RESUMEN
A low ratio of polymerization is a major problem in resin-based composites. In this paper, the plasmonic effect of gold-covered silica nanoparticles on the physicochemical and mechanical properties of bisphenol A diglycidyl dimethacrylate (Bis-GMA), triethylene glycol dimethacrylate (TEGDMA) and urethane dimethacrylate (UDMA) green light-photopolymerizable dental resin was investigated at an intensity of 1.4 mW/cm2 for 40 s. Transmission electron microscopy (TEM) showed silica of about 350 nm covered with 12-15 nm gold nanoparticles (Au NPs) at 100% nominal coverage. Five different concentrations of bare and patchy silica particles were used; in the latter composite, the calculated Au wt% were 0.0052 wt%, 0.0104 wt%, 0.0208 wt%, 0.04160 wt%, and 0.0823 wt%. The plasmon peak of patchy silica-filled nanocomposite overlapped with the absorption of Irgacure 784 photoinitiator and green LED light emission peak. The effect of plasmon-enhanced polymerization achieved with green light illumination was analyzed using diametral tensile strength (DTS), differential scanning calorimetry (DSC), surface plasmon resonance imaging (SPRi), and degree of conversion (DC) based on Raman spectroscopy. The values of the Au NP with 0.0208 wt% was found to be maximum in all the measured data. Based on our result, it can be concluded that the application of patchy silica particles in dental resin can improve the polymerization ratio and the mechanical parameters of the composite.
RESUMEN
The focused electron beam-induced deposition (FEBID) process was used by employing a GeminiSEM with a beam characteristic of 1 keV and 24 pA to deposit pillars and line-shaped nanostructures with heights between 9 nm and 1 µm and widths from 5 nm to 0.5 µm. All structures have been analyzed to their composition looking at a desired Si/O/C content measuring a 1:2:0 ratio. The C content of the structure was found to be â¼over 60% for older deposits kept in air (â¼at room temperature) and less than 50% for later deposits, only 12 h old. Upon depositing Si(OEt)4 at high rates and at a deposition temperature of under 0 °C, the obtained Si content of our structures was between 10 and 15 atom % (compositional percentage). The FEBID structures have been deposited on Au(111)/SiO2. The Au(111) was chosen as a substrate for the deposition of Si(OEt)4 due to its structural and morphological properties. With its surface granulation following a Chevron pattern and surface defects having an increased contribution to the changes in the composition of the final structure content, the Au(111) surface characteristic behavior at the deposition of Si(OEt)4 is an increase in the O ratio and a reduction in the nanodeposit heights.
RESUMEN
In this study, scaffolds were prepared via an electrospinning method for application in oral cavities. The hydrophilicity of the fiber mesh is of paramount importance, as it promotes cell spreading; however, the most commonly used polyvinyl alcohol (PVA) and other hydrophilic fiber meshes immediately disintegrate in aqueous media. In contrast, the excessive hydrophobicity of the scaffolds already inhibits cells adhesion on the surface. Therefore, the hydrophilicity of the fiber meshes needed to be optimized. Scaffolds with different polyvinyl alcohol (PVA)/chitosan/citric acid ratios were prepared. The addition of chitosan and the heat initiated cross-linkage of the polymers via citric acid enhanced the scaffolds' hydrophobicity. The optimization of this property could be followed by contact angle measurements, and the increased number of cross-linkages were also supported by IR spectroscopy results. The fibers' physical parameters were monitored via low-vacuum scanning electron microscopy (SEM) and atomic force microscopy (AFM). As biocompatibility is essential for dental applications, Alamar Blue assay was used to prove that meshes do not have any negative effects on dental pulp stem cells. Our results showed that the optimization of the fiber nets was successful, as they will not disintegrate in intraoral cavities during dental applications.
