RESUMEN
OBJECTIVE: To evaluate the ability of the water glass treatment to penetrate zirconia and improve the bond strength of resin cement. MATERIAL AND METHODS: Water glass was applied to zirconia specimens, which were then sintered. The specimens were divided into water-glass-treated and untreated zirconia (control) groups. The surface properties of the water-glass-treated specimens were evaluated using surface roughness and electron probe micro-analyser (EPMA) analysis. A resin cement was used to evaluate the tensile bond strength, with2 and without a silane-containing primer. After 24 h in water storage at 37 °C and thermal cycling, the bond strengths were statistically evaluated with t-test, and the fracture surfaces were observed using SEM. RESULTS: The water glass treatment slightly increased the surface roughness of the zirconia specimens, and the EPMA analysis detected the water glass penetration to be 50 µm below the zirconia surface. The application of primer improved the tensile bond strength in all groups. After 24 h, the water-glass-treated zirconia exhibited a tensile strength of 24.8 ± 5.5 MPa, which was significantly higher than that of the control zirconia (17.6 ± 3.5 MPa) (p < 0.05). After thermal cycling, the water-glass-treated zirconia showed significantly higher tensile strength than the control zirconia. The fracture surface morphology was mainly an adhesive pattern, whereas resin cement residue was occasionally detected on the water-glass-treated zirconia surfaces. CONCLUSION: The water glass treatment resulted in the formation of a stable silica phase on the zirconia surface. This process enabled silane coupling to the zirconia and improved the adhesion of the resin cement.
Asunto(s)
Recubrimiento Dental Adhesivo , Vidrio , Ensayo de Materiales , Cementos de Resina , Silanos , Propiedades de Superficie , Resistencia a la Tracción , Agua , Circonio , Circonio/química , Cementos de Resina/química , Silanos/química , Agua/química , Recubrimiento Dental Adhesivo/métodos , Vidrio/química , Microscopía Electrónica de Rastreo , Análisis del Estrés DentalRESUMEN
OBJECTIVE: This study aimed to evaluate the effect of ultrasonic activation of etch-and-rinse and self-etch adhesive systems on the bond strength of resin cement to irradiated root dentin. MATERIALS AND METHODS: Eighty human maxillary anterior teeth were distributed into 8 groups (n = 10), according to the type of adhesive system used (etch-and-rinse and self-etch), the ultrasonic activation of the adhesive systems, and the dentin condition (irradiated or non-irradiated - 70 Gy). Endodontic treatment was performed followed by fiberglass post-space preparation. After fiberglass posts' luting, the roots were transversely sectioned on dentin discs and submitted to the push-out bond strength test (0.5 mm/min). The fractured specimens were analyzed under a stereomicroscope and Scanning Electron Microscope (SEM) for failure mode classification. One of the dentin discs was analyzed under SEM to evaluate the characteristics of the adhesive interface. RESULTS: Irradiated specimens had lower bond strength than non-irradiated specimens (P < 0.0001). Ultrasonic activation of both adhesive systems increased the bond strength of the resin cement to irradiated dentin (P < 0.0001). Radiotherapy significantly affected the failure mode in the middle (P = 0.024) and apical thirds (P = 0.032) (adhesive failure). CONCLUSION: Non-irradiated specimens had a more homogeneous adhesive interface. When ultrasonically activated, both adhesive systems showed a greater number of resinous tags, regardless of the dentin condition. CLINICAL RELEVANCE: Ultrasonic activation of adhesive systems is a feasible strategy to enhance fiberglass posts retention in oncological patients.
Asunto(s)
Recubrimiento Dental Adhesivo , Dentina , Ensayo de Materiales , Microscopía Electrónica de Rastreo , Técnica de Perno Muñón , Cementos de Resina , Humanos , Cementos de Resina/química , Recubrimiento Dental Adhesivo/métodos , Dentina/efectos de la radiación , Técnicas In Vitro , Recubrimientos Dentinarios/química , Análisis del Estrés Dental , Propiedades de Superficie , Raíz del Diente/efectos de la radiación , Ultrasonido , Grabado Ácido Dental , Incisivo , Vidrio/químicaRESUMEN
OBJECTIVES: The first aim of this study was to determine whether there is a difference in degree of conversion (DC) of touch-cure cements polymerized by self-curing with adhesive or dual-curing under reduced light. The second aim was to compare interfacial adaptation of zirconia restoration cemented using touch-cure cements self-cured or dual-cured by reduced light. METHODS: The DC of touch-cure resin cements with adhesive was measured continuously using Fourier transform infrared spectrometry. Experimental groups differed depending on touch-cure cement. Each group had three subgroups of polymerization method. For subgroup 1, the DC was measured by self-curing. For subgroups 2 and 3, the DCs were measured by dual-curing with reduced light penetrating 3 mm and 1 mm zirconia blocks, respectively. For interfacial adaptation evaluation, Class I cavity was prepared on an extracted third molar, and zirconia restoration was fabricated. The restoration was cemented using the same cement. Groups and subgroups for interfacial adaptation were the same as those of the DC measurement. After thermo-cycling, interfacial adaptation at the tooth-restoration interface was evaluated using swept-source optical coherence tomography imaging. RESULTS: The DC of touch-cure cement differed depending on the measurement time, resin cement, and polymerization method (p < 0.05). Interfacial adaptation was different depending on the resin cement and polymerization method (p < 0.05). CONCLUSION: For touch-cure cement, light-curing with higher irradiance presented a higher DC and superior interfacial adaptation than light-curing with lower irradiance or self-curing. CLINICAL RELEVANCE: Although some adhesives accelerate the self-curing of touch-cure cement, light-curing for touch-cure cement is necessary for zirconia cementation.
