RESUMEN
This study aimed to evaluate the microleakage of light-cured and self-cured adhesives on enamel surfaces selectively etched with Er, Cr: YSGG laser or 35% phosphoric acid. A total of 60 class V cavities were prepared 1 mm above the cemento-enamel junction (CEJ). The specimens were randomly divided into six groups. Group 1: Clearfil SE Bond with no conditioning, Group 2: Tokuyama Universal Bond with no conditioning, Group 3: Clearfil SE Bond conditioned with 35% phosphoric acid, Group 4: Tokuyama Universal Bond conditioned with 35% phosphoric acid, Group 5: Clearfil SE Bond conditioned with Er, Cr: YSGG laser and Group 6: Tokuyama Universal Bond conditioned with Er, Cr: YSGG laser. Microleakage was evaluated qualitatively (visually) and quantitatively (ImageJ). The data were analyzed using IBM SPSS V23 and submitted to Kruskal-Wallis and Wilcoxon tests. The significance level was set at p < 0.05. In all evaluation methods, the microleakage scores exhibit significant differences (p*<0.001). Group 1 and Group 3 exhibited similar and lower microleakage values than the Group 5. In the occlusal margin, the microleakage values were similar in Group 2, Group 4, and Group 6, whereas in the gingival margin Group 4 showed significantly lower leakage compared to Group 2. Regardless of the etching protocols and adhesive systems used, less microleakage was observed on the occlusal surface than on the gingival surface. Phosphoric acid etching provides better results than laser etching for enamel surface treatment on both occlusal and gingival surfaces.
Asunto(s)
Grabado Ácido Dental , Esmalte Dental , Filtración Dental , Láseres de Estado Sólido , Humanos , Esmalte Dental/efectos de la radiación , Esmalte Dental/efectos de los fármacos , Láseres de Estado Sólido/uso terapéutico , Cementos de Resina/química , Ácidos Fosfóricos/química , Cementos Dentales/química , Técnicas In VitroRESUMEN
This study evaluated bond strength of glass fiber posts to root dentin using push-out (PO) and diametral compression (DC), testing glycolic acid as a conditioner and varying dentin moisture. An additional aim was to test whether DC can be an alternative test to PO for bond strength assessment. Eighty bovine teeth were divided into eight groups (n = 10) defined by the use of either 37% glycolic acid or 37% phosphoric acid (PA) on moist or wet dentin before bonding with either Adapter SingleBond/RelyX ARC or One Step Plus/Duo-Link Bisco. Each tooth provided discs with an internal diameter of 2 mm, external diameter of 5 mm, and height of 2 mm, which underwent PO and DC. Finite element analysis (FEA) was carried out on 3D models. When analyzing PO results through linear regression, the highest values of bond strength were observed using glycolic acid on wet dentin in the cervical and middle thirds of the teeth. Analyzing DC results, the only statistical influence on values was the dental thirds. The scatterplot of the DC results and the PO bond strength values indicated no relationship between the results of the two tests (r = 0.03; p = 0.64). PO test detected more sensitive changes in bond strength values than DC.
