Thermoradiationally Modified Polytetrafluoroethylene as a Basis for Membrane Fabrication: Resistance to Hydrogen Penetration, the Effect of Ion Treatment on the Chemical Structure and Surface Morphology, Evaluation of the Track Radius.

A study of the properties of thermoradiationally modified polytetrafluoroethylene and its importance for use as the basis of polymer membranes is presented. The hydrogen permeability of a TRM-PTFE film was studied in comparison with an original PTFE film, and showed a three-fold decrease in hydrogen permeability. Further, TRM-PTFE films were irradiated with accelerated Xe ions with an energy of 1 MeV with fluences from 1 × 108 to 1 × 1011. The changes induced by ion treatment were analyzed by infrared spectroscopy of disturbed total internal reflection (IR-ATR) and by atomic force microscopy (ASM). IR-ATR indicated the absence of destruction in the fluence range from 1 × 108 to 3 × 1010 cm-2 (in the area of isolated tracks) and the beginning of overlap of latent tracks on fluences from 3 × 1010 to 1 × 1011 cm-2. Topographic images with AFM showed layered lamellar structures that collapsed at a fluence of 108 cm-2. The destruction was accompanied by a decrease in roughness about seven times the size of the track core observed by the ASM method, fully corresponding to the value obtained on the basis of calculations using modeling in an SRIM program.

Structure of Polytetrafluoroethylene Modified by the Combined Action of γ-Radiation and High Temperatures.

By means of X-ray computed microtomography (XCMT), the existence of a developed porous structure with an average pore diameter of ~3.5 µm and pore content of ~1.1 vol.% has been revealed in unirradiated polytetrafluoroethylene (PTFE). It has been found that the combined action of gamma radiation (absorbed dose per PTFE of ~170 kGy) and high temperatures (327-350 °C) leads to the disappearance of the porous structure and the formation of several large pores with sizes from 30 to 50 µm in the bulk of thermal-radiation modified PTFE (TRM-PTFE). It has been established by X-ray diffraction (XRD) analysis that the thermal-radiation modification of PTFE leads to an increase in the interplanar spacings, the degree of crystallinity and the volume of the unit cell, as well as to a decrease in the size of crystals and the X-ray density of the crystalline phase in comparison with the initial polymer. It is assumed that the previously-established effect of improving the deformation-strength and tribological properties of the TRM-PTFE can be due not only to the radiation cross-linking of polymer chains but also to the disappearance of the pore system and to the ordering of the crystalline phase of PTFE.