Alkali Silicates Codoped with NIR-Emitting RE (Nd3+ and Yb3+) Ions for Thermometry Applications.

In the present study, the synthesis of BaSrSiO4 co-doped Yb3+ and Nd3+ nanophosphors (NPs) was successfully achieved through the conventional sol-gel method, as confirmed by X-ray diffraction and SEM analysis, verifying the formation of pure NPs. The FTIR and Raman spectra analysis confirm the formation of silicates, as different modes and vibrations of Si-O and Si-O-Si were seen at 800-1000 cm-1. The energy transfer (ET) mechanism between Nd3+ and Yb3+ ions was seen as the emission spectra showed a rise in intensity of one over another. PLE emission spectra showed transitions at 2F7/2-2F5/2 for Yb3+ and from 4F3/2 to (4I9/2, 4I11/2, and 4I13/2) for Nd3+ when excited at 785 nm. All the samples record low activation energy, which shows that the rate of reaction will be higher in all the samples, and it will be highest for 1 mol% Nd3+ and 1 mol% Yb3+. An increasing value of τ was seen with increasing Yb3+ concentration, which confirms the increase in the population of trap centers. The positron annihilation lifetime (PAL) curve showed that 1 mol% Yb3+ and 2 mol Nd3+ have single vacancies or shallower positron traps, whereas 3 mol% Yb3+ and 2 mol% Nd3+ have larger defects like surface oxygen vacancy clusters. The other two samples have balance vacancies, which makes them best for thermometry applications. The fluorescence intensity ratio (FIR) was calculated to get sensitivity for thermometry application. 2.13% K-1 sensitivity achieved at 303-333 K temperature.

Study of Thermoluminescence and Optically Stimulated Luminescence Properties of Synthesised CaB2O4 Nanoparticles Doped with Copper.

CaB2O4 nanorods doped with different concentrations of Cu were prepared by using co-precipitation method. The recorded Thermoluminescence (TL) and Optically stimulated luminescence (OSL) of CaB2O4:Cu samples for different concentrations of Cu irradiated with 6 Gy of X-Ray shows that 0.05 at.wt% of Cu concentrations have higher sensitivity. The TL and OSL kinetic parameters of glow curves were evaluated using "tgcd" and conventional fitting methods. The TL glow curve of the CaB2O4:Cu have three individual glow peaks with maximum peak temperatures at 404.50, 453.04 and 484.02 K respectively. The OSL glow curves of the CaB2O4:Cu nanoparticles follow non-first order kinetics which can be fitted with the sum of two first order decay curves.

Usability of sand samples in TL Radiation Dosimetry.

This study investigated natural sand thermoluminescence (TL) response as a possible option for retrospective high-dose gamma dosimetry. The natural sand under investigation was collected from six locations with selection criteria for sampling sites covering the highest probability of exposure to unexpected radiation on the Egyptian coast. Dose-response, glow curve, chemical composition, linearity, and fading rate for different sand samples were studied. Energy Dispersive X-ray Spectroscopy (EDX) analysis revealed differences in chemical composition among the various geological sites, leading to variations in TL glow curve intensity. Sand samples collected from Ras Sedr, Taba, Suez, and Enshas showed similar TL patterns, although with different TL intensities. Beach sands of Matrouh and North Coastal with a high calcite content did not show a clear linear response to the TL technique, in the dose range of 10 Gy up to 30 kGy. The results show that most sand samples are suitable as a radiation dosimeter at accidental levels of exposure. It is proposed here that for high-dose gamma dosimetry with doses ranging from 3 to 10 kGy, a single calibration factor might be enough for TL measurements using sand samples. However, proper calibration might allow dose assessment for doses even up to 30 kGy. Most of the investigated sand samples had nearly stable fading rates after seven days of storage. The Ras Sedr sands sample was the most reliable for retrospective dose reconstruction.

Investigations of thermoluminescence characteristics of SrAlBO4 :Eu3+ phosphors irradiated with gamma rays and carbon ion beam.

