Physical properties of artificial teeth after immersion in liquid disinfectant soaps.

PURPOSE: To evaluate the hardness, roughness and color stability of artificial teeth after immersion in liquid disinfectant soaps. METHODS: Artificial teeth (Vipi Dent Plus, ArtiPlus and Biolux) were divided into four groups (n=15), according to the type of immersion solution: distilled water/control group (DW); liquid disinfectant soap Dettol (SD); liquid disinfectant soap Protex (SP); and liquid disinfectant soap Lifebuoy (SL). The immersion cycles occurred every day, for 8 hours at room temperature in each disinfectant solution, following immersion in distilled water for 16 hours at 37°C. All solutions were changed daily. Properties were evaluated after 0, 7, 14, 21 and 28 days of immersion. The data were analyzed with a mixed three-way ANOVA followed by the Bonferroni post-hoc test (α= 0.05). RESULTS: Vipi teeth presented significant reduction (P< 0.05) in hardness and roughness prior to 7 days of immersion in all solutions, including control group. These values, in general, were maintained during the 28 days. Biolux teeth, in general, did not present significant changes in hardness prior to immersion in any of the time intervals. The roughness of these teeth increased after 21 and 28 days of immersion (P< 0.05) in all the solutions. ArtiPlus teeth maintained stable roughness and hardness during the assessment period, regardless of the type of soap used. Color alterations were considered clinically acceptable. The liquid soaps may be an alternative for the disinfection of partial or total removable dentures. CLINICAL SIGNIFICANCE: The liquid disinfectant soaps tested did not significantly alter the hardness, roughness and color stability of the artificial teeth tested and may be an alternative for the disinfection of partial or total removable dentures.

Antimicrobial efficacy and biocompatibility of extracts from Cryptocarya species.

This study evaluated the efficacy of Cryptocarya spp extracts on biofilm of Candida albicans and its biocompatibility. Mature biofilm of C. albicans was formed on denture base acrylic resin samples and the fungicidal effect of the extracts was evaluated by Alamar Blue® assay, counting colony-forming units (CFU/mL) and confocal laser scanning microscopy (CLSM). Cytotoxicity of extracts from Cryptocarya species was evaluated by AlamarBlue® assay, using normal oral keratinocytes (NOK) cells. In additional, Analysis of plant extracts by ultra-high-performance liquid chromatography-diode array detector-tandem mass spectrometry (UPLC-DAD-MS) was performed. The results showed significant reduction in the cellular metabolism and in the number of CFU/mL of C. albicans (p<0.05). The concentration of 0.045 g/mL completely inhibited the number of CFU/mL. Regarding cytotoxicity, all extracts decreased cell viability compared to the control group. CLSM analysis showed predominance of live cells, but with a great difference between the groups. Antimicrobial activity of extracts from Cryptocarya on C. albicans biofilm was confirmed. However, all extracts showed toxicity on NOK cells.

Properties of an acrylic resin after immersion in antiseptic soaps: Low-cost, easy-access procedure for the prevention of denture stomatitis.

Denture stomatitis triggered by Candida species requires better preventive measures. This study evaluated the physical and biological properties of a denture base acrylic resin after immersion in antiseptic soaps. Acrylic resin specimens were prepared and stored in distinct solutions for 0, 7, 14, 21, and 28 days. The solutions were as follows: DW: distilled water at 37°C (control group); DS: cycles of daily immersion in Dettol soap for 8 hours at room temperature, followed by immersion in distilled water for 16 hours at 37°C; PS: cycles of daily immersion in Protex soap, as described for the previous group; LS: cycles of daily immersion in Lifebuoy soap, as described for the DS group. The parameters evaluated at each time point were the following: biofilm formation capacity by Candida albicans and reduction of preformed fungal biofilms, cytotoxicity, surface roughness, hardness, and color change. For the fungal adhesion phase, the type of soap had a statistically significant effect (p = 0.0292), but after 24 hours, no differences were found between solutions or between storage times. Regarding the efficacy of biofilm reduction, there was a significant difference when the groups were compared to each other (p = 0.014). Dettol and Lifebuoy eliminated the preformed biofilm on the specimens. Moreover, all the soaps were classified as non-cytotoxic (on HaCaT cell line) because there was no difference in cell viability between the different groups, except after 21 days, when a decrease in cell viability occurred, regardless of the type of soap. Regarding the roughness, there was no statistically significant difference (p > 0.05) between the groups. Lifebuoy decreased resin hardness regardless of storage time (p = 0.003). After 21 and 28 days of storage, there was an increase in hardness value, regardless of the type of soap. The specimens' color, according to the National Bureau of Standards values, ranged from 0.27 to 0.58 (i.e., imperceptible or mild color changes). In general, the disinfectant soaps were not able to prevent biofilm formation, but all the soaps were effective in reducing the preformed biofilm. In addition, all soaps were non-cytotoxic and did not change surface roughness, hardness (except Lifebuoy), and color (except Lifebuoy). Therefore, immersion in two antiseptic soaps (Protex and Dettol) may be a cheap and easy procedure for preventing denture stomatitis.