Effect of diphenyliodonium hexafluorphosphate in the yellowing and properties of experimental resin cements

Aim: The yellowing effect is undesirable and can occur in the dental restoration margins when light-cured resin cements containing camphorquinone as photoinitiator is used. This study aimed to evaluate the effect of diphenyliodonium hexafluorphosphate (DPI) in photoinitiator systems that contained different concentrations of camphorquinone (CQ) and dimethylamino ethyl benzoate (EDAB) on resin cements. Methods: A base (1:1) of bisphenol A diglycidyl methacrylate (BisGMA) and triethylene glycol dimethacrylate (TEGDMA) was obtained, and 60wt% of glass fillers was added. Eight formulations were obtained: RC1 (0.5mol% CQ / 1mol% EDAB), RC2 (0.5mol% CQ / 2mol% EDAB), RC3 (1mol% CQ / 1mol% EDAB), RC4 (1mol% CQ / 2mol% EDAB), and RC5 to RC8, which contained the same bases plus 0.5mol% DPI. Experimental resin cements were evaluated by the degree of conversion (DC), L*a*b* color analysis, water sorption (WS) and solubility (S), flexural strength, and Elastic Modulus. The data were analyzed by three-way ANOVA, Tukey's and Mann-Whitney tests (α = 0.05). Results: The combination of DPI and 0.5mol% CQ increased DC in RC6 and L* in RC5 without increasing the WS and a* b* values. CQ at 1mol% showed higher values of b* and lower values of a*, except for RC3. Groups with 2mol% EDAB showed higher DC. Conclusion: The addition of DPI reduces CQ, generating a decreased yellowing effect, while maintaining adequate properties in the resin cements, especially with 2mol% EDAB

Effect of diphenyliodonium hexafluorphosphate on resin cements containing different concentrations of ethyl 4-(dimethylamino)benzoate and 2-(dimethylamino)ethyl methacrylate as co-initiators.

OBJECTIVE: The present study evaluated the influence of diphenyliodonium hexafluorphosphate (DPI) combined with two different amines [ethyl 4-(dimethylamino)benzoate (EDAB) and 2-(dimethylamino)ethyl methacrylate (DMAEMA)] on the properties of model resin cements. METHODS: A comonomer base containing a 1:1 mass ratio of 2.2-bis[4-(2-hydroxy-3-methacryloxypropoxy)phenyl]propane (bis-GMA) and triethyleneglycol dimethacrylate (TEGDMA) was obtained, after which 1mol% of camphorquinone and 0.1mol% of hydroxyl butyl toluene were added to the comonomer blend. Concentrations of co-initiators varied at 0, 0.5 or 1mol% for DPI and in 1 or 2mol% for amines (DMAEMA or EDAB). Silanated Ba-Al-Si glass (60wt%) was added as filler. The combination of each amine and DPI concentration resulted in 12 formulations, which had the following properties analyzed: degree of conversion (DC), water sorption (Wsp) and solubility (Wsl), flexural strength (FS) and flexural modulus (Ef). Data for DC, FS and Ef were analyzed by two-way ANOVA and Tukey's test (α=0.05) and Wsp and Wsl by Kruskal-Wallis and Dunn tests (α=0.05). RESULTS: EDAB promoted a higher DC than did DMAEMA; however, DPI increased DC for all materials with DMAEMA. The physical properties of resin formulations containing EDAB were significantly better than those of groups with DMAEMA; however, DPI had a positive influence on the chemical and physical properties of the model resin cement containing DMAEMA, especially with higher concentrations of amine. SIGNIFICANCE: EDAB proved to be more reactive than DMAEMA, being less influenced by DPI. Resins containing a 1:2 CQ/amine ratio had better properties than those with 1:1.