In vivosoft tissue regenerative potential of flax seed mucilage self-assembled collagen aerogels.

The present study demonstrates thein vivosoft tissue regenerative potential of flax seed mucilage (FSM) reinforced collagen aerogels in Wistar rats. The physiochemical, mechanical, and thermal properties were significantly improved upon the incorporation of flax mucilage into collagen when compared to the native collagen scaffold. In addition, the functional group of flax mucilage notably contributed to a better anti-oxidative potential than the control collagen. The flax mucilage-reinforced collagen at 4 mg ml-1concentration showed a 2-fold increase in porosity compared to native collagen. The tensile strength of native collagen, 2 mg ml-1, and 4 mg ml-1FSM reinforced collagen was 5.22 MPa, 9.76 MPa, and 11.16 MPa, respectively, which indicated that 2 mg ml-1and 4 mg ml-1FSM showed an 87% and 113% percentage increase respectively in tensile strength compared to the native collagen control. FSM-reinforced biomatrix showed 97% wound closure on day 15 post-wounding, indicating faster healing than controls, where complete healing occurred only on day 21. The mechanical properties of skin treated with FSM-reinforced collagen scaffold post-healing were considerably better than native collagen. The histological and immunohistochemistry analysis also showed complete restoration of wounded tissue like intact normal skin. The findings paved the way for the development of collagen-polysaccharide mucilage wound dressing materials and their further application in skin tissue engineering.

Lanthanum Oxide Nanoparticles Reinforced Collagen ƙ-Carrageenan Hydroxyapatite Biocomposite as Angio-Osteogenic Biomaterial for In Vivo Osseointegration and Bone Repair.

A composite biomatrix fabricated with collagen, ƙ-carrageenan, hydroxyapatite reinforced with lanthanum oxide nanoparticles is explored as proangiogenic and osteogenic bone tissue repair biomaterial. The biomatrix shows increased physical and biological stability as observed from proteolytic degradation and thermal stability studies. The addition of lanthanum oxide nanoparticles facilitates good osseointegration coupled with simultaneous activation of proangiogenic properties to act as a bone mimicking material. The minimal level of reactive oxygen species and superior cytocompatibility help the as-synthesized biomatrix in achieving capillary migration into the bone micro environment. The composite biomatrix upregulates the expression of VEGF, VEGF-R2 genes in endothelial cells and osteopontin, osteocalcin in osteoblasts cells, respectively. The in vivo hard tissue repair experiment conducted in a rat model shows complete healing of the bone defect by eight weeks with the application of collagen-ƙ-carrageenan-hydroxyapatite-lanthanum oxide nanoparticle biomaterial when compared to the biomaterial made out of individual constituents alone. The biomaterial matrix gets biointegrated into the bone tissue and exerts its therapeutic value in bringing a faster osseo repair process. The study shows the feasibility of using rare-earth metal nanoparticles in combination with protein-polysaccharide biopolymers for bone regeneration.