Zn-Doped Calcium Magnesium Phosphate Bone Cement Based on Struvite and Its Antibacterial Properties.

The development of magnesium calcium phosphate bone cements (MCPCs) has garnered substantial attention. MCPCs are bioactive and biodegradable and have appropriate mechanical and antimicrobial properties for use in reconstructive surgery. In this study, the cement powders based on a (Ca + Mg)/P = 2 system doped with Zn2+ at 0.5 and 1.0 wt.% were obtained and investigated. After mixing with a cement liquid, the structural and phase composition, morphology, chemical structure, setting time, compressive strength, degradation behavior, solubility, antibacterial activities, and in vitro behavior of the cement materials were examined. A high compressive strength of 48 ± 5 MPa (mean ± SD) was achieved for the cement made from Zn2+ 1.0 wt.%-substituted powders. Zn2+ introduction led to antibacterial activity against Staphylococcus aureus and Escherichia coli strains, with an inhibition zone diameter of up to 8 mm. Biological assays confirmed that the developed cement is cytocompatible and promising as a potential bone substitute in reconstructive surgery.

Preparation and Investigation of Spherical Powder Made from Corrosion-Resistant 316L Steel with the Addition of 0.2% and 0.5% Ag.

The paper describes the production and study of spherical powder made from corrosion-resistant 316L steel with the addition of 0.2% and 0.5% Ag. The study of granulometric composition, morphology, fluidity and bulk density, phase composition, microhardness and impurity composition of the spherical powders was carried out. The study showed compliance of the spherical powders with the requirements for powders used for additive manufacturing. The fluidity of the powders was 17.9 s, and the bulk density was 3.76 g/cm3. The particles have a spherical shape with a minimum number of defects and an austenitic-ferritic structure. The study of the phase composition of ingots, wires and powders showed that the ingot structure of all samples consists of austenite. According to the results of studies of the phase composition of the wire, there is a decrease in γ-Fe and an increase in α-Fe and σ-NiCr in going from wire No. 1 to wire No. 3. According to the results of studies of the phase composition of the powder particles, there are three phases, γ-Fe, α-Fe, and Fe3O4. The study of microhardness showed a decrease in HV depending on the increase in silver. The hardness of the powder is lower than that of the ingot by 16-24% due to the presence of a ferritic phase in the powder. As a result of plasma spraying, an increase in residual oxygen is observed, which is associated with the oxidation of the melt during plasma dispersion. The amount of nitrogen and sulfur does not change, while the amount of carbon and hydrogen decreases, and the impurities content corresponds to the standards for corrosion-resistant steel. Qualitative and quantitative analysis of the silver content in the samples indicates that it was not affected by the stages involved in obtaining the spherical powder.

Investigation of Antibacterial Properties of Corrosion-Resistant 316L Steel Alloyed with 0.2 wt.% and 0.5 wt.% Ag.

The article is devoted to the study of melted ingots, plates rolled from them, and the resulting spherical powder made of corrosion-resistant 316L steel with the addition of 0.2 wt.% and 0.5 wt.% Ag. The study of antibacterial properties, microstructure, and distribution of silver concentrations, as well as qualitative analysis of silver content was carried out. The optimal mode of homogenization annealing of the ingot was 1050 °C for 9 h, which leads to the formation of an austenitic structure. It is shown that the addition of a small amount of silver does not affect the formation of the austenitic structure and silver is distributed evenly throughout the volume of the ingot. The austenitic structure also prevails in the plates after rolling. Silver is distributed evenly throughout the entire volume of the plate. It is noted that the addition of 0.2 wt.% Ag does not affect the strength, elongation, and microhardness of steel, and the addition of 0.5 wt.% Ag does not significantly reduce the strength of steel, however, all samples meet the mechanical characteristics according to the ASTM A240 standard. The qualitative chemical composition of samples made of corrosion-resistant steels was confirmed by X-ray fluorescence analysis methods. By the method of energy-dispersion analysis, the presence of a uniform distribution of silver over the entire volume of the powder particle was determined. The particles have a spherical shape with a minimum number of defects. The study of the antibacterial activity of plates and powder shows the presence of a clear antibacterial effect (bacteria of the genus Xanthomonas campestris, Erwinia carotovora, Pseudomonas marginalis, Clavibacter michiganensis) in samples No. 2 and No. 3 with the addition of 0.2 wt.% and 0.5 wt.% Ag.

Bacteriostatic and Cytotoxic Properties of Composite Material Based on ZnO Nanoparticles in PLGA Obtained by Low Temperature Method.

A low-temperature technology was developed for producing a nanocomposite based on poly (lactic-co-glycolic acid) and zinc oxide nanoparticles (ZnO-NPs), synthesized by laser ablation. Nanocomposites were created containing 0.001, 0.01, and 0.1% of zinc oxide nanoparticles with rod-like morphology and a size of 40-70 nm. The surface of the films from the obtained nanomaterial was uniform, without significant defects. Clustering of ZnO-NPs in the PLGA matrix was noted, which increased with an increase in the concentration of the dopant in the polymer. The resulting nanomaterial was capable of generating reactive oxygen species (ROS), such as hydrogen peroxide and hydroxyl radicals. The rate of ROS generation increased with an increase in the concentration of the dopant. It was shown that the synthesized nanocomposite promotes the formation of long-lived reactive protein species, and is also the reason for the appearance of a key biomarker of oxidative stress, 8-oxoguanine, in DNA. The intensity of the process increased with an increase in the concentration of nanoparticles in the matrix. It was found that the nanocomposite exhibits significant bacteriostatic properties, the severity of which depends on the concentration of nanoparticles. In particular, on the surface of the PLGA-ZnO-NPs composite film containing 0.001% nanoparticles, the number of bacterial cells was 50% lower than that of pure PLGA. The surface of the composite is non-toxic to eukaryotic cells and does not interfere with their adhesion, growth, and division. Due to its low cytotoxicity and bacteriostatic properties, this nanocomposite can be used as coatings for packaging in the food industry, additives for textiles, and also as a material for biomedicine.