Asunto(s)
Recubrimiento Dental Adhesivo , Dentina , Análisis de Elementos Finitos , Vidrio , Ácidos Fosfóricos , Técnica de Perno Muñón , Animales , Bovinos , Dentina/efectos de los fármacos , Vidrio/química , Ácidos Fosfóricos/química , Recubrimientos Dentinarios/química , Cementos de Resina/química , Análisis del Estrés Dental , Ensayo de Materiales , Raíz del Diente , Glicolatos/química , Grabado Ácido DentalRESUMEN
Solvent evaporation within an adhesive layer is a crucial step during a bonding process. The aim of this current research was to test whether the use of different air temperatures (20 °C, 40 °C, and 60 °C) for solvent evaporation improves the performance of four adhesive systems to dentin. Sixty non-carious human molar teeth were randomly prepared for micro-tensile bond strength (µTBS) tests. Four different adhesive systems, Prime&Bond Universal (PBU), OptiBond Universal (OBU), OptiBond FL (OBFL), and Clearfil SE (CSE), were applied following the manufacturer's instructions. Three groups based on the air-drying temperature were used: solvent evaporation was performed with either of warm (40 °C), (60 °C), and cold air as control group (20 °C) for 10 s at a distance of 5 cm. In all bonded surfaces, three resin composite (Reflectys, Itena Clinical, Paris, France) layers of 2 mm thickness were built up. The resin-dentin samples were kept in distilled water at 37 °C for 24 h and 6 months, respectively, before µTBS testing. Failure analysis, scanning electron microscopy of resin-dentin bonded interface, and solvent evaporation rate were tested as secondary variables. All analyses were conducted using a significance level of α = 0.05. Bond strength (BS) values were similar among all the adhesive systems used (p > 0.05). Also, the aging factor did not affect the BS (p > 0.05). Only the factor of temperature used for solvent evaporation resulted in a statistically significant effect (p < 0.05), with the temperature of 60 °C being the highest value (p < 0.05). A failure mode evaluation revealed mostly adhesive or mixed modes of failures in all the different temperatures of air used for the solvent evaporation of each adhesive system. The thickness of the adhesive layer and the creation of resin tags varied amongst the temperatures evaluated. For all adhesive systems tested, the use of 40 °C or 60 °C air for solvent evaporation led to an increased mass loss. Warmer temperatures for solvent evaporation contributed positively to bonding performance, enhancing both the quality of the adhesive layer and its interaction with the dentin tissue. Optimizing solvent evaporation with warmer air temperatures (40 °C and 60 °C) significantly improved µTBS, offering a practical means to enhance the quality and longevity of adhesive restorations in esthetic dentistry.
RESUMEN
The aim of this study was to examine the influence of the orthodontic bracket material on the short-term and long-term post-cure development of the degree of conversion (DC) of resin-based orthodontic adhesive systems. Five commercially available materials characterized by different compositions and curing modes (light-curable or dual-curable) were tested under three different light curing conditions: without brackets (control group, CO), and in the presence of metal brackets (MB group) or ceramic brackets (CB group). Fourier-transform infrared spectroscopy was used to determine the post-cure DC development, both after "short-term" periods (2, 6, and 10 min) and "long-term" periods (1, 7, and 28 days). The short-term DC values ranged from 43.9% to 76.1%, and the long-term DC values were higher and ranged from 54.3% to 85.3%. The MB group demonstrated significantly lower short-term DC values compared to the CO and the CB groups, while the CB group had statistically similar or slightly lower DC values compared to the CO group. Long-term DC values in the MB and the CB groups were statistically lower or similar compared to the CO group, which depended on the post-cure time. The results indicated that the post-cure DC development was highly material-dependent and affected by the presence of different types of bracket material.
RESUMEN
OBJECTIVES: To examine whether dentin-etching extension and/or the hydrophobic-rich content of hybrid layers would affect fatigue strengths of a mild universal adhesive after long-term aging. METHODS: Twin-bonded resin-dentin interfaces were produced by etching sound midcoronal dentin beams with 32 % ortho-phosphoric acid for 15 s (OPA15s), 3 s (OPA3s) or 10 % meta-phosphoric acid for 15 s (MPA15s). Samples were bonded with a mild universal adhesive with or without additional coating using a solvent-free bisGMA-based bonding resin. Self-etch application served as control. Composite buildups were made with a nanofilled composite. Bar-shaped twin-bonded interfaces (0.9 × 0.9 × 12 mm) were aged for two years in artificial saliva at 37 â and tested under 4-point flexure at quasi-static (n = 16) and cyclic loads (n = 35) until failure. The stress-life fatigue behavior was evaluated using the staircase method at 4 Hz. Crack initiation and fracture patterns were evaluated by SEM. Cyclic-loaded data was analyzed by Kruskal-Wallis on Ranks (α = 0.05). RESULTS: Significantly higher fatigue life distributions and higher endurance limits were observed for less aggressive etch-and-rinse protocols (OPA3s and MPA15s) after long-term ageing. Hydrophobic-rich coating produced 20-32 % higher endurance limits, prevented micrometer-sized porosities at bonded interfaces, reduced etching-associated variability and lowered crack formation. Significance Long-term hydrolysis produces detrimental effects on the fatigue strength of resin-dentin interfaces. The bond-promotion effect of less aggressive etch-and-rinse protocols and the creation of hybrid layers with higher hydrophobic-rich content are critical to extend the durability of mild universal adhesives. Therefore, current oversimplification trends in adhesive dentistry may limit resin-dentin bonding performance.
