Fatigue behaviour of load-bearing polymeric bone scaffolds: A review.

Bone scaffolds play a crucial role in bone tissue engineering by providing mechanical support for the growth of new tissue while enduring static and fatigue loads. Although polymers possess favourable characteristics such as adjustable degradation rate, tissue-compatible stiffness, ease of fabrication, and low toxicity, their relatively low mechanical strength has limited their use in load-bearing applications. While numerous studies have focused on assessing the static strength of polymeric scaffolds, little research has been conducted on their fatigue properties. The current review presents a comprehensive study on the fatigue behaviour of polymeric bone scaffolds. The fatigue failure in polymeric scaffolds is discussed and the impact of material properties, topological features, loading conditions, and environmental factors are also examined. The present review also provides insight into the fatigue damage evolution within polymeric scaffolds, drawing comparisons to the behaviour observed in natural bone. Additionally, the effect of polymer microstructure, incorporating reinforcing materials, the introduction of topological features, and hydrodynamic/corrosive impact of body fluids in the fatigue life of scaffolds are discussed. Understanding these parameters is crucial for enhancing the fatigue resistance of polymeric scaffolds and holds promise for expanding their application in clinical settings as structural biomaterials. STATEMENT OF SIGNIFICANCE: Polymers have promising advantages for bone tissue engineering, including adjustable degradation rates, compatibility with native bone stiffness, ease of fabrication, and low toxicity. However, their limited mechanical strength has hindered their use in load-bearing scaffolds for clinical applications. While prior studies have addressed static behaviour of polymeric scaffolds, a comprehensive review of their fatigue performance is lacking. This review explores this gap, addressing fatigue characteristics, failure mechanisms, and the influence of parameters like material properties, topological features, loading conditions, and environmental factors. It also examines microstructure, reinforcement materials, pore architectures, body fluids, and tissue ingrowth effects on fatigue behaviour. A significant emphasis is placed on understanding fatigue damage progression in polymeric scaffolds, comparing it to natural bone behaviour.

Influence of Three-Dimensional Printing Parameters on Compressive Properties and Surface Smoothness of Polylactic Acid Specimens.

While the mechanical performance of fused filament fabrication (FFF) parts has been extensively studied in terms of the tensile and bending strength, limited research accounts for their compressive performance. This study investigates the effect of four process parameters (layer height, extrusion width, nozzle temperature, and printing speed) on the compressive properties and surface smoothness of FFF parts made of Polylactic Acid (PLA). The orthogonal Taguchi method was employed for designing the experiments. The surface roughness and compressive properties of the specimens were then measured and optimized using the analysis of variance (ANOVA). A microscopic analysis was also performed to identify the failure mechanism under static compression. The results indicated that the layer height had the most significant influence on all studied properties, followed by the print speed in the case of compressive modulus, hysteresis loss, and residual strain; extrusion width in the case of compressive strength and specific strength; and nozzle temperature in the case of toughness and failure strain. The optimal design for both high compressive properties and surface smoothness were determined as a 0.05 mm layer height, 0.65 mm extrusion width, 205 °C nozzle temperature, and 70 mm/s print speed. The main failure mechanism observed by SEM analysis was delamination between layers, occurring at highly stressed points near the stitch line of the PLA prints.