Development and characterization of nanocapsules comprising dodecyltrimethylammonium chloride and κ-carrageenan.

The aim of this work was to develop and characterize a new type of nanocapsules. To this end, a nanoemulsion bearing an oily core (Miglyol 812) was obtained by spontaneous emulsification and stabilized by dodecyl-trimethylammonium chloride (DTAC), a commercial cationic surfactant; this nanoemulsion was coated with proportionally very small amounts of κ-carrageenan (at molar charge ratios of Z ≤ 0.0045) that interact predominantly by an electrostatic mechanism with the positively charged sites at the polar heads of DTAC at the nanoemulsion's surface to harness nanocapsules of average size ~250-330 nm and zeta potential (ζ) ranging from ~+80 to +7 mV. The potential application of the new type of developed nanosystems as drug delivery vehicles has yet to be investigated and fully realized.

Study of the interpolyelectrolyte reaction between chitosan and alginate: influence of alginate composition and chitosan molecular weight.

The interpolyelectrolyte reaction between chitosan (CHI) and alginate (ALG) was followed by conductimetry and potentiometry. Five chitosan samples, all with almost the same degree of N-acetylation (DA approximately 0.20) and molecular weights ranging from 5 x 10(3) to 2.5 x 10(5) Da were used. The polyelectrolyte complex was formed using alginate samples with three different M/G values (0.44, 1.31 and 1.96). The composition of the complex, Z (Z = [CHI]/[ALG]) resulted 0.70 +/- 0.02, independently of the molecular weight of chitosan and the composition of the alginate used. The degree of complexation was 0.51 with no dependence on the alginate composition.

Self-curing membranes of chitosan/PAA IPNs obtained by radical polymerization: preparation, characterization and interpolymer complexation.

Chitosan/polyacrylic acid I PN's were prepared by radical polymerization of acrylic acid, AA, activated at low temperature, in an aqueous/alcoholic chitosan dispersion. AA monomer to polymer conversion and membrane compositions were determined by elemental analysis and FTIR. Evidences of interpolyelectrolite complex formation were found from the FTIR spectra as well. The gravimetric measurements and the elemental analysis after some exhaustive PAA extraction support the existence of some PAA grafting on the reactive amine group of the chitosan. Swelling degree of the membranes is highly dependent on pH and composition, showing a higher swelling in membranes richer in AA and increased pH due to the breaking of interpolyelectrolite salt bonds.