Asunto(s)
Ensayo de Materiales , Polimerizacion , Cementos de Resina , Circonio , Cementos de Resina/química , Circonio/química , Espectroscopía Infrarroja por Transformada de Fourier , Auto-Curación de Resinas Dentales , Luces de Curación Dental , Curación por Luz de Adhesivos Dentales , Propiedades de Superficie , Técnicas In Vitro , Humanos , Tercer Molar , Restauración Dental Permanente/métodosRESUMEN
Because the use of hydrofluoric acid (HF) poses health risks if handled improperly, many clinicians prefer to have the ceramic restorations pre-etched in dental laboratories. However, during the try-in procedure, the pre-etched glass-ceramic restorations may be contaminated with saliva resulting in reduced bond strength. This in-vitro study aimed to investigate the effect of different surface treatments on the bond strength of lithium disilicate (LD) glass-ceramic restorations (IPS e.max Press, Ivoclar Vivadent) to two resin cements. One-hundred eighty blocks (4X4X3mm) of LD glass-ceramic were divided into twelve groups (n = 15), of which six received Variolink Esthetic DC (VE) cement and six received RelyX Ultimate (RU) cement, following the surface treatments: G1) Control: Hydrofluoric Acid + Silane (HF + Sil); G2) Hydrofluoric Acid + Saliva + Silane (HF + S + Sil); G3) Hydrofluoric Acid + Saliva + Ivoclean + Silane (HF + S + IC + Sil); G4) Hydrofluoric Acid + Saliva + Phosphoric Acid + Silane (HF + S + P + Sil); G5) Hydrofluoric Acid + Saliva + Monobond Etch & Prime (HF + S + EP); G6) Monobond Etch & Prime (EP). Following treatment, a resin-cement cylinder (2.3 mm diameter) was built on the glass-ceramic surface, photocured (20 s), stored in distilled water (37 °C, 24 h) and submitted to the shear bond strength test. Bond strength data (MPa) were subjected to two-way ANOVA and Tukey (α = 0.01). Cement type and surface treatment had a significant effect on the bond strength (p < 0.001) (Table 4). Single-step Monobond Etch & Prime (EP) significantly improved the bond strength of resin-cements to glass-ceramic with and without saliva contamination.
Asunto(s)
Recubrimiento Dental Adhesivo , Cementos de Resina , Cementos de Resina/química , Ácido Fluorhídrico , Silanos , Propiedades de Superficie , Porcelana Dental , Cerámica , Cementos Dentales , Protocolos Clínicos , Ensayo de MaterialesRESUMEN
OBJECTIVES: To investigate the effect of cumulative doses of radiation on the pushout bond strength (BS) of a universal resin cement used in the self-etch (SE) and self-adhesive (SA) modes to the intraradicular dentin. MATERIALS AND METHODS: Forty-eight human teeth were distributed into three groups (n = 16) according to the radiation therapy dose (RT): NoRT (no-radiotherapy), 70RT (70 Gy), and 70 + 70RT (70 Gy + 70 Gy). The teeth were redistributed into two subgroups (n = 8), according to the adhesive mode: SE (NoRT-SE, 70RT-SE, and 70 + 70RT-SE) and SA (NoRT-SA, 70RT-SA, and 70 + 70RT-SA). Data were statistically compared after BS test (ANOVA, Tukey's post hoc test, and Fisher's exact test). RESULTS: In the SA mode, BS was significantly higher in nonirradiated teeth compared with 70RT and 70 + 70RT (p < 0.0001). There were no significant differences between SE and SA modes in nonirradiated teeth (p = 0.14). In the 70RT group, SE mode increased BS compared with SA mode (p < 0.0001). Most specimens had adhesive and mixed failures in SA and SE modes, respectively. CONCLUSIONS: The universal resin cement in the SE mode had greater BS to the irradiated dentin. When teeth were re-irradiated, the universal resin cement had similar performance in terms of BS, regardless of the adhesive approach. CLINICAL SIGNIFICANCE: There is no research establishing a correlation between radiotherapy and its impact on the BS of a universal resin cement used in SE and SA modes to intraradicular dentin.
