Plasma enhanced atomic layer deposition of silicon nitride using magnetized very high frequency plasma.
Nanotechnology
; 35(27)2024 Apr 18.
Article
en En
| MEDLINE
| ID: mdl-38522102
ABSTRACT
To obtain high-quality SiNxfilms applicable to an extensive range of processes, such as gate spacers in fin field-effect transistors (FinFETs), the self-aligned quadruple patterning process, etc, a study of plasma with higher plasma density and lower plasma damage is crucial in addition to study on novel precursors for SiNxplasma-enhanced atomic layer deposition (PEALD) processes. In this study, a novel magnetized PEALD process was developed for depositing high-quality SiNxfilms using di(isopropylamino)silane (DIPAS) and magnetized N2plasma at a low substrate temperature of 200 °C. The properties of the deposited SiNxfilms were analyzed and compared with those obtained by the PEALD process using a non-magnetized N2plasma source under the same conditions. The PEALD SiNxfilm, produced using an external magnetic field (ranging from 0 to 100 G) during the plasma exposure step, exhibited a higher growth rate (â¼1 Å/cycle) due to the increased plasma density. Additionally, it showed lower surface roughness, higher film density, and enhanced wet etch resistance compared to films deposited using the PEALD process with non-magnetized plasmas. This improvement can be attributed to the higher ion flux and lower ion energy of the magnetized plasma. The electrical characteristics, such as interface trap density and breakdown voltage, were also enhanced when the magnetized plasma was used for the PEALD process. Furthermore, when SiNxfilms were deposited on high-aspect-ratio (301) trench patterns using the magnetized PEALD process, an improved step coverage of over 98% was achieved, in contrast to the conformality of SiNxdeposited using non-magnetized plasma. This enhancement is possibly a result of deeper radical penetration enabled by the magnetized plasma.
Texto completo:
1
Colección:
01-internacional
Banco de datos:
MEDLINE
Idioma:
En
Revista:
Nanotechnology
Año:
2024
Tipo del documento:
Article