting and the cohesion between PSP work-blank and Mar-M247 matrix.