RESUMEN
Gold nanoparticles (AuNPs) display surface plasmon resonance (SPR) as a result of their irradiation at a targeted light frequency. SPR also results in heat production that increases the temperature of the surrounding environment, affecting polymerization. The aim was to investigate the SPR effect of AuNPs on a dimethacrylate-based photopolymer system. The tested composites were designed to overlap the illumination required for the polymerization and the plasmon effect. The 5 nm-sized dodecanethiol capped AuNPs were applied in different concentrations in the matrix that were irradiated with green light (λ = 532 nm), where the Irgacure 784 photoinitiator also absorbs the light. The plasmonic effect was investigated for the refractive index change by surface plasmon resonance imaging (SPRi) supplemented by ellipsometry. Moreover, optical transmission and transmission electron micrographs (TEM), diametral tensile stress (DTS), and confocal Raman spectroscopy was performed to determine the degree of conversion (DC) at 1.0, 1.4, and 2.0 mW/cm2 light intensities. It was found that the optimal conditions were at 0.0208 wt% AuNPs concentration and 1.4 mW/cm2 light intensity at which the refractive index change, DTS, and DC data were all maximal. The study confirmed that AuNPs are applicable to improve the polymerization efficiency of dental composite resin.
RESUMEN
INTRODUCTION: In this work we selected components, developed technology and studied a number of parameters of polymer nanocomposite materials, remembering that the material would have high optical and good mechanical characteristics, good sorption ability in order to ensure high value of the optical signal for a short time while maintaining the initial geometric shape. In addition, if this nanocomposite is used for medicine and biology (biocompatible or biocidal materials or the creation of a sensor based on it), the material must be non-toxic and/or biocompatible. We study the creation of polymer nanocomposites which may be applied as biocompatible materials with new functional parameters. MATERIAL AND METHODS: A number of polymer nanocomposites based on various urethane-acrylate monomers and nanoparticles of gold, silicon oxides, zinc and/or titanium oxides are obtained, their mechanical (microhardness) properties and wettability (contact angle) are studied. The set of required, biology-related properties of these materials, such as toxicity and sorption of microorganisms are also investigated in order to prove their possible applicability. RESULTS AND DISCUSSION: The composition of the samples influences their microhardness and the value of contact angle, which means that varying with the monomer and the metallic, oxide nanoparticles composition, we could change these parameters. Besides it, the set of required, biology-related properties of these materials, such as toxicity and sorption of microorganisms were also investigated in order to prove their possible applicability. It was shown that the materials are non-toxic, the adhesion of microorganisms on their surface also could be varied by changing their composition. CONCLUSION: The presented polymer nanocomposites with different compositions of monomer and the presence of nanoparticles in them are prospective material for a possible bio-application as it is biocompatible, not toxic. The sorption of microorganism could be varied depending on the type of bacterias, the monomer composition, and nanoparticles.
RESUMEN
Objectives: Using dental Ti implants has become a well-accepted and used method for replacing missing dentition. It has become evident that in many cases peri-implant inflammation develops. The objective was to create and evaluate the antibacterial effect of silver nanoparticle (Ag-NP) coated Ti surfaces that can help to prevent such processes if applied on the surface of dental implants. Methods: Annealing I, Ag ion implantation by the beam of an Electron Cyclotron Resonance Ion Source (ECRIS), Ag Physical Vapor Deposition (PVD), Annealing II procedures were used, respectively, to create a safely anchored Ag-NP layer on 1x1 cm2 Grade 2 titanium samples. The antibacterial effect was evaluated by culturing Staphylococcus aureus (ATCC 29213) on the surfaces of the samples for 8 hours, and comparing the results to that of glass as control and of pure titanium samples. Alamar Blue assay was carried out to check cytotoxicity. Results: It was proved that silver nanoparticles were present on the treated surfaces. The average diameter of the particles was 58 nm, with a 25 nm deviation and Gaussian distribution, the the filling factor was 25%. Antibacterial evaluation revealed that the nanoparticle covered samples had an antibacterial effect of 64.6% that was statistically significant. Tests also proved that the nanoparticles are safely anchored to the titanium surface and are not cytotoxic. Conclusion: Creating a silver nanoparticle layer can be an option to add antibacterial features to the implant surface and to help in the prevention of peri-implant inflammatory processes. Recent studies demonstrated that silver nanoparticles can induce pathology in mammal cells, thus safe fixation of the particles is essential to prevent them from getting into the circulation.