Obtaining a Wire of Biocompatible Superelastic Alloy Ti-28Nb-5Zr.

Using the methods of electric arc melting, intermediate heat treatments, and consecutive intensive plastic deformation, a Ti-Nb-Zr alloy wire with a diameter of 1200 µm was obtained with a homogeneous chemical and phase (ß-Ti body-centered crystal lattice) composition corresponding to the presence of superelasticity and shape memory effect, corrosion resistance and biocompatibility. Perhaps the wire structure is represented by grains with a nanoscale diameter. For the wire obtained after stabilizing annealing, the proof strength Rp0.2 is 635 MPa, tensile strength is 840 MPa and Young's modulus is 22 GPa, relative elongation is 6.76%. No toxicity was detected. The resulting wire is considered to be promising for medical use.

Development of a Biocompatible PLGA Polymers Capable to Release Thrombolytic Enzyme Prourokinase.

The novelty of the work lies in the creation and study of the physical and biological properties of biodegradable polymer coatings for stents based on poly(lactic-co-glycolic acid) (PLGA). Polymer coatings are capable of prolonged and directed release of molecules with a high molecular weight, in particular, protein molecules of prourokinase (m.w. 54 kDa). A technology has been developed to create coatings having a relative elongation of 40% to 165% and a tensile strength of 25-65 MPa. Coatings are biodegradable; the rate of degradation of the polymer in an isotonic solution varies in the range of 0.05%-1.0% per day. The created coatings are capable of controlled release of the protein of prourokinase, while about 90% of the molecules of prourokinase retain their enzymatic activity. The rate of release of prourokinase can vary from 0.01 to 0.08 mg/day/cm2. Coatings do not have a short-term toxic effect on mammalian cells. The mitotic index of cells growing on coatings is approximately 1.5%. When implanting the developed polymers in animals in the postoperative period, there are no complications. Histological examination did not reveal pathological processes. When implanting individual polymers 60 days after surgery, only traces of PLGA are detected. Thus, a biodegradable composite mechanically resistant polymer capable of prolonged release of the high molecular weight prourokinase enzyme has been developed.

Polylactide-Based Stent Coatings: Biodegradable Polymeric Coatings Capable of Maintaining Sustained Release of the Thrombolytic Enzyme Prourokinase.

The novelty of the study is the development, creation, and investigation of biodegradable polymeric membranes based on polylactide, that are capable of directed release of large molecular weight biomolecules, particularly, prourokinase protein (MW = 46 kDa). Prourokinase is a medication with significant thrombolytic activity. The created membranes possess the required mechanical properties (relative extension value from 2% to 10%, tensile strength from 40 to 85 MPa). The membranes are biodegradable, but in the absence of living cells in a water solution they decompose by less than 10% in half a year. The created membranes are capable of controlled prourokinase release into intercellular space, and the total enzymatic activity of prourokinase does not decrease by more than 12%. The daily release of prourokinase from one square centimeter of the membrane ranges from 1 to 40 µg per day depending on the technique of membrane preparation. The membranes have no acute toxic effect on cells accreting these surfaces de novo. The number of viable cells is at least 96%-97% of the overall cell count. The mitotic index of the cells growing on the surface of the polymeric films comprised around 1.5%. Histological examination did not reveal any disorders in tissues of the animals after the implantation of polymer membranes based on polylactide, both alone and as components of stent cover. Implantation of stents covered with prourokinase-containing polymers led to the formation of a mature connective tissue capsule that is thicker than in the case of uncovered stents. Thus, various polylactide-based biodegradable polymeric membranes possessing the required mechanical properties and capable of prolonged and directed release of prourokinase macromolecules are developed and investigated in the study.

Biocompatibility of new materials based on nano-structured nitinol with titanium and tantalum composite surface layers: experimental analysis in vitro and in vivo.

A technology for obtaining materials from nanostructured nitinol with titanium- or tantalum-enriched surface layers was developed. Surface layers enriched with titanium or tantalum were shown to provide a decrease in the formation of reactive oxygen species and long-lived protein radicals in comparison to untreated nitinol. It was determined that human peripheral vessel myofibroblasts and human bone marrow mesenchymal stromal cells grown on nitinol bases coated with titanium or tantalum-enriched surface layers exhibit a nearly two times higher mitotic index. Response to implantation of pure nitinol, as well as nano-structure nitinol with titanium or tantalum-enriched surface layers, was expressed though formation of a mature uniform fibrous capsule peripherally to the fragment. The thickness of this capsule in the group of animals subjected to implantation of pure nitinol was 1.5 and 3.0-fold greater than that of the capsule in the groups implanted with nitinol fragments with titanium- or tantalum-enriched layers. No signs of calcinosis in the tissues surrounding implants with coatings were observed. The nature and structure of the formed capsules testify bioinertia of the implanted samples. It was shown that the morphology and composition of the surface of metal samples does not alter following biological tests. The obtained results indicate that nano-structure nitinol with titanium or tantalum enriched surface layers is a biocompatible material potentially suitable for medical applications.