Asunto(s)
Recubrimiento Dental Adhesivo , Cementos Dentales , Recubrimientos Dentinarios , Cementos de Resina , Grabado Ácido Dental/métodos , Recubrimiento Dental Adhesivo/métodos , Dentina , Ensayo de Materiales , Resistencia a la Tracción , AdhesivosRESUMEN
AIM: To evaluate the microtensile bond strength of self-etching adhesive systems in dentin treated with 2% chlorhexidine digluconate (CHX). MATERIALS AND METHODS: The occlusal surfaces of 20 human molars were removed and divided into eight groups: 1A, Clearfil SE adhesive (SE) with self-etching technique (TS); 1B, SE with TS and previous application of CHX; 2A, Scotchbond Universal (SBU) adhesive with TS; 2B, SBU adhesive with TS and previous application of CHX; 1C, SE with total-etching technique (TT); 1D, SE with TT and previous application of CHX; 2C, SBU with TT; 2D SBU with TT and previous application of CHX. Composite resin (5mm) was applied on the hybridized surface. Samples were subjected to microtensile test and evaluated on Scanning Electron Microscope (SEM) and with energy-dispersive X-ray (EDX). RESULTS: Low values of bond strength were observed in groups 1A (39,77±11,56) and 2A (40,84±12,49) comparing with 1B (22,86±5,18) and 2B (27,02±5,58). TS group presented adhesive type remover fracture while TT groups presented cohesive at the top of hybrid layer. EDX revealed the presence of CHX crystals for TS, which was not found in the TT. CONCLUSION: The previous application of chlorhexidine on dentin decreased the bond strength of adhesive systems on self-etching technique.
Asunto(s)
Clorhexidina , Recubrimiento Dental Adhesivo , Humanos , Clorhexidina/química , Cementos Dentales , Recubrimiento Dental Adhesivo/métodos , Cementos de Resina/química , Resinas Compuestas/química , Dentina , Resistencia a la Tracción , Recubrimientos Dentinarios/química , Ensayo de Materiales , AdhesivosRESUMEN
This study evaluated the effect of different concentrations of alpha-tocopherol in gel form on fracture strength, hybrid layer formation, and microtensile bond strength of endodontically treated teeth bleached with 40% hydrogen peroxide (H2 O2 ). Sixty bovine incisors were randomized into one of six groups (n = 10 incisors per group) defined by the interventions carried out after endodontic treatment. In the control group, no additional intervention was carried out, while all teeth in the five intervention groups were bleached with 40% H2 O2 and subsequently treated with alpha-tocopherol at concentrations of 15% (15AT), 20% (20AT), or 25% (25AT), with 10% sodium ascorbate (10SA), or with nothing (40HP). Fracture strength was evaluated in a mechanical testing machine, hybrid layer formation was assessed using scanning electron microscopy, and bond strength was determined using microtensile bond-strength testing. Data were analyzed using Kruskal-Wallis and Dunn's tests. No statistically significant difference regarding fracture strength was observed among groups. Hybrid layer formation was greater in the 15AT group than in groups 40HP and 10SA. Teeth in groups 15AT, 20AT, and 25AT demonstrated higher bond strength than teeth in groups 40HP and 10SA. Alpha-tocopherol, preferably at 15%, effectively reverses the deleterious effects, of bleaching, on hybrid layer formation and bond strength to dentin.
Asunto(s)
Recubrimiento Dental Adhesivo , Blanqueamiento de Dientes , Diente no Vital , Bovinos , Animales , Antioxidantes/química , Antioxidantes/farmacología , alfa-Tocoferol/farmacología , Resistencia Flexional , Resinas Compuestas/química , Ácido HipoclorosoRESUMEN
Abstract This study evaluated a new method of adhesive system application on the bond strength between fiber post and root dentin using two adhesive systems. The canals of sixty bovine incisors were prepared and obturated. The roots were divided into six groups (n=10) according to the adhesive system (Clearfil SE - CSE and Single Bond Universal - SBU) and the application strategy (microbrush - MB; rotary brush - RB; and ultrasonic tip - US). The glass fiber posts were cemented with resin cement (RelyX ARC). The roots were sectioned perpendicularly to their long axis, and three slices per root were obtained. Previously to the push-out test, confocal laser scanning microscopy (CLSM) was performed to illustrate the interfacial adaptation of the cement to the root canal walls. Failure patterns were analyzed with 40x magnification. Shapiro-Wilk indicated a normal distribution of the data. The bond strength values were compared using one-way ANOVA and Tukey's tests. Student's T test analyzed the differences between the adhesive systems within each third and protocol. A significance level of 5% was used. CSE with RB showed higher mean bond strength values compared to MB (conventional technique) (P < 0.05). US application resulted in intermediate bond strength values for CSE (P > 0.05). The application of SBU using RB generated higher mean bond strength values compared to MB and US (P < 0.05). Adhesive failures were predominant (65.5%). CSE and SBU application with the new rotary brush improved the bond strength of fiber posts to root dentin compared to the conventional strategy.
