Novel Fabrication Processing of Porous Al2O3/CaAl12O19 Membrane by Combining Emulsion, Cement Curing and Tape-Casting Methods.

This paper presented an innovative method for fabrication of a porous Al2O3/CaAl12O19 ceramic membrane by combining emulsion method, cement curing and tape-casting technologies. The ceramic membrane featured a smooth surface and a porous internal structure. By adjusting the oil-water volume ratio from 1:1 to 4:1, the porosity of the samples increases from 45.6 to 67.3%, density decreases from 2.07 to 1.32 g/cm3 and bending strength decreases from 64.3 ± 1.2 to 31.7 ± 0.6 MPa. More significantly, the membranes showed great gas permeability (1.2 × 107-2.3 × 107 Lm-2 h-1 bar-1), opening up a wide range of applications in the field of gas filtration processes.

Simple Fabrication of Concrete with Remarkable Self-Cleaning Ability, Robust Superhydrophobicity, Tailored Porosity, and Highly Thermal and Sound Insulation.

Self-cleaning materials have attracted immense commercial and academic interests in recent years. A major challenge is the scalable and cost-effective fabrication of three-dimensional bulk materials with remarkable self-cleaning and a desirable combination of tailored porosity, robust superhydrophobicity, excellent mechanical strength, heat insulation, and sound absorption ability. Here, self-cleaning concrete was achieved in one step through the combination of the liquid template pore formation and in situ bulk hydrophobic modification. The concrete exhibited superhydrophobicity with a high water contact angle of 166° both on the surface and inside of the sample, which qualified the sample with remarkable stain repellency and long-term stability. The water contact angle remained unchanged under continuous mechanical grinding and harsh environments, such as high temperature (450 °C in air and 650 °C in Ar) and chemical erosion. The concrete with a controllable porosity from 56.3 to 77.4% and homogeneous small pore size (∼15 µm) exhibited high compressive strength and low thermal conductivity. Furthermore, high sound absorption capacity (97%, 500 Hz) at a vibration frequency from 400 to 600 Hz was realized. With these excellent performances and characteristics and easy scalable fabrication, the concrete prepared in this work possessed a wide application prospect.

Multifunctional Thin-Film Nanofiltration Membrane Incorporated with Reduced Graphene Oxide@TiO2@Ag Nanocomposites for High Desalination Performance, Dye Retention, and Antibacterial Properties.

High desalination performance, dye retention, and antibacterial properties were achieved with a multifunctional thin-film nanocomposite (MTFN) membrane, fabricated by the incorporation of a novel nanocomposite structure of reduced graphene oxide@TiO2@Ag (rGO@TiO2@Ag) into the polyamide active layer. The specific characteristics of the graphene-based nanocomposite, synthesized by the microwave-assisted irradiation process, favored water channelization and provided superhydrophilicity and antibacterial properties to the MTFN membranes. In comparison with the conventional methods, such as multistep chemical process using strong agents for reduction and long-term energy-consuming hydrothermal process, microwave irradiation facilitated a green, fast, and cost-effective route for the fabrication of GO-based nanocomposites for multifunctional applications. Interfacial polymerization was performed on a polyethersulfone/Si3N4 robust hollow fiber substrate using m-phenylenediamine aqueous solution and 1,3,5-benzenetricarbonyltrichloride organic solution. The structural and chemical characteristics of the synthesized nanocomposites and the MTFN membranes were thoroughly studied by a series of characterization analyses (transmission electron microscopy, field emission scanning electron microscopy, X-ray diffraction, Fourier transform infrared, energy-dispersive X-ray spectroscopy, X-ray photoelectron spectroscopy, and atomic force microscopy). The physicochemical properties and the nanofiltration performance of the MTFN membranes were investigated after the incorporation of rGO@TiO2@Ag at various concentrations. The water contact angles confirmed the superb surface hydrophilicity of the MTFN membranes. High permeability (52 L·m-2·h-1), desalination (96% for 1 g/L Na2SO4 feed solution), and dye retention (98% for 0.5 g/L rose bengal feed solution) were recorded for MTFN enriched with 0.2 wt % rGO@TiO2@Ag. A 90% reduction in the number of viable bacteria ( Escherichia coli), after 3 h of contact with MTFN membranes, confirmed the superior antibacterial activity of the produced membranes.

Preparation of a Porous, Sintered and Reaction-Bonded Si3N4 (SRBSN) Planar Membrane for Filtration of an Oil-in-Water Emulsion with High Flux Performance.

A porous, sintered, and reaction-bonded Si3N4 (SRBSN) planar membrane was prepared by phase-inversion tape-casting, nitridation (at 1350 °C), and sintering (at 1650 °C) of silicon slurry. The membrane was comprised of uniform rod-like β-Si3N4 crystals with a large length/diameter ratio and had high porosity and bending strength. The prepared membrane features a typical asymmetric structure with a skin layer, a sponge layer, and finger-like voids and an average pore size of 0.61 μm. A high permeation flux of 367 L m−2 h−1 and an oil rejection of 88.6% were recorded in oil-in-water emulsion separation experiments. These results suggest that SRBSN membranes have excellent potential for the treatment of oily wastewater.

Single-Phase White Light-Emitting Ca x Ba(9-x)Lu2Si6O24:Eu2+/Mn2+ Phosphors.

Single-phase white light-emitting Ca x Ba(9-x)Lu2Si6O24:Eu2+/Mn2+ codoped phosphors were successfully synthesized, and their photoluminescence properties were experimentally determined. The analysis of the experimental results suggests that the partial substitution of Ba2+ ions by smaller Ca2+ ions alters the distribution of the Eu2+ luminescence center among the three available Ba2+ sites in the host lattice, which enables the emission to be efficiently tuned from blue to blue-green-yellow region. The incorporation of Mn2+ ions resulted in a red light emission at around 618 nm, through energy transfer from Eu2+ to Mn2+ ions via dipole-dipole interactions. The incorporation of Ca2+ and Mn2+ ions also resulted in improved thermal stability. The results qualify the produced Ca x Ba(9-x)Lu2Si6O24:Eu2+/Mn2+ composition as a potential ultraviolet-convertible white light-emitting phosphor.