Asunto(s)
Implantación Dental/métodos , Nanopartículas del Metal/química , Plata/farmacología , Titanio/farmacología , Animales , Antibacterianos/farmacología , Supervivencia Celular/efectos de los fármacos , Materiales Biocompatibles Revestidos/farmacología , Iones , Pruebas de Sensibilidad Microbiana , Tamaño de la Partícula , Staphylococcus aureus/efectos de los fármacos , Células Madre/citología , Células Madre/efectos de los fármacos , Células Madre/ultraestructura , Propiedades de SuperficieRESUMEN
An unprecedented rate enhancement was observed in the wet-chemical synthesis of tellurium nanowires under crowded conditions of inert macromolecules. The synthesis was carried out at 105 °C using solutions of sodium tellurite (Na2TeO3) as a precursor, hydrazine (N2H4) as a reducing agent, and polyvinylpyrrolidone (PVP) as both a stabilizing and crowding agent. The PVP concentration was systematically varied between the dilute and crowding regimes up to 166 g l-1. The growth of the nanowires was monitored by measuring their size-dependent optical properties in the UV-Vis spectrum characterizing the size and morphology evolution of the nanowires and a coexisting phase of amorphous tellurium nanoparticles. The observed growth characteristics were interpreted in terms of non-specific structural organization of the crowded media due to the entropic-driven effects of space compartmentalization.
RESUMEN
Herein, a microfluidic device (MD) containing immobilized trypsin for rapid and efficient proteolysis was described. Trypsin was immobilized via non-specific protein adsorption onto the hydrophobic poly(dimethylsiloxane) (PDMS) channel wall of the MD. Peptide mapping of bovine serum albumin (BSA) samples was carried out to estimate the stability of trypsin adsorbed on PDMS surface. Peptide maps of BSA samples were obtained by capillary zone electrophoresis (CZE), the RSD% for migration times were under 1%. Several proteins (hemoglobin, myoglobin, lysozyme, and BSA) in a wide molecular size range (15-70 kDa) were digested efficiently with â¼50 s contact time. The number of separated peaks correlated well with the expected number of peptides formed in the complete tryptic digestion of the proteins. Peptide mass fingerprinting of BSA and human serum was carried out. Trypsin retained its activity for 2 h; within this period, the MD can be used for multiple digestions. The main properties of this device are simple channel pattern, simple immobilization procedure, regenerability, and disposability; all these features make this MD one of the simplest yet applicable enzymatic microreactors. Graphical abstract Development of microfluidic device including a serpentine channel as an enzyme reactor for protein digestion.
Asunto(s)
Dimetilpolisiloxanos/química , Enzimas Inmovilizadas/química , Mapeo Peptídico/métodos , Péptidos/análisis , Albúmina Sérica Bovina/química , Tripsina/química , Adsorción , Animales , Bovinos , Electroforesis Capilar/métodos , Diseño de Equipo , Interacciones Hidrofóbicas e Hidrofílicas , Dispositivos Laboratorio en un Chip , Mapeo Peptídico/instrumentación , PorcinosRESUMEN
Rare-earth-doped optical materials are important for light sources in optoelectronics, as well as for efficient optical amplification elements and other elements of photonics. On the basis of the previously developed method of anhydrous, low-temperature synthesis of Er/Yb oxides from their chlorides we fabricated proper nanoparticles with defined parameters and used them for the development of optically transparent, luminescent polymer nanocomposite with low optical scattering, suitable for direct, light-induced formation of photonic elements. Introduction of preformed gold nanoparticles in such a nanocomposite was also performed and an enhancement of luminescence due to the influence of plasmon effects was detected.