Resumo Este estudo avaliou o efeito de um novo método para aplicação do sistema adesivo na resistência de união entre pino de fibra e dentina radicular usando dois sistemas adesivos. Os canais de sessenta incisivos bovinos foram preparados e obturados. As raízes foram divididas em seis grupos (n=10) de acordo com o sistema adesivo (Clearfil SE - CSE e Single Bond Universal - SBU) e com a estratégia de aplicação (microbrush - MB, escova rotatória - RB e inserto ultrassônico - US). Os pinos de fibra foram cimentados utilizando cimento resinoso (RelyX ARC). As raízes foram seccionadas perpendicularmente ao seu longo eixo e três fatias foram obtidas. Previamente ao teste de push-out, foi realizada microscopia de varredura confocal a laser para ilustrar a adaptação interfacial do cimento às paredes do canal radicular. Os padrões de falha foram analisados com magnificação de 40x. O teste de Shapiro-Wilk indicou distribuição normal dos dados. Os valores de resistência de união foram comparados usando o teste ANOVA de uma via e post hoc de Tukey. As diferenças entre os sistemas adesivos em cada terço e de acordo com cada protocolo foram analisadas pelo teste T de Student. O nível de significância foi de 5%. CSE aplicado com RB apresentou maiores valores médios de resistência de união do que quando aplicado com MB (técnica convencional) (P<0,05). Aplicação com US apresentou valores intermediários de resistência de união para o CSE (P>0,05). A aplicação do SBU utilizando RB gerou maiores valores médios de resistência de união comparados com MB e US (P<0,05). Falhas adesivas foram predominantes (65,5%). A aplicação do CSE e SBU com a nova escova rotatória melhorou a resistência de união dos pinos de fibra à dentina radicular comparados com a estratégia convencional.
RESUMEN
Purpose: The aim of this study is to evaluate the amount of microleakage resulting from the application of self-etch, selective etch, etch-and-rinse of adhesive systems in class II cavities. Materials and methods: Four adhesive systems with etch-and-rinse, selective etch and self etch methods were used on the extracted teeth. All groups were restored with G-aenial A'CHORD (Nanohybrid) (GC, Tokyo, Japan) A2 composite. After 1000 thermal cycles were applied to the teeth after restoration, the samples were kept in 0.5% basic fuchsin for 24 hours. Microleakage values formed after dye penetration with basic fuchsin were determined quantitatively by scoring method on sections taken from each sample in the mesiodistal direction. One-way Analysis of Variance (ANOVA) and Tukey test were used for statistical analysis of the data (p<0.05). Results: While there was no statistically significant difference between the etch-and-rinse and selective etch applications of adhesive systems (G2-Bond Universal, Clearfil Tri-S Bond Universal Prime&Bond Universal and Tokuyama Bond Force II) (p>0.05), there was a statistically significant difference in self-etch application (p<0.05). As a result of Prime&Bond Universal's self-etch application, it showed statistically more microleakage than the other three adhesive systems (p<0.05). Conclusion: It has been observed that additional etching of enamel and/or dentin with phosphoric acid reduces the amount of microleakage.
RESUMEN
The study evaluated the persistence of residues, bond strength and tags formation of a cementation system after post-space irrigation with different sodium hypochlorite-based irrigants. The groups were divided according to the irrigation protocol (DW: distilled water; SHS: sodium hypochlorite solution; SHG: sodium hypochlorite gel; and, SHT: sodium hypochlorite with surfactant). Forty roots (n=10) were used to evaluate the persistence of residues by scanning electron microscopy. Other forty roots were used to the push-out bond strength test, failure mode and tag formation analyses. Non-parametric data were submitted to Kruskal Wallis and Dunn tests, while parametric data were evaluated by one-way ANOVA. No difference was observed in the persistence of residues. DW showed the highest bond strength and tag formation. Type 2 failure mode was the most frequent in the experimental groups. Compared to control, SHT showed the best performance, since less negative effects on adhesive interface was observed.
