Effect of surface treatment and manufacturing process on the shear bond strength of veneering composite resin to polyetherketoneketone (PEKK) and polyetheretherketone (PEEK).

STATEMENT OF PROBLEM: Polyaryletherketones (PAEKs) are high-performance polymer materials in which polyetheretherketone (PEEK) and polyetherketoneketone (PEKK) are the most used. Although mechanical and shear bonding strength tests have been performed on the 2 materials, studies on the influence of processing on bonding are scarce. PURPOSE: The purpose of this in vitro study was to determine the influence of the surface treatment and the manufacturing process on the shear bond strength of veneering composite resin to PEKK and PEEK. MATERIAL AND METHODS: Thirty pressed PEKK, 30 milled PEKK, and 30 milled PEEK specimens were distributed in 6 groups (n=13) as per the manufacturing process and treatment surface. The specimens were either treated with airborne-particle abrasion with 110-µm aluminum oxide, or no surface treatment was applied. Moreover, the PEKK specimens were grouped regarding their manufacturing process, as either milled or heat-pressed. The specimens were all bonded by using a methyl methacrylate-based adhesive (visio.link), and composite resin (Gradia Revolution 2) was bonded to the specimens. An Instron universal machine was used to calculate the shear bond strength between the PEEK or PEKK and the composite resin. Two specimens from each group had their topography modification assessed with a scanning electron microscope. Statistical analysis was performed by using a 3-way ANOVA for multiple comparisons (α=0.05) RESULTS: The groups that were surface treated with 110-µm aluminum oxide (Al2O3) before bonding showed significantly higher shear bond strength (P=.001) than the other groups. However, no statistically significant difference was observed among the groups, regardless of the manufacturing process (milled or heat-pressed) (P=.607). CONCLUSIONS: PEEK and PEKK surfaces treated with 110-µm aluminum oxide airborne-particle abrasion displayed better shear bond strength to composite resin. The manufacturing process (milled or heat-pressed) did not significantly affect the bond strength of PEKK when subjected to the same bonding process.

Biomimetic coatings enhance tribocorrosion behavior and cell responses of commercially pure titanium surfaces.

Biofunctionalized surfaces for implants are currently receiving much attention in the health care sector. Our aims were (1) to create bioactive Ti-coatings doped with Ca, P, Si, and Ag produced by microarc oxidation (MAO) to improve the surface properties of biomedical implants, (2) to investigate the TiO2 layer stability under wear and corrosion, and (3) to evaluate human mesenchymal stem cells (hMSCs) responses cultured on the modified surfaces. Tribocorrosion and cell experiments were performed following the MAO treatment. Samples were divided as a function of different Ca/P concentrations and treatment duration. Higher Ca concentration produced larger porous and harder coatings compared to the untreated group (p < 0.001), due to the presence of rutile structure. Free potentials experiments showed lower drops (-0.6 V) and higher coating lifetime during sliding for higher Ca concentration, whereas lower concentrations presented similar drops (-0.8 V) compared to an untreated group wherein the drop occurred immediately after the sliding started. MAO-treated surfaces improved the matrix formation and osteogenic gene expression levels of hMSCs. Higher Ca/P ratios and the addition of Ag nanoparticles into the oxide layer presented better surface properties, tribocorrosive behavior, and cell responses. MAO is a promising technique to enhance the biological, chemical, and mechanical properties of dental implant surfaces.

Tribocorrosion behavior of biofunctional titanium oxide films produced by micro-arc oxidation: Synergism and mechanisms.

Dental implants, inserted into the oral cavity, are subjected to a synergistic interaction of wear and corrosion (tribocorrosion), which may lead to implant failures. The objective of this study was to investigate the tribocorrosion behavior of Ti oxide films produced by micro-arc oxidation (MAO) under oral environment simulation. MAO was conducted under different conditions as electrolyte composition: Ca/P (0.3M/0.02M or 0.1M/0.03M) incorporated with/without Ag (0.62g/L) or Si (0.04M); and treatment duration (5 and 10min). Non-coated and sandblasted samples were used as controls. The surfaces morphology, topography and chemical composition were assessed to understand surface properties. ANOVA and Tukey׳s HSD tests were used (α=0.05). Biofunctional porous oxide layers were obtained. Higher Ca/P produced larger porous and harder coatings when compared to non-coated group (p<0.001), due to the presence of rutile crystalline structure. The total mass loss (Kwc), which includes mass loss due to wear (Kw) and that due to corrosion (Kc) were determined. The dominant wear regime was found for higher Ca/P groups (Kc/Kw≈0.05) and a mechanism of wear-corrosion for controls and lower Ca/P groups (Kc/Kw≈0.11). The group treated for 10min and enriched with Ag presented the lowest Kwc (p<0.05). Overall, MAO process was able to produce biofunctional oxide films with improved surface features, working as tribocorrosion resistant surfaces.