A series of SrAlBO4 :Eu phosphors doped with different concentrations of Eu (0.1, 0.3, 0.5, 0.7, 1.0 mol%) was synthesized using a solid-state diffusion method, and their thermoluminescence (TL) properties were analyzed for gamma and carbon ion irradiation. The phase purity, morphological properties, vibrational features, and thermal stability of the prepared sample were analyzed using X-ray diffraction (XRD) and scanning electron microscopy (SEM), Fourier transform infrared (FT-IR) spectroscopy, and thermogravimetric/differential thermal analyzer (TG/DTA) techniques, respectively. The TL properties of the proposed materials showed broad dosimetric bands, peaking at 202°C for 0.12 kGy gamma irradiation. The highest TL intensity was obtained for a 0.7 mol% concentration of Eu ions under gamma irradiation. Furthermore, the glow curve of the proposed materials showed a broad emission band, centred at 148°C under carbon ion beam irradiation and exhibited the highest emission intensity for a 0.1 mol% Eu concentration. In addition, the dosimetric trapping parameters of the prepared samples such as symmetry factor, order of kinetics, activation energy, and frequency factor, were analyzed using various methods such as Chen's peak shape method, initial growth method, and the Ilich method. The obtained results of the samples showed the potential for dosimetric application.

Synthesis and characterization of high-sensitivity Dy,Eu co-doped CaSO4 thermoluminescent phosphor using coprecipitation technique.

In this work, (99 - x)CaSO4 -Dy2 O3 -xEu2 O3 , (where x = 0, 0.05, 0.1, 0.2, 0.3, 0.4, 0.5) thermoluminescence phosphors were prepared using a coprecipitation method. The thermoluminescence (TL) dosimetry (TLD) characteristics such as TL sensitivity, dose-response, minimum detectable dose, thermal fading, and the effect of sunlight on the prepared phosphors were investigated. The obtained results indicated that the most sensitive phosphor was obtained at x = 0.05. Large thermal fading of 6% after 1 h and 26% after 24 h from irradiation followed by 71% after 1 month with no additional fading was observed within a time frame exceeding 2 months throughout the remaining duration of the investigation, which also spanned over 2 months. Despite the phosphor's high fading rate, the relative sensitivity of the prepared samples was ~90% compared with TLD-100. The marked effect of day sunlight was also determined. High dose-response within the low-dose range from 0.01 to 5 Gy was observed. The obtained results suggested that the synthesized phosphor is well suited for applications involving radiation biology and radiotherapy dosimetry.

Studies of thermoluminescence properties of liquid crystalline N-phenyl substituted phenyl polysiloxane hydroxamic acids.

The investigation of thermoluminescence (TL) glow curves in liquid crystalline side chain N-phenyl-substituted phenyl polysiloxane hydroxamic acids (PHAs) has yielded significant insights. These polymers demonstrated TL behavior when exposed to ß-radiation between 0 and 220°C, indicating inherent luminescent properties when irradiated. Notably, a dose-dependent relationship was observed in reported derivatized polymers; this study elucidates the diverse TL characteristics exhibited by various liquid crystalline side chain N-phenyl-substituted phenyl PHAs when exposed to ß-radiation. Understanding these dose-dependent and dose-independent behaviors enhances the knowledge of their luminescent properties and potential applications in radiation detection.

Investigation of zinc polycarboxylate cement used in dental treatments in terms of retrospective dosimeter.

Zinc polycarboxylate cement is one of the few dental materials that demonstrate true adhesion to tooth structure. It is suitable for use in living organisms without causing harm. Its strong adhesion to teeth and low level of irritancy are two important parameters for the dental applications. In this study, the dosimetry properties of zinc polycarboxylate cement using thermoluminescence (TL) method were investigated and determined the effectiveness of its use as a good dosimeter. According to the results of this study, the sample shows a good TL properties with three main peaks found around 140°C, 220°C and 330°C. It has a wide linear dose response between 72 Gy and 2.3 kGy and good reusability of the TL peak found at 330°C. Unfortunately, the TL peak intensity values are rapidly faded within a short waiting time interval. Zinc polycarboxylate cement, which is frequently used in dental crowns, can be used as a retrospective dosimeter for measuring the amount of radiation in space studies and nuclear accidents due to its wide linear dose-response curve in the high dose region.