Asunto(s)
Recubrimiento Dental Adhesivo , Técnica de Perno Muñón , Cementación/métodos , Hipoclorito de Sodio/farmacología , Hipoclorito de Sodio/química , Dentina , Irrigantes del Conducto Radicular , Cementos de Resina/química , Ensayo de MaterialesRESUMEN
OBJECTIVE: This study aims to evaluate the effects of exposure time and irradiance on the dentin bonding properties (microtensile bond strength (µTBS) and nanoleakage (NL)) of the Clearfil Universal Bond Quick (CUQ) adhesive and Scotchbond Universal Adhesive (SBU) immediately and after 2 years of water storage. MATERIAL AND METHODS: Hence, 128 human molars were randomly assigned to 16 groups based on adhesive strategy, irradiance/exposure times, and storage time for each universal adhesive tested. The adhesives were applied using the etch-and-rinse and self-etch strategies and were light-cured using four different irradiance/exposure times: 1400 mW/cm2 for 5 s (1400 × 5), 1400 mW/cm2 for 10 s (1400 × 10), 3200 mW/cm2 for 5 s (3200 × 5), and 3200 mW/cm2 for 10 s (3200 × 10). Then, each sample was restored and sectioned into a resin-dentin bonded stick to be tested for µTBS and NL (immediately and after 2 years of water storage). The mean µTBS and NL of all resin-dentin bonded sticks from the same hemi-tooth (factor time) were statistically analyzed using a three-way ANOVA and Tukey's test (a = 0.05). RESULTS: Despite a significant decrease in the µTBS values for all groups after 2 years of water storage, the 3200 × 5 group showed higher µTBS values, whereas the 3200 × 10 group showed lower µTBS values for both universal adhesives tested. Although a significant increase in the NL values was observed for all groups after 2 years of water storage, the 3200 × 10 group showed higher NL values than the other groups (p < 0.001). CONCLUSION: Results indicate that light-curing the adhesive layer with 14-16 J/cm2 led to an improvement in the stability of the resin-dentin adhesive interface. A longer exposure time (10 s) coupled with a higher irradiance (3200 mW/cm2) resulted in a greater degree of degradation of the adhesive interface. CLINICAL SIGNIFICANCE: To guarantee better stability of the adhesive interface, clinicians could be preferred a light-cured universal adhesive layer with 14-16 J/cm2. Higher irradiances should be avoided.
Asunto(s)
Recubrimiento Dental Adhesivo , Cementos Dentales , Humanos , Recubrimientos Dentinarios/química , Recubrimiento Dental Adhesivo/métodos , Dentina , Cementos de Resina/química , Agua/química , Resistencia a la Tracción , Ensayo de Materiales , Adhesivos , Resinas Compuestas/químicaRESUMEN
The study aimed to investigate the rechargeability of ion-releasing dental material specimens immersed in distilled water for 25 months, which depleted their ion-releasing ability. Four restorative dental materials (alkasite composite, giomer, glass-ionomer, and composite material) presented with 24 specimens were studied after topical treatment with a concentrated fluoride gel. The effect of resin coating on the ion uptake and release was investigated on additional 42 specimens of restorative dental materials with coatings. The composite materials were coated with two adhesive systems, whereas the glass-ionomer was coated with the special coating resin. After topical fluoride exposure, ion release and specimen mass were measured at 1, 2, 3, 4, 5, 6, 7, and 14-day intervals using an ion-selective electrode and an analytical balance, respectively. The cumulative fluoride levels for the uncoated specimens of alkasite composite were significantly higher than those of giomer and glass-ionomer cement, with no statistically significant difference between the latter two materials. The conventional composite had the lowest cumulative concentration of fluoride ions (p < 0.05). The adhesive systems affected the fluoride recharge and reduced the ion concentrations absorbed by the specimens. Specimens coated with universal adhesive showed significantly higher ion release compared to universal fluoride-releasing adhesive or special coating resin for glass-ionomers (p < 0.05). No statistically significant change in specimen mass was observed during the 14-day period. Surface coating with adhesive systems as well as special coating resin for glass-ionomers affects the fluoride recharge process.
