Hydrothermal assisted synthesis of hierarchical SnO2 micro flowers with CdO nanoparticles based membrane for energy storage applications.

Hierarchical nanostructures with appropriate morphology and surface functionalities are highly desired to achieve an optimized electrochemical property for active electrode materials. This work renders the facile hydrothermal synthesis of CdO, SnO2, and CdO-SnO2 nanocomposite, and their capacitive performance was tested. The formation of the pure samples and their composite was committed by low-temperature Raman spectroscopy and x-ray diffraction studies which revealed the tetragonal and cubic structures of CdO and SnO2 powder samples with good crystallinity and purity. The morphological postmortem reveals the formation of nanoparticles morphology of CdO with a highly smooth surface appearance. Besides, the SnO2 illustrates the morphology of the micro flowers composed of ultrathin nanosheets. More specifically, the electrochemical properties indicate the pseudocapacitive charge storage mechanism based on cyclic voltammetry and chronopotentiometry analysis. The CdO-SnO2 composite electrode displayed a higher capacitance due to additional pores/space offered for active sites and continuously allowed electrolyte ions to interact with the inner/outer surface of the electrode. These exciting findings led us to design and fabricate battery hybrid supercapacitors (BHSC) from CdO-SnO2, and activated carbon (AC), referred to as CdO-SnO2//AC BHSC, attains a high power delivery (5717 W/kg), and a maximum energy density of 42 Wh/kg at low discharge rate. Noteworthy, a stable cycling performance was obtained with only 91.3% retention after 8000 cycling at a large discharge current of 10 A/g, denoting the magnificent durability of the active electrode material.

SnO2 Quantum Dots Distributed along V2O5 Nanobelts for Utilization as a High-Capacity Storage Hybrid Material in Li-Ion Batteries.

In this study, the facile synthesis of SnO2 quantum dot (QD)-garnished V2O5 nanobelts exhibiting significantly enhanced reversible capacity and outstanding cyclic stability for Li+ storage was achieved. Electrochemical impedance analysis revealed strong charge transfer kinetics related to that of V2O5 nanobelts. The SnO2 QD-garnished V2O5 nanobelts exhibited the highest discharge capacity of ca. 760 mAhg-1 at a density of 441 mAg-1 between the voltage ranges of 0.0 to 3.0 V, while the pristine V2O5 nanobelts samples recorded a discharge capacity of ca. 403 mAhg-1. The high capacity of QD-garnished nanobelts was achieved as an outcome of their huge surface area of 50.49 m2g-1 and improved electronic conductivity. Therefore, the as-presented SnO2 QD-garnished V2O5 nanobelts synthesis strategy could produce an ideal material for application in high-performance Li-ion batteries.