Synthesis and characterization of chitosan/polyacrylamide hydrogel grafted poly(N-methylaniline) for methyl red removal.

Chitosan/polyacrylamide hydrogel grafted poly(N-methylaniline) (CS/PACM-gr-PNMA) was good synthesized by chemical oxidative radical polymerization using potassium persulphate (KPS). The obtained polymer samples are characterized using IR and Uv-visible spectroscopy. Both surface properties and thermal stability were studied using XRD, SEM, BET and TGA techniques respectively. The characterized polymeric samples were used as a new sorbent for methyl red (MR). MR as an example of azo-dyes presence as pollutants in industrial wastewater which cause physiological damages was chosen to uptake. The influence of contact time, adsorbent dose, and temperature on the efficiency of CS/PACM-gr-PNMA towards the removal of MR was investigated. The efficacy was equal to 98% through 120 min at room temperature. The obtained data show that, ∆H = -21.478 kJ mol-1, so adsorption process is physically spontaneous and follow Freundlich isotherm. The sorption process of MR on the surface of CS/PACM-gr-PNMA is proceed via the Lagergren pseudo-second order reaction. This confirms the removal mechanism by both chemical and physical adsorption of MR with both unpaired and π electrons present in polymer structure on NH, NH2, and benzene or quinoid units respectively. In addition, it can explain the chemical adsorption type which occurs through sharing between the used adsorbent materials and the dissolved materials beside the physical adsorption.

Effect of Cu, Ni and Pb doping on the photo-electrochemical activity of ZnO thin films.

In the present study, the effects of metallic doping on the photoelectron\chemical properties of zinc oxide thin films have been studied. All films have been deposited using the spray pyrolysis technique at a constant doping level of 3 wt% whereby Cu, Ni, and Pb were used as dopants. The structure of all films was studied by X-ray diffraction which showed the grain size of all doped films to be 50 nm. The energy band gap of all films was estimated using optical transmission spectroscopy. The Ni, Cu, and Pb-doped ZnO photoelectrodes were applied for the photoelectrochemical (PEC) H2 generation from H2O. Pb doping leads to the highest photocurrent of the ZnO photoelectrodes. The current density-potential characteristics were measured under white light and monochromatic illumination. The stability of the electrode was quantified as a function of the number of H2 production runs and exposure time. Finally, the incident photon-to-current conversion efficiency, IPCE, and applied bias photon-to-current efficiency, ABPE, were calculated. The optimum IPCE at 390 nm was ∼30% whereas the ABPE was 0.636 at 0.5 V.