Structural and thermoluminescence properties of lithium borate glass matrices under UV and beta radiation.

In the present work, glass samples in the (100 - x)B2O3-xLi2O binary system, with x varying from 30 to 50 mol%, were prepared using the conventional melting and moulding method, with the main objective of evaluating the thermoluminescence response when exposing these materials to ultraviolet (UV) radiation. Complementary analysis based on density, optical absorption on the UV-visible region (UV-vis absorbance), Fourier transform infrared spectroscopy on the medium region, X-ray diffraction, and differential thermal analysis measurements were performed. Thermoluminescence measurements of vitreous samples showed glow curves with at least one peak with a maximum temperature of ~170°C after exposure to UV radiation in the temperature range 50-250°C. Samples were also exposed to beta radiation in the temperature range 25-275°C, also showing single peaks with a maximum temperature of ~150°C.

Photoluminescence and thermoluminescence dosimetry properties of Ag/Y co-doped ZnO nanophosphor for radiation measurements.

This work explores the thermoluminescence (TL) and photoluminescence (PL) properties of Ag/Y co-doped zinc oxide (ZnO) nanophosphor. The proposed dosimeter was prepared by the coprecipitation method and sintered at temperatures from 400°C to 1000°C in an air atmosphere. Raman spectroscopy was studied to investigate the structural features of this composition. The new proposed dosimeter revealed two peaks at 150°C and 175°C with a small shoulder at high temperature (225°C). The PL spectrum showed strong green emissions between 500 to 550 nm. The Raman spectrum showed many bands related to the interaction between ZnO, silver (Ag), and yttrium oxide (Y2 O3 ). The rising sintering temperature enhanced the TL glow curve intensity. The Ag/Y co-doped ZnO nanophosphor showed an excellent linearity index within a dose from 1 to 4 Gy. The minimum detectable dose (MDD) of the Ag/Y co-doped ZnO nanopowder (pellets) equaled 0.518 mGy. The main TL properties were achieved in this work as follows: thermal fading (37% after 45 days at 1 and 4 Gy), optical fading (53% after 1 h and 68% after 6 h by exposure to sunlight), effective atomic number (27.6), and energy response (flat behavior from 0.1 to 1.3 MeV). Finally, the proposed material shows promising results nominated to be used for radiation measurements.

Effect of IRSL-BLSL-TSL reading modes combination on thermoluminescence (TL) response of BeO dosimeter.

The ultimate goal of this work is the study of the effect of luminescence stimulations and signals reading modes combinations on the thermoluminescence intensity and glow curve behaviour for the same X-ray irradiation dose. Three interesting stimulating and reading modes are considered, namely, infrared stimulated luminescence (IRSL), blue light-emitting diode stimulated luminescence (BLSL) and thermally stimulated luminescence (TSL). The studied stimulation and reading modes combination protocols are (Protocol 1) IRSL-TSL, (Protocol 2) IRSL-BLSL-TSL and (Protocol 3) BLSL-IRSL-TSL. Experiments are performed on beryllium oxide (BeO) dosimeter. Results demonstrate well that the combination of reading modes have direct impact on the TL signal in terms of intensity and glow curve shape. It was also found that when reading modes are correctly combined, particularly when IRSL is applied first, then BLSL and TL, it is possible to collect two or more exploitable signals of different stimulation types for the same irradiation that can be used for different purposes and final applications.

Comparison of linear energy transfer measurement for therapeutic carbon beam using CR-39 and TLD.

The measurement of linear energy transfer (LET) is crucial for the evaluation of the radiation effect in heavy ion therapy. As two detectors which are convenient to implant into the phantom, the performance of CR-39 and thermoluminescence detector (TLD) for LET measurement was compared by experiment and simulation in this study. The results confirmed the applicability of both detectors for LET measurements, but also revealed that the CR-39 detector would lead to potential overestimation of dose-averaged LET compared with the simulation by PHITS, while the TLD would have a large uncertainty measuring ions with LET larger than 20 keVµm-1. The results of this study were expected to improve the detection method of LET for therapeutic carbon beam and would finally be benefit to the quality assurance of heavy ion radiotherapy.

