J e (4.2 K, 31.2 T) beyond 1 kA/mm2 of a ~3.2 µm thick, 20 mol% Zr-added MOCVD REBCO coated conductor.
Sci Rep
; 7(1): 6853, 2017 07 31.
Article
en En
| MEDLINE
| ID: mdl-28761173
ABSTRACT
A main challenge that significantly impedes REBa2Cu3Ox (RE = rare earth) coated conductor applications is the low engineering critical current density J e because of the low superconductor fill factor in a complicated layered structure that is crucial for REBa2Cu3Ox to carry supercurrent. Recently, we have successfully achieved engineering critical current density beyond 2.0 kA/mm2 at 4.2 K and 16 T, by growing thick REBa2Cu3Ox layer, from â¼1.0 µm up to â¼3.2 µm, as well as controlling the pinning microstructure. Such high engineering critical current density, the highest value ever observed so far, establishes the essential role of REBa2Cu3Ox coated conductors for very high field magnet applications. We attribute such excellent performance to the dense c-axis self-assembled BaZrO3 nanorods, the elimination of large misoriented grains, and the suppression of big second phase particles in this ~3.2 µm thick REBa2Cu3Ox film.
Texto completo:
1
Colección:
01-internacional
Banco de datos:
MEDLINE
Idioma:
En
Revista:
Sci Rep
Año:
2017
Tipo del documento:
Article
País de afiliación:
Estados Unidos