RESUMEN
OBJECTIVE: The aim: To study the latest approaches to optimizing the composition and application protocols of modern adhesive systems, which are used during the restoration of defects in hard dental tissues with restorative materials. PATIENTS AND METHODS: Materials and methods: Thirty articles published between January 1, 2020 and February 1, 2023 in the scientific databases PubMed, Scopus, and Google Scholar were selected. The selected scientific works contained the results of laboratory studies, systematic reviews, meta-analyses of the physical and mechanical characteristics of adhesive systems with a modified composition or application protocols different from the instructions of the manufacturing companies. CONCLUSION: Conclusions: The most promising directions for improving adhesive systems are modifications of the composition and protocols of their use with the aim of deactivating matrix metalloproteinases, improving the structure of the hybrid layer due to the creation of a three-dimensional mesh of collagen fibres with optimal properties, the introduction of antimicrobial agents to slow down the growth of bacterial colonies along the line of the adhesive joint. The available research results of modified adhesive systems are often contradictory, which determines the need to develop standardized test methods to obtain more reliable indicators of their physical, mechanical and biological properties. In some cases, the consequences of non-compliance with the recommendations of the manufacturing companies are a significant deterioration of the characteristics of the hybrid layer, adhesive strength, marginal fit, which, in turn, explains the need for further search for an optimized composition and techniques for applying bonding agents to improve the prognosis of restorative treatment.
Asunto(s)
Adhesivos , Dentina , Humanos , OdontologíaRESUMEN
Introduction: : Dental adhesion is responsible for the chemical processes of dentin-enamel union for a correct choice before its application in restorative treatments; it is important to know properly the generation to which it belongs, its properties, application techniques, etc. All this is to ensure success in the procedures to be performed. Currently, adhesive systems have evolved, and 8 generations are available in the market, each with a better-quality standard than the previous one. Objective: To identify which generation of the adhesive system is the most viable to be applied in direct dental restorative treatments. Materials and methods: We reviewed and compiled 133 articles published from 20 years ago to date. After analyzing them according to their clinical relevance, 88 were excluded, the remaining articles were reanalyzed, of which only those focused on describing the generations of adhesive systems applied in direct restorations were selected, leaving a total of 56 articles, which included clinical case reports. The Google Scholar search engine, SciELO and databases of interest, such as PubMed, Scopus and Medigraphic, were used, three reviewers independently performed the analysis and search of data, and the keywords were used; adhesive systems, generations of adhesive systems, evolution, and direct restorations. Results: : 56 articles were evaluated, according to their relationship with the subject and with the information previously sought, it was determined that the seventh generation of adhesive systems is the most viable to be applied in dental treatments, due to the improvements it presents in its characteristics, and the results with good prognosis mentioned by both dental professionals, as in research. Conclusion: The advancement of technology implies new knowledge; therefore, the effectiveness of adhesive systems has changed significantly. Scientific evidence has shown that seventh-generation adhesives are more effective in direct restorations.
RESUMEN
Purpose: To systematically review in vitro studies that incorporated MMP inhibitors into adhesive systems in terms of the effect on immediate and aged bond strength of dental composite to dentine. Materials and methods: Independently, two reviewers conducted an electronic search in three databases (MEDLINE, EMBASE, and Google Scholar) following the Preferred Reporting Items for Systematic Review and Meta-Analyses Protocols (PRISMA-P), up to 6 March 2022. Results: The search resulted in 894 papers, 33 of which were eligible to be included in the review; of those, 13 fulfilled the meta-analysis eligibility criteria. Nineteen inhibitors were used among the studies, and those included in the meta-analysis were 2%, 0.2% chlorhexidine (CHX), 5 µM GM1489, and 0.5%, 1% benzalkonium chloride (BAC). In the meta-analysis, while above inhibitors showed no adverse effect on bond strength, 0.2% CHX and 5 µM GM1489 caused a significant increase in immediate and 12-months bond strength. All other inhibitors resulted in a significant increase in bond strength at six months of ageing. Conclusions: Incorporation of MMP inhibitors into the adhesive system has no unfavourable effect on immediate bond strength but a favourable effect on longer-term bond strength. Additionally, inhibitors other than CHX could have similar or better effects on bond strength.