Asunto(s)
Recubrimiento Dental Adhesivo , Cementos de Resina , Humanos , Cementos de Resina/química , Recubrimiento Dental Adhesivo/métodos , Dentina , Análisis del Estrés Dental , Ensayo de Materiales , Recubrimientos Dentinarios/química , Grabado Ácido DentalRESUMEN
OBJECTIVE: Demonstrate the ability of 0.5 mm thickness lithium disilicate laminates associated with resin cement to mask different substrate saturations. METHODS: 60 specimens (n = 5) were prepared with CAD/CAM lithium disilicate glass-ceramic IPS e.max CAD, 0.5 mm thick, in three degrees of translucency (HT, MT and LT); cemented by Variolink Esthetic LC Light+ (L) and Neutral (N) on composite resin substrates A1 and A4 shades. Color measurements were performed by a spectrophotometer (CM-3700d -Konica Minolta). The L*, a*, b* parameters of the tri-layer structure (laminate/ resin cement/ substrate) were used to calculate color difference ( ∆ E 00 ) by CIEDE2000 formula and Translucency Parameter ( TP 00 ). This study adopted ∆ E 00 = 0.8, as perceptibility threshold (PT), and ∆ E 00 = 1.8, as acceptability threshold (AT). Statistical analyses were performed by one-way ANOVA and Tukey tests (a = 0.05). RESULTS: Color difference between resin cement shades showed statistical differences (p < 0.0001) and ∆ E 00 > 1.8 for all groups. Color difference between substrates saturations showed a significant statistical difference (p < 0.0001) and ∆ E 00 values above AT for all groups. The TP 00 demonstrated significant statistical differences (p < 0.0001). The LTL combination, the opaquest set, showed the smallest ∆ E 00 values between substrate shades differences, however, above AT. CONCLUSION: The translucency of the lithium disilicate, the substrate saturation and the resin cement opacity influenced final color of restoration. The ceramic translucency impact on final color was reduced by opaque resin cement. Furthermore, the LT lithium disilicate and the Light+ resin cement reduced the translucency of the restoration, contributing to mask saturated substrate. CLINICAL RELEVANCE: This study shows the influence of conservative lithium disilicate laminates with different degrees of translucency associated with resin cement on final color of saturated substrate restorations. A minimally invasive esthetic protocol for masking substrates is demonstrated by associating low translucency ceramic laminates and opaque resin cement.
Asunto(s)
Estética Dental , Cementos de Resina , Cementos de Resina/química , Porcelana Dental/química , Cerámica/química , Ensayo de Materiales , Color , Propiedades de SuperficieRESUMEN
OBJECTIVES: The objective of this study was to evaluate the effect of mouthwashes on the optical properties of resin cement. MATERIALS AND METHODS: One hundred and 60 resin cement discs (6x2mm) were produced from 4 different brands of resin cement (Panavia V5, Estecem II, RelyX Veneer, NX3) with the help of a Teflon mould. The discs were divided into 4 subgroups, 1 of which served as the control group, to be immersed in mouthwashes after measuring the initial L, a, and b values on white and black backgrounds. Colour measurements were repeated after the 1st and 7th days. The collected data were used to calculate the ∆E00 value to measure colour stability, the translucency parameter (TP00), and the contrast ratio parameter (CR) to compare translucency change. Data were statistically analysed using mixed-design analysis of ANOVA and the Bonferroni-Dunn test. Repeated measures ANOVA was used for dependent results (α = 0.05). RESULTS: On the ∆E00, TP00, and CR parameters; the joint effect of resin groups, mouthwash groups, and measurement times were found to be statistically significant. The ∆E00 (colour difference) parameter; the joint effect of resin groups, mouthwash groups, and measurement times was found to be statistically significant. The TP00; the joint effect of resin groups, mouthwash groups, and measurement times were found to be statistically significant. The CR parameter; the joint effect of resin groups, mouthwash groups, and measurement times was found to be statistically significant. In the Estecem II (Tokuyama) group, the means of Listerine Cool Mint (Johnson & Johnson) was above acceptable limits in both time periods. In the Panavia V5 (Kuraray Noritake) group, the color change was above acceptable limits in all time periods and in all mouthwash groups. Among the resin materials used, Estecem II (Tokuyama) shows the most color change. Listerine Cool Mint (Johnson & Johnson) caused more color change than other mouthwashes at all times. CONCLUSIONS: Within the limitations of this study; the colour stability and translucency value of resin cement depend on both the resin cement content and the mouthwash. Long-term use of mouthwash may adversely affect the optical properties of the resin cement. CLINICAL RELEVANCE: Clinicians should take into account the fact that mouthwash use and the composition of the resin cement employed will have an impact on the colour of laminate veneers.
