Synthesis and Evaluation of a Chitosan-Silica-Based Bone Substitute for Tissue Engineering.

Bone defects have prompted the development of biomaterial-based bone substitutes for restoring the affected tissue completely. Although many biomaterials have been designed and evaluated, the combination of properties required in a biomaterial for bone tissue engineering still poses a challenge. In this study, a chitosan-silica-based biocomposite was synthetized, and its physicochemical characteristics and biocompatibility were characterized, with the aim of exploring the advantages and drawbacks of its use in bone tissue engineering. Dynamic light scattering measurements showed that the mean hydrodynamic size of solid silica particles (Sol-Si) was 482 ± 3 nm. Scanning electron microscopy of the biocomposite showed that Sol-Si were homogenously distributed within the chitosan (CS) matrix. The biocomposite swelled rapidly and was observed to have no cytotoxic effect on the [3T3] cell line within 24 h. Biocompatibility was also analyzed in vivo 14 days post-implant using a murine experimental model (Wistar rats). The biocomposite was implanted in the medullary compartment of both tibiae (n = 12). Histologically, no acute inflammatory infiltrate or multinucleated giant cells associated to the biocomposite were observed, indicating good biocompatibility. At the tissue-biocomposite interface, there was new formation of woven bone tissue in close contact with the biocomposite surface (osseointegration). The new bone formation may be attributed to the action of silica. Free silica particles originating from the biocomposite were observed at the tissue-biocomposite interface. According to our results, the biocomposite may act as a template for cellular interactions and extracellular matrix formation, providing a structural support for new bone tissue formation. The CS/Sol-Si biocomposite may act as a Si reservoir, promoting new bone formation. A scaffold with these properties is essential for cell differentiation and filling a bone defect.

Recent Advances in Synthetic and Natural Biomaterials-Based Therapy for Bone Defects.

Synthetic and natural biomaterials are a promising alternative for the treatment of critical-sized bone defects. Several parameters such as their porosity, surface, and mechanical properties are extensively pointed out as key points to recapitulate the bone microenvironment. Many biomaterials with this pursuit are employed to provide a matrix, which can supply the specific environment and architecture for an adequate bone growth. Nevertheless, some queries remain unanswered. This review discusses the recent advances achieved by some synthetic and natural biomaterials to mimic the native structure of bone and the manufacturing technology applied to obtain biomaterial candidates. The focus of this review is placed in the recent advances in the development of biomaterial-based therapy for bone defects in different types of bone. In this context, this review gives an overview of the potentialities of synthetic and natural biomaterials: polyurethanes, polyesters, hyaluronic acid, collagen, titanium, and silica as successful candidates for the treatment of bone defects.

Baicalein-modified hydroxyapatite nanoparticles and coatings with antibacterial and antioxidant properties.

Aseptic loosening and bacterial infections are the two main causes of failure for metallic implants used for joint replacement. A coating that is both bioactive and possesses antimicrobial properties may address such shortcomings and improve the performance of the implant. We have sought to study the properties of combining hydroxyapatite-based nanoparticles or coatings with baicalein, a plant-extracted molecule with both antibacterial and antioxidant properties. (B-type) carbonated hydroxyapatite nanoparticles prepared by a chemical wet method could subsequently adsorbed by soaking in a baicalein solution. The amount of adsorbed baicalein was determined to be 63 mg.g-1 by thermogravimetric measurements. In a second approach, baicalein was adsorbed on a biomimetic calcium-deficient hydroxyapatite planar coating (12 µm thick) deposited on Ti6Al4V alloy from an aqueous solution of calcium, phosphate, sodium and magnesium salts. Soaking of the hydroxyapatite coated on titanium alloy in a baicalein solution induced partial dissolution/remodeling of the upper surface of the coating. However, the observed remodeling of the surface was much more pronounced in the presence of a baicalein solution, compared to pure water. The presence of adsorbed baicalein on the HAp layer, although it could not be precisely quantified, was assessed by XPS and fluorescence analysis. Planar coatings exhibited significant antibacterial properties against Staphylococcus epidermidis. Baicalein-modified nanoparticles exhibited significant antioxidant properties. These results illustrate the potential of hydroxyapatite used as a carrier for natural biologically-active molecules and also discuss the challenges associated with their applications as antibacterial agents.

Stimuli-Responsive Materials for Tissue Engineering and Drug Delivery.

Smart or stimuli-responsive materials are an emerging class of materials used for tissue engineering and drug delivery. A variety of stimuli (including temperature, pH, redox-state, light, and magnet fields) are being investigated for their potential to change a material's properties, interactions, structure, and/or dimensions. The specificity of stimuli response, and ability to respond to endogenous cues inherently present in living systems provide possibilities to develop novel tissue engineering and drug delivery strategies (for example materials composed of stimuli responsive polymers that self-assemble or undergo phase transitions or morphology transformations). Herein, smart materials as controlled drug release vehicles for tissue engineering are described, highlighting their potential for the delivery of precise quantities of drugs at specific locations and times promoting the controlled repair or remodeling of tissues.

Dodecenylsuccinic anhydride modified collagen hydrogels loaded with simvastatin as skin wound dressings.

Skin wound healing presents a unique challenge because of its complex healing process. Herein, we developed a hydrophobic wound dressing to incorporate simvastatin, which has potential application in the treatment of ulcers and prevention of wound infection. For that matter, collagen hydrogels were grafted with dodecenylsuccinic anhydride (DDSA). The chemical modification was confirmed by FTIR and solid state 13 C-NMR spectroscopies while the ultrastructure was observed by scanning electron microscope (SEM) images. In contact angle measurements, a higher water droplet angle in DDSA-collagen gels was observed. This was consistent with the swelling assay, in which water absorption was 5.2 g/g for collagen and 1.9 g/g for DDSA-collagen. Additionally, viability and adhesion studies were performed. Cell adhesion decreased ~11% in DDSA-collagen and the number of viable cells showed a tendency to decrease as DDSA concentration increased but it was only significantly lower above concentrations of 12%. Modified gels were loaded with simvastatin showing higher adsorption capacity and lower release. Lastly, the antimicrobial and anti-inflammatory activity of DDSA-collagen materials were assessed. DDSA-collagen hydrogels, either unloaded or loaded with simvastatin showed sustained antimicrobial activity against Pseudomonas aeruginosa and Staphylococcus aureus for 72 hr probably due to the hydrophobic interaction of DDSA chains with bacterial cell walls. The antimicrobial activity was stronger against S. aureus. Collagen hydrogels also presented a prolonged antibacterial activity when they were loaded with simvastatin, confirming the antimicrobial properties of statins. Finally, it was observed that these materials can stimulate resident macrophages and promote an M2 profile which is desirable in wound healing processes.