RESUMEN
PURPOSE: To evaluate the clinical efficacy at 6 months (6 M) and 12 months (12 M) of 3 adhesive strategies (two-step etch-and-rinse; two-step self-etch; one step self-etch) used in composite resin restorations in primary molars. METHODS: This randomized clinical study involved 101 class II restorations in primary molars of 34 children (4-8 years old), distributed by 3 groups according to the 3 tested adhesive systems: GI- ClearfilTMS3Bond Plus (CSB); GII- ClearfilTMSE Protect Bond (CSEPB); GIII- Prime&Bond®XP (PBXP). Restorations were evaluated according to FDI criteria, immediately after execution, at 6 M and 12 M. All ethical and legal requirements were met. Statistical analysis was performed using IBM®SPSS®v26 and MS Excel® (5% significance level). RESULTS: The aesthetic, biological and most of the functional parameters evaluated remained without significant changes over time. Statistically significant differences were only found regarding the "marginal adaptation" parameter at 12 M, with worsening of scores for the three groups (p < 0.001). Comparing the groups, no significant differences were detected between any of the evaluated parameters (aesthetics properties: p = 0.721; functional properties: p = 0.122). CONCLUSIONS: After a one-year period, the self-etch adhesives tested presented a clinical efficacy similar to the etch-and-rinse adhesive in restoring class II cavities in primary molars. TRIAL REGISTRATION NUMBER: ISRCTN11458186.
Asunto(s)
Recubrimiento Dental Adhesivo , Recubrimientos Dentinarios , Niño , Humanos , Preescolar , Cementos de Resina , Restauración Dental Permanente , Cementos Dentales , Estudios Prospectivos , Resinas Compuestas , Diente MolarRESUMEN
OBJECTIVE: To determine whether smear layer management, via conservative etching protocols, and the hydrophobic-rich content of hybrid layers would affect the fatigue strength of resin-dentin interfaces. METHODS: Bar-shaped dentin beams obtained from sound third molars were wet-polished for 30 s. Dentin was etched with 32 % ortho-phosphoric acid for 3 or 15 s, 10 % meta-phosphoric acid for 15 s or by a prime-and-rinse application using a mild universal adhesive (Scotchbond Universal, 3M ESPE). Self-etch application served as control. Coating was performed with a solvent-free bisGMA-based resin. Composite buildups were made with a nanofilled composite. Resin-dentin beams with twin-bonded interfaces were sectioned and stored in deionized water for 24 h at 37 â before 4-point flexural quasi-static monotonic testing (n = 16). Stress-life fatigue behavior was evaluated under cyclic loading (n = 35) by the staircase method at 4 Hz. The tension side of cyclic-loaded unfractured beams were evaluated under SEM, along with the micro-morphology of etched dentin surfaces. Monotonic data was analyzed by two-way ANOVA followed by the Tukey Test and cyclic-loaded data by Kruskal-Wallis on Ranks (α = 0.05). RESULTS: Etching protocols and higher hydrophobic-rich content produced significantly higher fatigue life distributions (p < 0.05). Dentin demineralization was ranked as OPA 15 s > MPA 15 s > OPA 3 s > P + R > SE. Less aggressive etching and coating reduced crack formation at hybrid layers. SIGNIFICANCE: Current oversimplification trends in resin-dentin bonding constitute a trade-off between hybridization quality and easier adhesive handling. Controlled dentin etching and increasing the hydrophobic-rich content of hybrid layers may be necessary to extend the longevity of mild universal adhesives.