Asunto(s)
Cerámica , Porcelana Dental , Humanos , Cementos de Resina , Antisépticos Bucales , Color , Propiedades de Superficie , Ensayo de MaterialesRESUMEN
BACKGROUND: The aim of this study is to evaluate the stress distributions of a primary molar tooth restored with a stainless steel crown (SSC) using resin and glass ionomer luting cements by Finite Element Analysis (FEA). METHODS: Original DICOM data of a primary molar was used to create a 3D model. One model was prepared as a tooth model with SSC. A 30 µm cement layer was used in model. Two different luting cements were tested in the study: self-cure adhesive resin cement, and glass ionomer cement. Vertical and oblique loads of 330 N were applied to simulate maximum bite force and lateral forces in the occlusal contact areas of the models. Maximum von Mises stress values in the models were evaluated as MPa. RESULTS: The maximum von Mises stress value was observed in the force application and general occlusal contact areas for all models. The maximum von Mises stress values were higher in the tooth model with SSC using self-cure adhesive resin cement (478.09 MPa and 214.62 MPa) than in the tooth model with SSC using glass ionomer cement (220.06 MPa and 198.72 MPa) in both vertical and oblique loading, respectively. CONCLUSIONS: Depending on the magnitude of the bite force on the SSC, fracture of the luting cement materials could occur if the stress exceeds the endurance limit of the luting cement. Cementation with glass ionomer cement may help to reduce stress levels in SSC restorations of primary molars in children.
Asunto(s)
Cementos de Resina , Acero Inoxidable , Niño , Humanos , Cementos de Resina/uso terapéutico , Cementos Dentales/uso terapéutico , Cementos de Ionómero Vítreo/uso terapéutico , Coronas , Diente Molar , Ensayo de MaterialesRESUMEN
BACKGROUND: N-acetylcysteine (NAC) reduces the cytotoxicity and genotoxicity induced by monomers leached from dental composite resins. Herein, we investigated the effects of methacrylate-based resin cement used in dental implant restoration on apoptosis and genotoxicity, as well as the antiapoptotic and antigenotoxic capabilities of its component, NAC. METHODS: The antioxidant NAC (0.1 or 1 wt.%) was experimentally incorporated into the methacrylate-based dental resin cement Premier®. The Premier® + NAC (0.1 or 1 wt.%) mixture was subsequently immersed into Dulbecco's modified Eagle's medium for 72 h, and used to treat human gingival fibroblasts (HGFs). The viability of HGFs was determined using the XTT assay. The formation of deoxyribonucleic acid (DNA) double-strand breaks (DNA-DSBs) was determined using a γ-H2AX assay. Reactive oxygen species (ROS), apoptosis, necrosis, and cell cycles were detected and analyzed using flow cytometry. RESULTS: The eluate of Premier® significantly inhibited HGF proliferation in vitro by promoting a G1-phase cell cycle arrest, resulting in cell apoptosis. Significant ROS production and DNA-DSB induction were also found in HGFs exposed to the eluate. Incorporating NAC (1 wt.%) into Premier® was found to reduce cell cytotoxicity, the percentage of G1-phase cells, cell apoptosis, ROS production, and DNA-DSB induction. CONCLUSION: Incorporating NAC (1 wt.%) into methacrylate-based resin cement Premier® decreases the cell cytotoxicity, ROS production, and DNA-DSBs associated with resin use, and further offers protective effects against the early stages of cell apoptosis and G1-phase cell cycle arrest in HGFs. Overall, our in vitro results indicate that the addition of NAC into methacrylate-based resin cements may have clinically beneficial effects on the cytotoxicity and genotoxicity of these materials.
Asunto(s)
Acetilcisteína , Metacrilatos , Humanos , Acetilcisteína/farmacología , Metacrilatos/toxicidad , Cementos de Resina , Especies Reactivas de Oxígeno , Apoptosis , ADN/farmacología , Fibroblastos , Supervivencia CelularRESUMEN
PURPOSE: This systematic review and meta-analysis aimed to evaluate the difference in the color stability of light-cured and dual-cured resin cements. MATERIALS AND METHODS: Two separate reviewers used the PubMed, Scopus, Web of Science, Embase, and Scielo databases to execute the systematic review. For the analysis, studies that evaluated the color stability of dual-cured and light-cured resin cements over time were used. The random effects model was used in the meta-analysis. Analyses of subgroups were carried out based on the aging technique. The methodological quality of each in vitro study was evaluated in accordance with the parameters of a prior systematic review. RESULTS: From all databases, a total of 2223 articles were retrieved. Following the screening of titles and abstracts, 44 studies were selected for full text review, and a total of 27 articles were used for the qualitative analysis. Finally, 23 articles remained for the qualitative analysis. The majority of studies were labeled as having a medium risk of bias. The global analysis showed that the dual-cure resin cements had considerably greater differences in the color change (p = 0.006). A high heterogeneity index (86%) was found in the analysis. CONCLUSIONS: The best available in vitro evidence suggests that dual-polymerizing cement has higher color variation than light-polymerized materials. To reduce the likelihood of color change after the luting of thin ceramic restorations, clinicians should employ light-polymerizable resin cements.
