RESUMO
INTRODUCTION: Dental erosion has a great effect on oral health, when diagnosed it is irreversible, this sets the importance of different preventive measures being investigated against dental erosion. AIM: This in vitro study aims to evaluate the effectiveness of silver diamine fluoride and Potassium iodide (SDF-KI) in comparison to casein phosphopeptide-amorphous calcium phosphate fluoride (CPP-ACPF) varnish, sodium fluoride (NaF) varnish, silver diamine fluoride (SDF) alone and deionized water as a control group in the prevention of dental erosion in primary teeth and assessing its staining effect. MATERIALS AND METHODS: Forty deciduous teeth enamel specimens were randomly allocated into the five study groups. Tested materials were applied. An erosive challenge was done by immersing the specimens in a citric acid-containing soft drink with pH 2.85, for 5 min, 4 times/day, for 5 days. Changes in surface microhardness, mineral loss, and color change were evaluated besides recording of the surface topography and surface roughness for selected specimens. RESULTS: The highest decrease in surface microhardness was recorded in the control group (-85.21 ± 10.60%), with a statistically significant difference (p = 0.002). SDF-KI group (-61.49 ± 21.08%) showed no statistically significant difference when compared to CPP-ACPF, NaF, and SDF groups. For calcium and phosphorous loss, control group was statistically significantly higher compared to the treatment groups (p = 0.003) and (p < 0.001) respectively, while there was no statistically significant difference between the tested treatment groups. The highest mean value for color change was recorded in SDF group (26.26 ± 10.31), followed by SDF-KI group (21.22 ± 12.87) with no statistically significant difference between groups. CONCLUSIONS: SDF-KI is as effective as CPP-ACPF, NaF varnishes and SDF in the prevention of dental erosion in primary teeth, there was no statistically significant difference regarding its staining potential.