Influences of luting cement shade on the color of various translucent monolithic zirconia and lithium disilicate ceramics for veneer restorations.

PURPOSE: The purpose of this study was to assess the effect of resin cement shade on the color of different novel ultratranslucent monolithic zirconia and lithium disilicate veneer materials. MATERIALS AND METHODS: For a total of 40 specimens, flat cylindrical discs with a 9-mm diameter and 0.5-mm thickness were created using CAD/CAM technology. The specimens were divided into five groups according to their material (n = 8) (e.max, Prettau, Aidite, Shofu and Dima) using A1 shade. Resin discs with the same diameter and shade as the specimens served as tooth-colored substructures. Three shades (neutral, light and warm) of resin cement try-in pastes (Variolink Esthetic LC) were used as the luting cement material. The color of each material group was measured before and after cementation using the three cement shades, and the CIE L*a*b* coordinates were obtained with a spectrophotometer. Values for the translucency parameter (TP) and color change delta E (E) before (baseline) and after cementation of each specimen were determined. To compare differences among the material groups within each shade of cement and among various shades of cement within each material, the data were analyzed using one-way ANOVA and post hoc testing. RESULTS: Color coordinates L*, a* and b* significantly changed after the application of try-in pastes relative to baseline values, with a noticeable decrease in lightness (L*) (P < .05). A significant color change (ΔE) was observed in all tested materials after cementation, with ΔE values exceeding 3.3 (P < .05). Although TP changed after cementation for most materials tested, these changes were not statistically significant (P > .05). Shofu and Dima ceramics showed the lowest TP values, while Aidite and Prettau showed the highest TP values. For e.max, translucency decreased after cementation with neutral and warm shades, and it significantly increased after cementation with a light shade. CONCLUSION: The shade of cement significantly altered the final color of the ceramic veneer material to a level above the threshold at which the clinical perception of color change occurred (> 3.3). The TP was not influenced by the cement shade. The translucency levels of the novel ultratranslucent multilayer monolithic zirconia ceramics Aidite and Prettau were higher than that of the lithium disilicate e.max material.

Evaluation of the Effect of Electronic Cigarette Devices/Vape on the Color of Dental Ceramics: An In Vitro Investigation.

The use of vaping or electronic cigarette devices (ECDs) has recently increased as an alternative to conventional tobacco smoking products. By recording the CIELAB coordinates (L*a*b*) and computing the total color difference (ΔE) values using a spectrophotometer, the effect of ECDs on contemporary aesthetic dental ceramics was investigated in this in-vitro study. A total of seventy-five (N = 75) specimens from five different (n = 15) dental ceramic materials (Pressable ceramics (PEmax); Pressed and layered ceramics (LEmax); Layered zirconia (LZr); Monolithic zirconia (MZr) and Porcelain fused to metal (PFM)) were prepared and exposed to aerosols produced by the ECDs. The color assessment was performed using a spectrophotometer at six time intervals (0 = baseline; 250-puff exposures; 500-puff exposures; 750-puff exposures; 1000-puff exposures; 1250-puff exposures; and 1500-puff exposures). By recording L*a*b* and computing total color difference (ΔE) values, the data were processed. A one-way ANOVA and Tukey procedure for pairwise comparisons were used to assess color differences between tested ceramics (p < 0.05). All test materials demonstrated significant color differences (ΔE) after exposure to vaping (p < 0.05). The LZr group displayed noticeably high ΔE values at all the distinct puff exposure intervals, with the highest ΔE value of (13.67) after 1500 puffs. The lowest (ΔE) values were observed in the PFM group after 250 and 500 puffs (0.85 and 0.97, respectively). With the exception of the group PEmax (p = 0.999), all groups produced readings of "ΔE" that indicated significant differences (p < 0.05) at various degrees of puff exposures. ECDs can noticeably alter the color of the dental ceramics affecting the esthetics of the patients. All the materials tested demonstrated significant color changes (ΔE > 3.33) above the clinically acceptable threshold, except for the PFM and PEmax group (ΔE < 3.33) which showed color stability after exposure to the ECDs.

Push-Out Bond Strength of Endodontic Posts Cemented to Extracted Teeth: An In-Vitro Evaluation.

(1) Background: An ideal bond strength between endodontic posts and root canal dentin is essential for optimal retention and good prognosis. This study aimed to evaluate the push-out bond strength (PBS) of prefabricated fiber and metal posts, luted with resin cement to natural dentin. (2) Methods: Extracted premolars with similar root dimensions were assigned into two groups of 30 each for the metal and fiber posts. Teeth were mounted in acrylic blocks exposing 2 mm of the coronal root. Teeth were subjected to endodontic treatment and post-space preparations. Two groups were further subdivided into three sub-groups (n = 10) according to the size of the posts (# 4, 5 and 6). Posts were cemented with resin cement. Specimens were sectioned into 4 mm slices and subjected to the PBS test. (3) Results: The mean PBS was similar for the metal and fiber posts bonded with resin cement, showing a statistically significant result. An increase in post size increased the bond strength initially, but a further increase in size did not show any marked difference. A total of 71.66% of tested specimens failed with the adhesive failure mode. (4) Conclusions: Metal posts showed slightly higher retention compared to the fiber posts, although the p-value was similar for both types. An increase in the size of posts showed increased retention. The most common mode of failure was adhesive failure between cement and dentin.