Asunto(s)
Cerámica , Cementos de Resina , Color , Ensayo de Materiales , Proyectos de InvestigaciónRESUMEN
PURPOSE: To evaluate the effect of different surface treatments and adhesive cementation on the miniflexural strength (MFS) of monolithic zirconia. MATERIALS AND METHODS: Two-hundred and forty (240) sintered bars of translucent zirconia (ZT) and ultra-translucent zirconia (ZUT) were obtained (8 mm ×2 mm ×1 mm). The bars were divided into 16 groups (n = 15) according to the factors "Zirconia" (ZT and ZUT), "Cementation" (Cem) and "surface treatment" (Ctrl:Control, Al:Aluminum oxide/Al2O3 50 µm, Si:Silica/SiO2 coated alumina particles oxide 30 µm, Gl:Glazing+hydrofluoric acid). Half of the bars received an adhesive layer application, followed by application of resin cement and light curing. The surface roughness was measured in non-cemented groups. All the bars were subjected to the MFS test (1.0 mm/min; 100 kgf). Scanning electron microscopy was used for qualitative analyses. MFS data (MPa) and roughness (µm) were statistically evaluated by three-way and two-way ANOVA respectively and Tukey's test (5%). RESULTS: The surface treatment and the interaction were significant for roughness. Glazing promoted less roughness compared to silicatization. Regarding MFS, only the zirconia and surface treatment factors were significant. For ZT, the sandblasted groups had an increase in MFS and glazing reduced it. There was no difference between the groups without cementation for the ZUT; however, ZUT.Si/Cem, and ZUT.Al/Cem obtained superior MFS among the cemented groups. CONCLUSIONS: Sandblasting increases the flexural strength for ZT, while glaze application tends to reduce it. Applying resin cement increases the flexural strength of ZUT when associated with sandblasting. Sandblasting protocols promote greater surface roughness.
RESUMEN
INTRODUCTION: This study evaluates the impact of decontamination methods on Microtensile bond strength (µTBS) between resin cement and resin blocks. METHODS: Twenty CAD/CAM resin blocks from two manufacturers were wet-polished, sandblasted, and ultrasonically cleaned. After blood and saliva contamination, blocks were divided into subgroups: control, water rinsing, acid etching, alkaline cleaning paste, or 10-MDP containing cleaner. Resin-based cement was then applied. After 24 hours, the blocks were sectioned to obtain bars for testing. Half of the specimens were tested immediately for µTBS, and the other half underwent artificial aging. The surfaces of the blocks were inspected with a scanning electron microscope (SEM). Three-way ANOVA was performed for µTBS values (α=0.05). RESULTS: In one of the substrates, the positive control subgroup obtained the highest value (56,01 MPa, SD:6,96) followed by 10-MDP cleaner and universal cleaning paste, when immediately tested, with significant differences respect to the water rinsing (p⟨0.041) and acid etching (p⟨0.048) groups. After thermocycling, higher values were found in the 10-MDP cleaner (47,57 MPa, SD:8,15), but differences were not significant. In the other substrate group, the 10-MDP cleaner subgroup showed highest bond strengths (64,46 MPa SD: 10,92) at the initial test. After thermocycling, 10-MDP cleaner (58,66 MPa, SD: 9,93) gave the highest µTBS value. Significant differences between water rinsing group and the rest of subgroups (p⟨0.001), and between 10-MDP cleaner and the positive control group (p⟨0.006) were observed. CONCLUSION: Cleaning after contamination improves bonding. 10-MDP containing cleaner can help to restore initial µTBS value and maintain it in the long-term.
Asunto(s)
Recubrimiento Dental Adhesivo , Metacrilatos , Cementos de Resina , Cementos de Resina/química , Descontaminación , Propiedades de Superficie , Agua/química , Resistencia a la Tracción , Ensayo de Materiales , Análisis del Estrés DentalRESUMEN
OBJECTIVES: In-office and lab milled prostheses are the staple for indirect restorations. It is therefore critical to determine their long-term bonding durability. METHODS: CAD/ CAM blocks of two classes of restorative materials: 1) a nano-ceramic reinforced polymer matrix (NCPM) and, 2) a polymer-infiltrated ceramic network (PICN) were bonded using four different universal adhesives (UA) and silane systems. A lithium disilicate glassceramic (LDS) was used as a reference. The blocks were bisected and bonded with different UA/resin-cement pairs. Bonded blocks were then cut into 1.0x1.0x12.0 mm bar specimens for microtensile bond testing. Half the bars were subjected to bond strength testing immediately and the other half after aging by 50,000 thermal cycles between 5°C and 55°C. ANOVA and post-hoc tests were used to compare mean bond strength among groups. RESULTS: NCPM presented consistently high bond strength regardless of bonding techniques, while the bond strength of PICN and LDS were lower when bonded with UA relative to traditional silanes. The more hydrophilic UA produced higher bond strengths. DISCUSSION: Glass-ceramics exhibited lower bond strength with UA than the conventional etch-rinse-silane techniques. However, UAs preserved bonding interface in the long-term. SIGNIFICANCE: NCPM displayed superior bond strength relative to PICN and LDS regardless of the type of adhesives and bonding techniques.
