Extrinsic Hardening of Superhard Tungsten Tetraboride Alloys with Group 4 Transition Metals.
J Am Chem Soc
; 138(17): 5714-21, 2016 05 04.
Article
en En
| MEDLINE
| ID: mdl-27113430
ABSTRACT
Alloys of tungsten tetraboride (WB4) with the group 4 transition metals, titanium (Ti), zirconium (Zr), and hafnium (Hf), of different concentrations (0-50 at. % on a metals basis) were synthesized by arc-melting in order to study their mechanical properties. The phase composition and purity of the as-synthesized samples were confirmed using powder X-ray diffraction (PXRD) and energy dispersive X-ray spectroscopy (EDS). The solubility limit as determined by PXRD is 20 at. % for Ti, 10 at. % for Zr, and 8 at. % for Hf. Vickers indentation measurements of WB4 alloys with 8 at. % Ti, 8 at. % Zr, and 6 at. % Hf gave hardness values, Hv, of 50.9 ± 2.2, 55.9 ± 2.7 and 51.6 ± 2.8 GPa, respectively, compared to 43.3 GPa for pure WB4 under an applied load of 0.49 N. Each of the aforementioned compositions are considered superhard (Hv > 40 GPa), likely due to extrinsic hardening that plays a key role in these superhard metal borides. Furthermore, these materials exhibit a significantly reduced indentation size effect, which can be seen in the plateauing hardness values for the W1-xZrxB4 alloy. In addition, W0.92Zr0.08B4, a product of spinoidal decomposition, possesses nanostructured grains and enhanced grain hardening. The hardness of W0.92Zr0.08B4 is 34.7 ± 0.65 GPa under an applied load of 4.9 N, the highest value obtained for any superhard metal at this relatively high loading. In addition, the WB4 alloys with Ti, Zr, and Hf showed a substantially increased oxidation resistance up to â¼460 °C, â¼510 °C, and â¼490 °C, respectively, compared to â¼400 °C for pure WB4.
Texto completo:
1
Colección:
01-internacional
Banco de datos:
MEDLINE
Idioma:
En
Revista:
J Am Chem Soc
Año:
2016
Tipo del documento:
Article