Prolonged application time effects on universal adhesives in non-carious cervical lesions: An 18-month split mouth randomized clinical trial.

OBJECTIVE: This double-blind, split mouth randomized clinical trial aimed to assess the clinical performance of Clearfil Universal Bond Quick (CBUq) universal adhesive under different application times (no waiting and waiting) compared to Clearfil SE Bond adhesive in non-carious cervical lesions (NCCLs) over 18 months. METHODS: One hundred and eighty-three restorations were distributed randomly into three groups based on the adhesive system and waiting time: CUBq without waiting time (CUBq-NW), CUBq with a 20 s waiting time (CUBq-W), and CSE with a 20 s waiting time. After placement, restorations were evaluated after 18 months using the International Dental Federation (FDI) and United States Public Health Service (USPHS) criteria. Statistical analyses involved Friedman repeated measures analysis of variance and Wilcoxon tests, with a significance level set at 5 %. RESULTS: Over the 18-month period, no restorations were lost across the tested groups. Marginal adaptation evaluation indicated minor discrepancies in 21 restorations (8 CUBq-NW, 6 CUBq-W, and 7 CSE). There were no significant differences observed among the three groups following the 18-month clinical assessment (p > 0.05). Only two restorations showed marginal discoloration after 18 months (1 CUBq-NW and 1 CSE). CONCLUSIONS: The application of Clearfil Universal Bond Quick using either the "waiting" or "no-waiting" technique exhibited excellent clinical results in NCCLs during the 18-month follow-up period, demonstrating comparable performance to Clearfil SE Bond in all assessed outcomes. CLINICAL SIGNIFICANCE: The findings suggest that the new universal adhesive applied using the no-waiting technique demonstrates promising clinical performance when compared to conventional application methods. TRIAL REGISTRATION: ClinicalTrials.gov identifer RBR-69p7mpr.

Effect of the Viscosity and Application Time of Different Phosphoric Acids on the Bond Strength and Nanoleakage of Fiber Posts to Root Dentin.

PURPOSE: To evaluate the effect of application time and viscosity of meta-phosphoric acid (MPA) and ortho-phosphoric acid (OPA) on the push-out resin-dentin bond strength (PBS) and nanoleakage (NL) at the adhesive-root dentin interface. METHODS AND MATERIALS: Ninety-six roots of premolars were endodontically prepared and randomly assigned into groups according to the (i) acid (OPA and MPA), (ii) viscosity (gel and liquid), and (iii) application time (7 and 15 seconds). Fiber posts were cemented to the roots, which were then transversally sectioned into serial slices. The slices (cervical, medium, and apical) were subjected to PBS or NL. Analysis of the dentin etching pattern was performed using scanning electron microscopy (SEM). The PBS (MPa) and NL (%) data were subjected to three-way repeated-measures analysis of variance (ANOVA) and Tukey's test (α=0.05). RESULTS: The cross-product interaction was significant for both PBS and NL (p<0.001). No significant difference in the PBS was observed with the use of OPA compared to MPA (p>0.05). Higher PBS values were observed in the groups etched for 15 seconds compared to 7 seconds, regardless of the acid, viscosity, or root third (p<0.05). Lower NL was observed for MPA etching when compared to OPA etching (p<0.05), and these values were not affected by increasing the application time or acid viscosity (p>0.05). A more pronounced etching pattern was observed with OPA than MPA regardless of the acid viscosity. CONCLUSION: The use of 40% meta-phosphoric acid promoted adequate bond strength without increasing dentin demineralization or void spaces in the hybrid layer.

Nanofiller Particles and Bonding Durability, Water Sorption, and Solubility of Universal Adhesives.

The aim of this study was to evaluate the influence of nanofiller particles in simplified universal adhesive on the long-term microtensile bond strength and silver nitrate up-take, as well as water sorption and solubility. Commercial adhesives Ambar Universal (FGM) in nanofilled-containing version (filled) and same lot without fillers (unfilled) were donated and applied by means of etch-and-rinse strategy. Microtensile bond strength was surveyed after 24-hours or 1-year water storage. Silver nitrate uptake was assayed using scanning electron microscopy (SEM). Water sorption and solubility experiments were performed based on ISO 4049:2009. Statistical analysis was performed using two-way ANOVA and Tukey test (p<0.05). The bond strength of both the adhesives were statistically similar at 24 hours (p>0.05), but the filled group attained significant bond strength reduction after aging when compared to initial bond strength (p<0.001). Conversely, unfilled adhesive presented stable adhesion after 1-year storage (p=0.262). Silver nitrate uptake was similar for both adhesives, with little silver impregnation at the hybrid and adhesive layers. Water sorption was higher with filled adhesive compared to the unfilled one (p=0.01). Conversely, solubility was higher in unfilled in comparison to filled one (p=0.008). The presence of nanofillers in universal adhesive achieves higher water sorption and dentin bond degradation, which did not occur in the unfilled adhesive.