RESUMEN
Ceramic based on zirconium dioxide (ZD) is a modern, durable material for the manufacture of dentures. It is known that ZD is not etched as glass-ceramic, making it difficult to prepare this material before fixing. OBJECTIVE: To study the impact of various methods of surface treatment of ZD-based ceramic on adhesive strength. MATERIALS AND METHODS: Sandblasting with Al2O3 particles sized 50 µm and application of primers with 10-MDP phosphate monomer were used. Adhesive strength values for following 4 groups of samples were obtained: 1st group - RelyX U200 + sandblasting + Compofix new primer (n=9); 2nd group - Compofix + sandblasting + Compofix new primer (n=9); 3rd group - Panavia F 2.0 + sandblasting (n=9); 4th group (control) - Variolink Esthetic DC + sandblasting + Monobond Plus primer (n=9). RESULTS: The highest strength of adhesion was in the 4th group - 48.71±5.71MPa, the smallest in the 3rd group - 9.49±35.24 MPa. Fully domestic components used in the 2nd group allowed to obtain values of 42.50±9.79 MPa. Adhesive strength in the 1st group was 34.11±4.78 MPa. CONCLUSION: The absence of the 10-MDP-based primers application in the preparation of ZD ceramic reduces the adhesive strength between resin cement and its surface. The domestic set for fixation of dentures can be effectively used for ZD on the same basis as European analogue.
Asunto(s)
Propiedades de Superficie , Circonio , Circonio/química , Ensayo de Materiales , Cerámica/química , Recubrimiento Dental Adhesivo/métodos , Cementos de Resina/química , Humanos , Cementos Dentales/química , Grabado Dental/métodosRESUMEN
OBJECTIVE: The purpose of this study was to perform an integrative review on laser texturing the inner surface of lithium disilicate-reinforced glass ceramic or zirconia to increase their bond strength to resin-matrix cements. MATERIALS AND METHOD: A bibliographic review was performed on PubMed using the following search terms: "zirconia" OR "lithium disilicate" AND "laser" AND "surface" OR "roughness" AND "bond strength" AND "luting agent" OR "resin cement." Studies published in English language until March 15, 2023, were selected regarding the purpose of this study. RESULTS: A total of fifty-six studies were identified althoug thirteen studies were selected. The findings revealed that zirconia surfaces were significantly modified after laser irradiation resulting in macro-scale aligned retentive regions with depth values ranging from 50 to 120 µm. Average roughness values of laser-textured zirconia by Er,Cr:YSGG laser (~ 0.83 µm) were quite similar when compared to grit-blasted zirconia surfaces (~ 0.9 µm) although roughness increased up to 2.4 µm depending on the laser type and parameters. Lithium disilicate-reinforced glass ceramics textured with Er:YAG revealed an average roughness of around 3.5 µm while surfaces textured using Nd:YAG laser revealed an average roughness of 2.69 µm; that was quite similar to the roughness values recorded for etched surfaces (2.64 µm). The shear bond strength (SBS) values of zirconia surfaces textured on Nd:YVO4 laser irradiation were slightly higher (~ 33.5 MPa) than those recorded for grit-blasted zirconia surfaces (28 MPa). Laser-textured zirconia surfaces on CO2 laser revealed higher SBS values (18.1 ±0.8 MPa) than those (9.1 ± 0.56 MPa) recorded for untreated zirconia surfaces. On lithium disilicate-reinforced glass ceramics, higher SBS values to resin-matrix cements were recorded for specimens textured with a combination of fractional CO2 laser irradiation and HF acid etching (~ 22-24 MPa) when compared with grit-blasted specimens (12.2 MPa). Another study revealed SBS values at around 27.5 MPa for Er:YAG-textured lithium disilicate-reinforced glass ceramics to resin-matrix cements. CONCLUSIONS: The laser irradiation at high power increases the roughness of the inner surface of lithium disilicate-reinforced glass ceramic or zirconia leading to an enhanced bond strength to resin-matrix cements. Thus, the laser type and irradiation parameters can be adjusted to enhance the macro- and micro-scale retention of zirconia and glass ceramic surfaces to resin-matrix cements. CLINICAL RELEVANCE: Alternative methods for surface modification of lithium disilicate-reinforced glass ceramic and zirconia surfaces have been assessed to provide proper morphological aspects for enhanced adhesion to resin-matrix cements. An increase in the bond strength of glass ceramics or zirconia to resin-matrix cements can improve the long-term performance of cemented prosthetic structures in the oral cavity.