Thermoluminescence dosimeter (TLD) studies of Ca10 K(PO4 )7 :Dy phosphor for applications in radiation dosimetry.

This study reports the thermoluminescence (TL) aspects of Ca10 K(PO4 )7 :Dy phosphor synthesized using a wet chemical method for the first time. The X-ray diffraction (XRD) results confirm the formation of the desired crystalline phase. Surface morphological studies reveal the formation of polyhedrons and agglomerations having an average diameter of 200 nm, while energy dispersive X-ray spectroscopy (EDS) data show the presence and composition of the elements in appropriate amounts. The effect of Dy doping concentration has been studied on the TL properties with exposure to gamma radiations from the Co-60 source. The best TL response has been observed for 5 mol% Dy doping concentration. The glow curve is simple and consists of a single peak at 130°C. The effect of the heating rate has been studied on the TL glow curve, and the heating rate of 5°C/s shows the best TL response. The various TL properties such as annealing conditions, dose-response, TL linearity, fading, and reusability of the prepared phosphor have been studied to check its suitability as a good TL dosimeter (TLD). TL characterization of the phosphor reports that the TL response is linear from 5- to 2000 Gy. The results show that this phosphor can be a good TLD for the dosimetry of gamma radiations from Co-60.

Photoluminescence and thermoluminescence properties of pure and rare-earth-doped ZrO2 prepared by Pechini-type sol-gel.

In this article, photoluminescence (PL) and thermoluminescence (TL) properties of ZrO2 , ZrO2 :Dy3+ , ZrO2 :Dy3+ -Gd3+ , ZrO2 :Dy3+ -Yb3+ , ZrO2 :Dy3+ -Er3+ , and ZrO2 :Dy3+ -Sm3+ phosphors synthesized by the Pechini method were investigated. The crystal structure, thermal properties, morphology, PL and TL properties were investigated using X-ray powder diffraction (XRD), differential thermal analysis/thermogravimetric analysis (DTA/TGA), scanning electron microscopy (SEM), PL and TL, respectively. The room temperature emission bands corresponding to 4 F9/2  â†’ 6 HJ (J = 9/2, 11/2, 13/2 and 15/2) transitions of Dy3+ ions were measured. The phosphors were analysed using Tm -TSTOP , variable dose, and computerized glow curve fitting methods. Reusability, dose-response, and fading characteristics were investigated. The phosphors have a natural TL emission that vanished by heating treatment. Moreover, new peaks with similar properties to the natural emissions were observed after high-dose irradiation and long-term fading experiments. The glow curves of the phosphors have 13 individual peaks and many low- and high-temperature satellite peaks. The origin of the peaks is ZrO2 host material and doping with rare-earth ions (Gd3+ , Dy3+ , Yb3+ , Er3+ and Sm3+ ) does not lead to a new glow peak. The dopants cause drastic changes in individual peak intensities of ZrO2 .The initial fading rates of all the phosphors are relatively fast, but they slow down as time goes on.

Europium doped Sr2 YNbO6 double perovskite phosphor for photoluminescence and thermoluminescence properties.

A luminescent double perovskite phosphor Sr2 YNbO6 doped with Eu3+ crystallized to the monoclinic phase and was synthesized successfully via a conventional high-temperature combustion method. The formation of the crystal structure, phase purity, and surface morphology were studied using X-ray diffraction patterns and scanning electron microscopy. The characteristic vibrations between the atoms of the functional groups present in phosphor were studied using Fourier transform infrared spectra analysis. The luminescence properties of the prepared phosphors were investigated in terms of photoluminescence (PL) and thermoluminescence (TL). PL excitation spectra exhibited charge transfer bands and the characteristic 4f6 transitions of Eu3+ . A prominent PL emission was obtained for the phosphor doped with 4 mol% Eu3+ under the 396 nm excitation wavelength. PL emission quenching was observed for the higher doping concentrations due to a multipole-multipole interaction. A highly intense PL emission arose due to the hypersensitive 5 D0 -7 F2 electric dipole transition of Eu3+ that dominated the emission spectra. The thermal stability of the phosphor was examined through temperature-dependent PL. The TL properties of the Sr2 YNbO6 double perovskites irradiated with a 90 Sr beta source at different doses were measured. The double perovskite phosphors under study showed a linear dose-response with increasing beta dose, ranging from 1 Gy to 10 Gy. Trapping parameters of the TL glow curves were determined using Chen's peak shape method and computerized glow curve deconvolution (CGCD). CGCD fitting of the TL glow curves revealed that it was consisted of three major peaks and followed second-order kinetics. The estimated activation energies were determined using different methods and were comparable and significant.

