Shear bond strengths between alumina-toughened zirconia cores and veneering ceramics and their susceptibility to aging.
Asian Pac J Trop Med
; 5(5): 402-5, 2012 May.
Article
en En
| MEDLINE
| ID: mdl-22546659
ABSTRACT
OBJECTIVE:
To evaluate the shear bond strength (SBS) between alumina-toughened zirconia (ATZ) cores and veneering ceramics, investigate the effect of aging in artificial saliva on SBS and compare it with that of yttria-stabilized tetragonal zirconia polycrystals(Y-TZP).METHODS:
Bars of ATZ and Y-TZP were layered with veneering ceramics in accordance to the recommendation of the manufacturer. Half of each group (n = 10) was aged at 134 °C (under 2 bar pressure) in an autoclave for 48 h. Subsequently, all specimens were subjected to shear force in a universal testing machine. The interface and fractured surface of the specimens were evaluated using scanning electron microscopy and X-ray energy dispersive spectroscopy.RESULTS:
The initial mean SBS values in MPa±SD were 28.9±8.0 for ATZ and 26.2±7.6 for Y-TZP. After aging, the mean SBS values for ATZ and Y-TZP were 22.9±4.9 MPa and 22.8±6.9 MPa, respectively. Neither the differences between the SBS values of the ATZ and Y-TZP groups nor the influence of aging on all groups were statistically significant.CONCLUSIONS:
The SBS between the ATZ core and the veneering ceramics was not affected by aging. The SBS of ATZ to veneering ceramics was not significantly different compared with that of Y-TZP.
Texto completo:
1
Colección:
01-internacional
Banco de datos:
MEDLINE
Asunto principal:
Circonio
/
Cerámica
/
Resistencia al Corte
/
Coronas con Frente Estético
/
Óxido de Aluminio
Idioma:
En
Revista:
Asian Pac J Trop Med
Año:
2012
Tipo del documento:
Article