Asunto(s)
Recubrimiento Dental Adhesivo , Láseres de Estado Sólido , Cementos de Resina/química , Litio , Dióxido de Carbono , Propiedades de Superficie , Cerámica/química , Porcelana Dental/química , Resistencia al Corte , Ensayo de Materiales , Circonio/químicaRESUMEN
OBJECTIVES: The objective of this study is to evaluate the longevity of two fiber post cementation strategies in a prospective, multicenter, non-inferiority, double-blind randomized controlled trial. METHODS: A total of 152 teeth, with adequate endodontic treatment and loss of coronal structure and bilateral simultaneous posterior occlusal contacts, were randomly allocated to receive glass fiber posts cemented with a conventional cementation strategy (CRC group: adhesive system + resin cement) (Adper Single Bond + RelyX ARC; 3 M-ESPE) or a self-adhesive cementation strategy (SRC group: self-adhesive resin cement; RelyX U100/U200; 3 M-ESPE). The patients were recalled annually for clinical and radiographical evaluation with a 93% recall rate (142 teeth, with 74 at CR groups and 68 at SRC group). The primary outcome was survival rate, considering the fiber post debonding (loss of retention). The secondary outcome included the success rate of the prosthetic treatment with crown debonding, post fracture, and tooth loss (not related to post failure). Both outcomes were evaluated annually. The Kaplan-Meier method and Cox regression with 95% confidence interval were used for the statistical analysis. RESULTS: For the primary outcome (failures directly related to fiber posts cementation strategy), there were 4 fiber post debondings (2 per group), 8 root fractures (3 for SRC group and 5 for CRC group), and one mixed failure (debonding combined with root fracture for CRC), with both strategies presenting similar survival rates (p = 0.331), with 88.9% for the CRC group and 90.9% for the SRC group. For the secondary outcome (failures not related to fiber post cementation strategies), there were 8 crown debondings, 3 post fractures, and 3 tooth losses, with no statistically difference between groups (p = 0.701), with 77% for SRC and 82% for CRC. CONCLUSION: Fiber post cementation strategies with conventional or self-adhesive resin cement presents similar tooth survival and success rates. TRIAL REGISTRATION: NCT01461239 CLINICAL RELEVANCE: Both adhesive cementation strategies led to high survival and success rates and are indicated for fiber post cementation, even after a long follow-up period (up to 106 months).
Asunto(s)
Recubrimiento Dental Adhesivo , Técnica de Perno Muñón , Humanos , Cementos de Resina/química , Cementación/métodos , Cementos Dentales/química , Tasa de Supervivencia , Estudios Prospectivos , Vidrio/química , Ensayo de Materiales , Análisis del Estrés Dental , DentinaRESUMEN
OBJECTIVES: To evaluate the longevity of metal-ceramic single crowns cemented onto resin composite prosthetic cores using a self-adhesive resin cement in a prospective clinical descriptive study. METHODS: A total of 152 teeth were endodontically treated and received resin composite prosthetic cores and metal-ceramic crowns cemented with a self-adhesive resin cement. The patients included in the sample were recalled for clinical and radiography evaluation in an up-to-106-month period after the final cementation procedures, with an average of 62 months of follow-up. 91.5% of the sample (142 teeth) were evaluated regarding the treatment survival rate, analyzed considering the loss of crown retention (crown debonding) and tooth loss as the primary outcome. In addition, post debonding, and root fracture occurrences were also recorded as secondary outcomes to evaluate the success rate of the prosthetic treatment. The aesthetic parameters were also evaluated according to the FDI criteria. The Kaplan-Meier method and Cox regression with 95% confidence interval were applied for the statistical analysis. RESULTS: Regarding the primary outcome, the metal-ceramic crowns cemented with self-adhesive resin cement presented a high survival rate (91.5%), with 8 crown debondings and 3 tooth losses (1 due to caries and 2 due to periodontal disease) occurring after the evaluation period. For secondary outcomes, 9 root fractures and 4 post debondings occurred, generating a success rate of 72%. All crowns had a score 1 on the FDI criteria, indicating that they were clinically excellent or very good regarding the aesthetic parameters. CONCLUSION: The metal-ceramic crowns luted with a self-adhesive resin cement presented a survival rate of 91.5% after an average of 62 months of follow-up. Furthermore, the restorations remained aesthetically satisfactory over time, without changes that would indicate prosthetic retreatment. A success rate of 72% was obtained considering the secondary outcome, mainly related to intraradicular retainer failures (root fractures or post debonding). CLINICAL SIGNIFICANCE: The self-adhesive resin cement is clinically indicated for cementation of metal-ceramic crowns onto resin composite prosthetic cores.