Thermoluminescence in pumice stone collected from the Mediterranean coast.

Pumice is a low-density, light-coloured volcanic rock (igneous rock) formed when the magma from a volcanic eruption is suddenly cooled. It has a porous structure and can be different colours and have different densities. Pumice stone, unlike other rock, does not sink in water because it has a low density. In the present study, the thermoluminescent (TL) dosimetric characteristics, such as the dose-response, TL signal fading as a function of storage time, heating rate, and reusability of pumice collected on the Mediterranean coast were investigated. From this study, it was concluded that the pumice stone showed TL properties with a TL glow curve including an obviously wide peak at ∼200°C. A wide linear dose-response region up to 144 Gy, low fading of the TL signal when it was kept in a dark room for a long time, and poor reusability properties were observed for dosimetry use.

Electronic structure and defect-induced luminescence study of phase-stabilized t-ZrO2 nanocrystals.

Luminescent tetragonal-ZrO2 (t-ZrO2 ) nanocrystals were synthesized using an optimized combustion method without post-synthesis annealing and characterized using X-ray diffraction, electron microscopy, Raman spectroscopy, X-ray photoelectron spectroscopy, UV-Vis. spectroscopy, photoluminescence spectroscopy, thermoluminescence (TL), and vibrating sample magnetometry. The as-synthesized t-ZrO2 nanocrystals have a bandgap of 4.65 eV and exhibit defect-assisted blue emission (Commission Internationale de I'Elcairage coordinates 0.2294, 0.1984) when excited at 270 nm. The defect states were qualitatively and quantitatively analyzed using TL after irradiating nanocrystals with γ- and UV radiations at various doses. The TL glow curves show intense emission in the high-temperature region from 523 to 673 K for both UV- and γ-irradiated samples; however, another less-intense TL peak was also observed in the low-temperature region from 333 to 453 K with γ irradiation at higher doses, indicating the formation of shallow trapping states. The activation energies, frequency factor, and order of kinetics were estimated using the computerized glow curve deconvolution method for the shallow and deep traps for γ- and UV-irradiated samples. The present study shows that phase-stabilized t-ZrO2 nanocrystals are potential candidates for luminescence-based applications.

Luminescence investigation of CaY2 Al4 SiO12 :Dy3+ phosphor synthesized by sol-gel method.

Dy3+ -doped CaY2 Al4 SiO12 phosphors were prepared using the sol-gel method. X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and energy dispersive spectroscopy analyses (EDS) were used to analyse the crystal structure, morphology, and elemental composition of the prepared samples. The luminescence behaviour of the sample was investigated using photoluminescence (PL) and thermoluminescence (TL) techniques. The prepared CaY2 Al4 SiO12 :xDy3+ phosphor showed a characteristic blue and yellow emission at ~480 and 583 nm, respectively, with an excitation wavelength of 350 nm. The most intense PL emission was found for a 4 mol% doping concentration of Dy3+ ions. The CIE diagram of the phosphor showed bluish-white colour emission. For TL studies, the prepared phosphors were irradiated with a 60 Co γ (gamma) source and the TL glow curve of the CaY2 Al4 SiO12 :0.04Dy3+ phosphor showed three overlapped peaks. For the Gaussian peaks, Chen's peak shape method was applied to determine the kinetic parameters of the samples.

Luminescence properties of Ce-doped ZrO2 phosphors synthesized by combustion method.

