Fibrin-Based Hydrogels with Reactive Amphiphilic Copolymers for Mechanical Adjustments Allow for Capillary Formation in 2D and 3D Environments.

This study focuses on enhancing controllable fibrin-based hydrogels for tissue engineering, addressing existing weaknesses. By integrating a novel copolymer, we improved the foundation for cell-based angiogenesis with adaptable structural features. Tissue engineering often faces challenges like waste disposal and nutrient supply beyond the 200 µm diffusion limit. Angiogenesis breaks through this limitation, allowing the construction of larger constructs. Our innovative scaffold combination significantly boosts angiogenesis, resulting in longer branches and more capillary network junctions. The copolymer attached to fibrin fibers enables precise adjustment of hydrogel mechanical dynamic properties for specific applications. Our material proves effective for angiogenesis, even under suppression factors like suramin. In our study, we prepared fibrin-based hydrogels with and without the copolymer PVP12400-co-GMA10mol%. Using a co-culture system of human umbilical vein endothelial cells (HUVEC) and mesenchymal stem cells (MSC), we analyzed angiogenetic behavior on and within the modified hydrogels. Capillary-like structures were reproducibly formed on different surfaces, demonstrating the general feasibility of three-dimensional endothelial cell networks in fibrin-based hydrogels. This highlights the biomaterial's suitability for in vitro pre-vascularization of biohybrid implants.

Enhancing Adhesion of Fibrin-Based Hydrogel to Polythioether Polymer Surfaces.

The development of stable (bio)hybrid constructs composed of scaffolds and (bio)matrices is a major challenge in the field of tissue engineering. In the present work, the adhesion of fibrin-based hydrogels to the surface of polythioether-based polymers relevant to the 3D printing of polymer scaffolds produced by thiol-ene click chemistry was investigated. Adhesion properties were characterized by single-lap tensile shear testing. Both the sample preparation and the test method were optimized for the analysis of fibrin gel bonding to the polythioether surface. Our experimental results show that even without further modification, an adhesion between the fibrin hydrogel and polythioether is substantial, with an adhesion strength of 4.9 ± 1.0 kPa. To further improve the bonding, linear functional poly(N-vinylpyrrolidone-co-glycidyl methacrylate) (PVP-co-GMA) copolymers were used that are known for covalently binding to fibrin. The maximum adhesion strength in our study was found to be 18.4 ± 3.4 kPa. The pure PVP-co-GMA copolymers also demonstrate covalent binding to the thiol-ene-based polymers with a maximum adhesion strength of 32.2 ± 2.7 kPa. Therefore, compared to pure fibrin, the presence of copolymer coating both on the polythioether surface and in the fibrin gel led to a significant increase of the adhesion strength by a factor of 1.6.

From In Vitro to Perioperative Vascular Tissue Engineering: Shortening Production Time by Traceable Textile-Reinforcement.

BACKGROUND: The production of tissue-engineered vascular graft (TEVG) usually involves a prolonged bioreactor cultivation period of up to several weeks to achieve maturation of extracellular matrix and sufficient mechanical strength. Therefore, we aimed to substantially shorten this conditioning time by combining a TEVG textile scaffold with a recently developed copolymer reinforced fibrin gel as a cell carrier. We further implemented our grafts with magnetic resonance imaging (MRI) contrast agents to allow the in-vitro monitoring of the TEVG's remodeling process. METHODS: Biodegradable polylactic-co-glycolic acid (PLGA) was electrospun onto a non-degradable polyvinylidene fluoride scaffold and molded along with copolymer-reinforced fibrin hydrogel and human arterial cells. Mechanical tests on the TEVGs were performed both instantly after molding and 4 days of bioreactor conditioning. The non-invasive in vitro monitoring of the PLGA degradation and the novel imaging of fluorinated thermoplastic polyurethane (19F-TPU) were performed using 7T MRI. RESULTS: After 4 days of close loop bioreactor conditioning, 617 ± 85 mmHg of burst pressure was achieved, and advanced maturation of extracellular matrix (ECM) was observed by immunohistology, especially in regards to collagen and smooth muscle actin. The suture retention strength (2.24 ± 0.3 N) and axial tensile strength (2.45 ± 0.58 MPa) of the TEVGs achieved higher values than the native arteries used as control. The contrast agents labeling of the TEVGs allowed the monitorability of the PLGA degradation and enabled the visibility of the non-degradable textile component. CONCLUSION: Here, we present a concept for a novel textile-reinforced TEVG, which is successfully produced in 4 days of bioreactor conditioning, characterized by increased ECM maturation and sufficient mechanical strength. Additionally, the combination of our approach with non-invasive imaging provides further insights into TEVG's clinical application.