Effect of a novel sterilization method on biomechanical properties of soft tissue allografts.

PURPOSE: Evaluate allograft tissue commonly used in soft tissue reconstruction to determine whether stiffness and strength were significantly altered after grafts were treated with different sterilization methods. Unprocessed, irradiated, and grafts treated with supercritical CO2 were compared. METHODS: Thirty-eight anterior or posterior tibialis tendons were obtained from a tissue bank (Allograft Innovations, Gainesville, FL). Group I was unprocessed, group II was sterilized with gamma irradiation (20-28 kGy), and group III was sterilized with supercritical CO2. The grafts were pretensioned to 89 N for 300 s. Specimens were then loaded from 50 to 300 N at 0.5 Hz for 250 cycles before being loaded to failure at 50 mm/min. Dependent variables were compared between sterilization groups with one-way ANOVA (P < 0.05) and equivalence trial. RESULTS: There was no significant difference in load to failure or failure stress among groups I, II, and III. Group III resulted in 27-36 % lower stiffness than group I and II. This difference was significant at 1, 10, 50, 100, and 250 cycles. There was no significant difference in stiffness between group I and group II. CONCLUSION: The two sterilization methods tested in this study do not affect allograft strength. The supercritical CO2 sterilization method resulted in significantly lower stiffness than unprocessed and irradiated allografts. However, the stiffness and strength of all groups tested were greater than that of published values of the native intact anterior cruciate ligament (ACL). This study provides previously unpublished mechanical test data on a new sterilization technique that will assist surgeons to decide which allograft to use in ACL reconstruction surgery. LEVEL OF EVIDENCE: III.

Bone strength and related traits in HcB/Dem recombinant congenic mice.

Fracture susceptibility depends jointly on bone mineral content (BMC), gross bone anatomy, and bone microarchitecture and quality. Overall, it has been estimated that 50-70% of bone strength is determined genetically. Because of the difficulty of performing studies of the genetics of bone strength in humans, we have used the HcB/Dem series of recombinant congenic (RC) mice to investigate this phenotype. We performed a comprehensive phenotypic analysis of the HcB/Dem strains including morphological analysis of long bones, measurement of ash percentage, and biomechanical testing. Body mass, ash percentage, and moment of inertia each correlated moderately but imperfectly with biomechanical performance. Several chromosome regions, on chromosomes 1, 2, 8, 10, 11, and 12, show sufficient evidence of linkage to warrant closer examination in further crosses. These studies support the view that mineral content, diaphyseal diameter, and additional nonmineral material properties contributing to overall bone strength are controlled by distinct sets of genes. Moreover, the mapping data are consistent with the existence of pleiotropic loci for bone strength-related phenotypes. These findings show the importance of factors other than mineral content in determining skeletal performance and that these factors can be dissected genetically.

A physical, chemical, and mechanical study of lumbar vertebrae from normal, ovariectomized, and nandrolone decanoate-treated cynomolgus monkeys (Macaca fascicularis).

Ovariectomized cynomolgus monkeys have previously been investigated as a nonhuman primate model of postmenopausal osteoporosis (Jerome et al., Bone Miner 9:527-540; 1994). In the present study, Fourier transform infrared microspectroscopy (FTIRM) was used to verify that differences in bone mineral quality and quantity in the vertebrae of mature intact (INT) and ovariectomized (ovx) monkeys were analogous to those seen in osteoporotic and nondiseased human bones. FTIRM spectra were acquired from 15 trabeculae per vertebra from three ovx and three INT adult monkeys (mean age 8 years). These spectra were compared with those of both trabecular and previously reported osteonal bone obtained from 3 "normal" and 11 postmenopausal osteoporotic human subjects. While variations in the mineral:matrix ratio (mineral content), carbonate:phosphate ratio, and crystallinity are typical for trabecular bone from iliac crests of normal human subjects, the values of these parameters were relatively static for trabecular bone from postmenopausal osteoporotic human subjects. In general, trabecular bone from postmenopausal osteoporotic human subjects exhibited decreased mineral content (1.0 +/- 0.5 vs. 2.9 +/- 0.6), increased crystallinity, and increased carbonate:phosphate relative to controls. Similarly, trabecular bone from ovariectomized monkeys exhibited lower mineral content (5.8 +/- 0.2) compared with the INT group (6.2 +/- 0.2; p

Interference screw position and hamstring graft location for anterior cruciate ligament reconstruction.

Anterior cruciate ligament reconstruction with hamstring tendon graft and interference screw fixation has recently been considered. Concerns for the use of interference screws with soft tissue grafts include damage to the graft during screw insertion, decreased fixation strength, and a decrease in the bone-tendon contact area for healing within the tunnel when the screw is placed in an eccentric position. This last concern could be addressed by placing the interference screw centrally between the four limbs of the hamstring graft. The purpose of this study was to determine the mode of failure, the pullout force, and graft slippage before graft fixation failure of hamstring tendons fixed with an interference screw positioned eccentrically in relation to the hamstring tendons verses an interference screw positioned centrally between the four graft limbs. The semitendinosus and gracilis tendons were harvested from six, fresh cadaveric specimens. Each tendon was divided into two segments of equal length. Both the semitendinosus and gracilis tendon segments were looped to form four strands. The specimens were then fixed with a bioabsorbable interference screw in the two different positions and pulled from a standardized polyurethane foam. All tendons in both groups failed by pulling out from between the interference screw and tunnel, regardless of the screw position. No tendon was cut by the screw in either group. There was no significant difference between the forces required to produce specific amounts of graft slippage between the two fixation techniques tested. There was no significant difference between the average total slippage at maximum pullout, 11.8 mm for the screw placed in the eccentric position and 13.7 mm for the screw placed in the central position. The maximum pullout force averaged 265.3 N for the screw placed in the eccentric position, and 244.7 N for the screw placed in the central position; these values were not significantly different. Placement of the interference screw in the central position did not compromise strength and it improves graft contact within the bone tunnel. Interference screw fixation, when applied against a bone plug, has been shown to consistently have a pullout force of more than 400 N.