Zr1-x Cex O2 with x = 0.005, 0.01, 0.02, and 0.03 samples were synthesized using a combustion technique. The X-ray diffraction results revealed that Ce-doped ZrO2 nanoparticles were in a monoclinic structure up to 1 mol% Ce concentration. The increase in the Ce concentration caused more distortion in the monoclinic structure of zirconia. The samples showed a mixed phase (monoclinic + tetragonal) beyond 1 mol% Ce content. The crystallite size (D) and strain (ε) were calculated from the Williamson-Hall equation. The D decreased from 25 ± 1 to 20 ± 1 nm and ε increased from 0.03 to 0.28% with an increase in Ce concentration. Photoluminescence (PL) spectra of Zr1-x Cex O2 showed emission in the blue region under an excitation wavelength of 290 nm. Zr0.995 Ce0.005 O2 showed the highest PL intensity with an average lifetime of 0.93 µs, and the PL intensity decreased with the increase in the Ce concentration. Thermoluminescence (TL) glow curves of Zr1-x Cex O2 were measured after gamma irradiation (500 Gy) with a heating rate of 5 K s-1 . The TL curve of Zr0.995 Ce0.005 O2 showed two prominent peaks at 412 K (peak 1) and 600 K (peak 2). The first TL glow peak was shifted towards a higher temperature at 440 K above 1 mol% Ce concentration. Repetitive TL measurements on the same aliquot exhibited excellent repeatability. Kinetic parameters associated with the TL peaks were calculated using the curve fitting method. Peak 1 followed non-first-order kinetics. The value of the activation energy of the 440 K peak was found to be 0.95 ± 0.01 eV for Zr0.99 Ce0.01 O2 . These findings showed that Zr1-x Cex O2 might be used in lighting and radiation dosimeter applications.

Thermoluminescence studies of zinc borate (ZnB2 O4 ) phosphor doped with rare earths for dosimetric aspects.

A series of ZnB2 O4 phosphors doped with different concentrations of Eu and Dy (0.05 0.1, 0.2, 0.5, 1.0 mol%) and co-doped with Ce (1, 2, 5, 7, 10 mol%) respectively was prepared via the solid-state reaction technique and the thermoluminescence (TL) behaviour of gamma ray-irradiated samples was studied. The synthesized samples were irradiated with γ-rays for the dose range 0.03-1.20 kGy. The TL intensity variations with dose, dopant concentration, and the effect of co-doping were studied. The TL response curves for ZnB2 O4 :Eu3+ and ZnB2 O4 :Dy3+ , ZnB2 O4 :Eu3 ,Ce3+ and ZnB2 O4 :Dy3+ ,Ce3+ phosphor were observed. It was revealed that ZnB2 O4 :Eu3+ showed a linear TL behaviour for the dose 0.03-1.20 kGy and ZnB2 O4 :Dy3+ showed linearity for the gamma dose range 0.03-0.10 kGy. Furthermore, fading for all the samples was observed to be less than 10% for a storage period of 30 days. In addition to this, the trapping parameters, especially activation energies were evaluated using the Ilich method and the initial rise method. The activation energy values obtained from both methods were in complete agreement with each other.

Thermoluminescence properties of the rock naturally annealed for thousands of years by flames from the earth's inner layers.

The gas leak in Chimaera near Çirali, Antalya, has been active for thousands of years. It is also known to be the source of the first Olympic flame in the Hellenistic period. The sample taken from the Chimaere seepage annealed for thousands of years was determined to be calcite-magnesian (Ca, Mg)O3 . In this study, thermoluminescence (TL) properties of calcite-magnesian annealed for thousands of years in the fire caused by methane gas were investigated for particle size, dose-response, heating rate, and fading experiments. It exhibits a clear TL glow curve with two distinct peaks positioned at 160 and 330°C, and its shape is not affected by variation in applied dose and reproduciility of experiment. There is a wide linear relationship between TL output and applied dose up to 614 Gy. Although the positions of the TL peaks are stable with the cycle of measurement, a poor reusability was observed in terms of the area under the TL glow curve and peak intensity.