Asunto(s)
Recubrimiento Dental Adhesivo , Recubrimientos Dentinarios , Grabado Ácido Dental/métodos , Recubrimiento Dental Adhesivo/métodos , Cementos Dentales , Dentina , Recubrimientos Dentinarios/química , Ensayo de Materiales , Cementos de Resina/química , Propiedades de Superficie , Resistencia a la TracciónRESUMEN
Since the adhesion of resin composites to calcium silicate-based cement is considered challenging. Therefore, the best adhesion strategy should be indicated. This review aimed to assess the effect of different adhesive systems on the bond strength of resin composite to calcium silicate-based cement through a systematic review and meta-analysis. The subsequent PICOS framework used was: population, calcium silicate-based cement; intervention, use of self-etch adhesive systems; control, use of total-etch adhesive systems; outcome, bond strength; study design, in vitro studies. The literature search was conducted independently by two reviewers up to 18 February 2021. Electronic databases (PubMed, ISI Web of Science, SciELO, Scopus, and Embase) were searched for applicable articles. In vitro manuscripts studying the effect of adhesive systems on the bond strength of calcium silicate-based cement were considered. The meta-analyses were performed using Review Manager Software version 5.3.5 (The Nordic Cochrane Centre, The Cochrane Collaboration, Copenhagen, Denmark). Bond strength comparisons were made considering the type of calcium silicate-based cement (Mineral Trioxide Aggregate (MTA), Biodentine™, or TheraCal LC®). A p-value < 0.05 was considered statistically significant. A total of 7321 studies were retrieved in databases searched. After full-text evaluation, 37 eligible papers were assessed for qualitative analysis, leaving a total of 22 papers for the quantitative analysis. According to the meta-analysis, the bond strength values of resin composite materials to MTA and TheraCal LC® cement were favored when a total-etch adhesive system was used (p ≤ 0.02). On the other hand, the meta-analysis of the bond strength of resin-based materials to Biodentine™ calcium silicate-based cement was similar between both approaches (p = 0.12). The in vitro evidence suggests that the bond strength of resin-based materials to both MTA and TheraCal LC® cement was preferred by using the total-etch adhesive strategy. However, when bonding to Biodentine™, the use of self-etch or total-etch strategies displayed promising results. Given the lack of evidence related to the chemical interaction of self-etch adhesive materials with the bioceramics, if self-etch adhesives are used for bonding resin-based restorations to calcium silicate-based cement, a pretreatment with phosphoric acid could be recommended.
RESUMEN
Self-etch adhesive systems have the advantages of simple operating steps and low technique sensitivity. However, some deficiencies of self-etch adhesive result that the immediate bonding strength between self-etch adhesive and dentine is not so high. Non-thermal atmospheric pressure plasma (NTAPP) can be used for surface modification. Previous studies of our research group have proven that NTAPP can improve bonding durability between dentine and etch-and-rinse adhesive. However, it is still unknown whether NTAPP can improve bonding strength between dentine and self-etch adhesive. The study observed the contact angle on dentine surface, the adhesive permeability and MTBS. The study proved that NTAPP can improve dentine surface wettability, clear up smear layer, and enhanced the self-etch adhesive permeability in dentine bonding interface. In conclusion, NTAPP could improve the bonding strength between dentine and self-etch adhesive systems. The most optimum treating time was 15 s.
Asunto(s)
Recubrimiento Dental Adhesivo , Gases em Plasma , Grabado Ácido Dental/métodos , Argón , Recubrimiento Dental Adhesivo/métodos , Cementos Dentales , Dentina , Recubrimientos Dentinarios , Ensayo de Materiales , Metacrilatos , Cementos de Resina , Propiedades de Superficie , Resistencia a la TracciónRESUMEN
OBJECTIVES: This randomized, prospective, and split-mouth study aimed to evaluate flowable bulk-fill resin composites in class II restorations, comparing it with a conventional layering technique after 4-year follow-up. MATERIALS AND METHODS: Fifty-three subjects received three class II restorations according to the restorative systems: conventional microhybrid composite resin (PA - Peak Universal + Amelogen Plus, Ultradent); flowable bulk-fill and nanoparticulate composite resins (ABF - Adper Single Bond 2 + Filtek Bulk Fill Flow + Filtek Z350XT, 3M/Espe); and flowable bulk-fill and microhybrid composite resins, (XST - XP Bond + SDR + TPH3, Dentsply). The clinical performance and interproximal contacts were evaluated. Statistical analyses were performed using the Kaplan-Meier, equality test of two proportions, Friedman, Wilcoxon, Kruskal-Wallis, Mann-Whitney, and Logistic regression analysis tests (alpha = 0.05). RESULTS: In total, 106 restorations were evaluated at 4 years. Both systems with bulk-fill composites presented higher marginal discoloration than PA. About surface texture, ABF restorative system showed superior bravo scores being statistically similar to XST. Better performance for wear and surface staining was found for XST restorative system. All restorative systems resulted in the decreased interproximal contacts, occurring early for XST. CONCLUSIONS: The restorative systems that used flowable bulk-fill resin composites showed satisfactory clinical performance compared with conventional resin composite after 4 years. All restorative systems had decreased proximal contact after 4 years. CLINICAL RELEVANCE: Initial marginal discoloration was observed in more than 50% of class II restorations performed with restorative systems that used flowable bulk-fill resin composite. All restorative systems had decreased proximal contact strength over time.