RESUMO
Casting of aluminum with different concentration of alloying elements such as Mg, Mn (similar to that in AA5083) with additional percentages of 0.1, 0.2 and 0.3% Ti, are carried out using graphite crucible. The as-cast microstructure is modified by hot rolling to a thickness of ~ 2 mm. Mechanical and metallurgical and characterization of heat-treated thin sheets are carried out using tensile testing, hardness measurement, metallography, image analysis and optical microscope. By increasing the Ti content, the results show grain refinement and increase in the formation of Al3Ti which reflected positively on the mechanical properties. Specifically, Ultimate tensile strength is increased from 260 MPa (0 wt% Ti) to 345 MPa (0.3 wt% Ti) when using water quenching, 32.6% improvement for air cooling, and 23.3% for furnace cooling. Electrochemical corrosion behavior of heat-treated water quenched, air cooled and furnace cooled samples were tested in 3.5% NaCl solution. The results show that the heat-treated alloys have very good resistance against corrosion, while by increasing the Ti content, the corrosion rate increases due to the grain refinement phenomena.