Thermal Transport and Rheological Properties of Hybrid Nanofluids Based on Vegetable Lubricants.

Nanofluids based on vegetal oil with different wt.% of carbon nanotubes (CNT), hexagonal boron nitride (h-BN), and its hybrid (h-BN@CNT) were produced to investigate the effects of these nano-additives on the thermal conductivity and rheological properties of nanofluids. Stable suspensions of these oil/nanostructures were produced without the use of stabilizing agents. The dispersed nanostructures were investigated by SEM, EDS, XRD, and XPS, while the thermal conductivity and rheological characteristics were studied by a transient hot-wire method and steady-state flow tests, respectively. Increases in thermal conductivity of up to 39% were observed for fluids produced with 0.5 wt.% of the hybrid nanomaterials. As for the rheological properties, it was verified that both the base fluid and the h-BN suspensions exhibited Newtonian behavior, while the presence of CNT modified this tendency. This change in behavior is attributed to the hydrophobic character of both CNT and the base oil, while h-BN nanostructures have lip-lip "bonds", giving it a partial ionic character. However, the combination of these nanostructures was fundamental for the synergistic effect on the increase of thermal conductivity with respect to their counterparts.

Micro Scalable Graphene Oxide Productions Using Controlled Parameters in Bench Reactor.

The detailed study of graphene oxide (GO) synthesis by changing the graphite/oxidizing reagents mass ratios (mG/mROxi), provided GO nanosheets production with good yield, structural quality, and process savings. Three initial samples containing different amounts of graphite (3.0 g, 4.5 g, and 6.0 g) were produced using a bench reactor under strictly controlled conditions to guarantee the process reproducibility. The produced samples were analyzed by Raman spectroscopy, atomic force microscopy (AFM), x-ray diffraction (XDR), X-ray photoelectron spectroscopy (XPS), Fourier-transform infrared spectroscopy (FTIR) and thermogravimetry (TGA) techniques. The results showed that the major GO product comprised of nanosheets containing between 1-5 layers, with lateral size up to 1.8 µm. Therefore, it was possible to produce different batches of graphene oxide with desirable physicochemical characteristics, keeping the amount of oxidizing reagent unchanged. The use of different proportions (mG/mROxi) is an important strategy that provides to produce GO nanostructures with high structural quality and scale-up, which can be well adapted in medium-sized bench reactor.