Asunto(s)
Cementos Dentales , Cementos de Resina , Humanos , Estudios de Seguimiento , Estética Dental , Resinas Compuestas , Coronas , Cementación/métodos , Cerámica , Ensayo de Materiales , Fracaso de la Restauración DentalRESUMEN
OBJECTIVES: Photo- and dual-polymerized resin-based luting agent was evaluated for elastic moduli effects on ultra-thin lithium disilicate (LD) glass-ceramic strengthening, structural reliability, and stress distribution. MATERIALS AND METHODS: One hundred-sixty LD discs (IPS e.max CAD, Ivoclar/Vivadent) were produced in ultra-thin thicknesses (half with 0.3 mm and the other half with 0.5 mm). The ultra-thin ceramic disks were coated with two different cement types (Variolink Veneer - V and Panavia F 2.0 - P). Two positive control groups were tested following hydrofluoric (HF) acid etching (LDt3, LDt5) and two negative control groups were tested for untreated ceramic (LD 3, LD 5). Biaxial flexural strength (BFS), characteristic strength (σ0) and Weibull modulus (m) were the response variables (n = 20) at the ceramic/resin cement interface (z = 0). Finite element analysis (FEA) was used to calculate maximum principal stress. Data were analyzed using two-way ANOVA, and Tukey's test. Scanning electron microscopy (SEM) was used to analyze the failed specimens using fractography and surface morphology. RESULTS: The BFS of LD at either thickness was not affected by cement types, as also demonstrated by FEA. Structural reliability significantly improved in the positive control group (LDt5). CONCLUSION: The cementation of ultra-thin LD with a resin-cement of varying elastic moduli did not influence BFS. LD surface modification by HF acid-etching increased the reliability. CLINICAL RELEVANCE: Ultra-thin anterior veneer designs made from lithium disilicate have been widely proposed and the apparent success of LD ultra-thin veneers was not influenced by the cement choice in the current studies albeit the elastic moduli luting agents used were of similar values.
Asunto(s)
Recubrimiento Dental Adhesivo , Cementos de Resina , Cementos de Resina/química , Resistencia Flexional , Módulo de Elasticidad , Reproducibilidad de los Resultados , Ensayo de Materiales , Propiedades de Superficie , Porcelana Dental/química , Cerámica/química , Cementos Dentales , Ácido Fluorhídrico/químicaRESUMEN
OBJECTIVES: To investigate the clinical performance of chairside fabricated tooth-supported posterior single crowns from lithium disilicate ceramic. MATERIALS AND METHODS: Thirty-four crowns (IPS e.max CAD, Ivoclar Vivadent, Schaan, Liechtenstein) were inserted between 2006 and 2007 and again evaluated after 15 years. Survival and success rates were calculated according to Kaplan-Meier, and the quality of the crowns was evaluated by using modified United States Public Health (USPHS) criteria. RESULTS: Twenty-two crowns were available for recall; six patients were defined as dropouts. The mean observation period was 15.2 years (± 0.2). Six failures occurred (1 technical/5 biological) resulting in a survival rate of 80.1%. The success rate was 64.2%. The roughness of the crowns increased (p = 0.021) and the majority of adhesive gaps were discolored (p = 0.001) in comparison to baseline. The color, tooth, and crown integrity remained stable over the follow-up period (p ≥ 0.317). CONCLUSION: The fabrication of tooth-supported lithium disilicate crowns using a chairside approach yielded acceptable long-term survival and success rates. Due to discoloration, the long-term use of dual-cure self-adhesive resin cements might result in unpleasing esthetic results. CLINICAL RELEVANCE: The performance of posterior lithium disilicate single crowns revealed excellent to good clinical quality and an acceptable number of events after 15 years of clinical service.
Asunto(s)
Diseño Asistido por Computadora , Diseño de Prótesis Dental , Humanos , Estética Dental , Porcelana Dental , Coronas , Cerámica , Fracaso de la Restauración DentalRESUMEN
The main aim of this study was to perform an integrative review on the toxic effects of resin-matrix cements and their products in contact with fibroblasts or mesenchymal cells. A bibliographic search was performed on PubMed using the following search terms: "cytotoxicity" AND "fibroblast" OR "epithelial" OR "mesenchymal" AND "polymerization" OR "degree of conversion" OR "methacrylate" OR "monomer" AND "resin cement" OR "resin-based cement". The initial search in the available database yielded a total of 277 articles of which 21 articles were included in this review. A decrease in the viability of mouse fibroblasts ranged between 13 and 15% that was recorded for different resin-matrix cements after light curing exposure for 20 s. The viability of human fibroblasts was recorded at 83.11% after light curing for 20 s that increased up to 90.9% after light curing exposure for 40 s. Most of the studies linked the highest toxicity levels when the cells were in contact with Bis-GMA followed by UDMA, TEGDMA and HEMA. Resin-matrix cements cause a cytotoxic reaction when in contact with fibroblasts or mesenchymal cells due to the release of monomers from the polymeric matrix. The amount of monomers released from the resin matrix and their cytotoxicity depends on the polymerization parameters.