Effects of Amphiphilic Polypeptoid Side Chains on Polymer Surface Chemistry and Hydrophilicity.

Polymers are commonly used in applications that require long-term exposure to water and aqueous mixtures, serving as water purification membranes, marine antifouling coatings, and medical implants, among many other applications. Because polymer surfaces restructure in response to the surrounding environment, in situ characterization is crucial for providing an accurate understanding of the surface chemistry under conditions of use. To investigate the effects of surface-active side chains on polymer surface chemistry and resultant interactions with interfacial water (i.e., water sorption), we present synchrotron ambient pressure X-ray photoelectron spectroscopy (APXPS) studies performed on poly(ethylene oxide) (PEO)- and poly(dimethylsiloxane) (PDMS)-based polymer surfaces modified with amphiphilic polypeptoid side chains, previously demonstrated to be efficacious in marine fouling prevention and removal. The polymer backbone and environmental conditions were found to affect polypeptoid surface presentation: due to the surface segregation of its fluorinated polypeptoid monomers under vacuum, the PEO-peptoid copolymer showed significant polypeptoid content in both vacuum and hydrated conditions, while the modified PDMS-based copolymer showed increased polypeptoid content only in hydrated conditions due to the hydrophilicity of the ether monomers and polypeptoid backbone. Polypeptoids were found to bind approximately 2.8 water molecules per monomer unit in both copolymers, and the PEO-peptoid surface showed substantial water sorption that suggests a surface with a more diffuse water/polymer interface. This work implies that side chains are ideal for tuning water affinity without altering the base polymer composition, provided that surface-driving groups are present to ensure activity at the interface. These types of systematic modifications will generate novel polymers that maximize bound interfacial water and can deliver surface-active groups to the surface to improve the effectiveness of polymer materials.

Thromboresistance of Silicones Modified with PEO-Silane Amphiphiles.

The antifouling properties of poly(ethylene oxide) (PEO)-silane amphiphiles as surface-modifying additives (SMAs) in a condensation cure silicone have been previously demonstrated against simple protein solutions. Comprising an oligo(dimethylsiloxane) tether (m = 13 or 30) and PEO segment (n = 8), sustained protein resistance was achieved even in the absence of a cross-linkable triethoxysilane group, particularly when comprising the longer tether. To probe their potential for thromboresistance, PEO-silane amphiphile SMAs were used to bulk-modify silicones and evaluated for adhesion resistance against whole human blood under both static and dynamic conditions. Both a cross-linkable (XL diblock, m = 13) and a non-cross-linkable (Diblock, m = 30) SMA were evaluated at various concentrations (5-50 µmol SMA/g silicone) in a condensation cure silicone. Under static conditions, silicones modified with either SMA at concentrations of 10 µmol/g or greater were effective in reducing adhesion of human fibrinogen and platelets. Dynamic testing further showed that modified silicones were able to reduce protein adsorption and thrombus formation. This occurred at 5 and 10 µmol/g for silicones modified with XL diblock, m = 13 and Diblock, m = 30 SMAs, respectively. Combined, these results indicate the effectiveness of PEO-silane amphiphiles as SMAs in silicone for improved thromboresistance.

Antifouling amphiphilic silicone coatings for dairy fouling mitigation on stainless steel.

Pasteurization of dairy products is plagued by fouling, which induces significant economic, environmental and microbiological safety concerns. Herein, an amphiphilic silicone coating was evaluated for its efficacy against fouling by a model dairy fluid in a pilot pasteurizer and against foodborne bacterial adhesion. The coating was formed by modifying an RTV silicone with a PEO-silane amphiphile comprised of a PEO segment and flexible siloxane tether ([(EtO)3Si-(CH2)2-oligodimethylsiloxanem-block-(OCH2CH2)n-OCH3]). Contact angle analysis of the coating revealed that the PEO segments were able to migrate to the aqueous interface. The PEO-modified silicone coating applied to pretreated stainless steel was exceptionally resistant to fouling. After five cycles of pasteurization, these coated substrata were subjected to a standard clean-in-place process and exhibited a minor reduction in fouling resistance in subsequent tests. However, the lack of fouling prior to cleaning indicates that harsh cleaning is not necessary. PEO-modified silicone coatings also showed exceptional resistance to adhesion by foodborne pathogenic bacteria.

Antifouling silicones based on surface-modifying additive amphiphiles.

Surface modifying additives (SMAs), which may be readily blended into silicones to improve anti-fouling behavior, must have excellent surface migration potential and must not leach into the aqueous environment. In this work, we evaluated the efficacy of a series of poly(ethylene oxide) (PEO)-based SMA amphiphiles which varied in terms of crosslinkability, siloxane tether length (m) and diblock versus triblock architectures. Specifically, crosslinkable, diblock PEO-silane amphiphiles with two oligodimethylsiloxane (ODMS) tether lengths [(EtO)3Si-(CH2)3-ODMS m -PEO8, m = 13 and 30] were compared to analogous non-crosslinkable, diblock (H-Si-ODMS m -PEO8) and triblock (PEO8-ODMS m -PEO8) SMAs. Prior to water conditioning, while all modified silicone coatings exhibited a high degree of water-driven surface restructuring, that prepared with the non-crosslinkable diblock SMA (m = 13) was the most hydrophilic. After conditioning, all modified silicone coatings were similarly hydrophilic and remained highly protein resistant, with the exception of PEO8-ODMS 30 -PEO8. Notably, despite twice the PEO content, triblock SMAs were not superior to diblock SMAs. For diblock SMAs, it was shown that water uptake and leaching were also similar whether or not the SMA was crosslinkable.

Protein resistance efficacy of PEO-silane amphiphiles: Dependence on PEO-segment length and concentration.

UNLABELLED: In contrast to modification with conventional PEO-silanes (i.e. no siloxane tether), silicones with dramatically enhanced protein resistance have been previously achieved via bulk-modification with poly(ethylene oxide) (PEO)-silane amphiphiles α-(EtO)3Si(CH2)2-oligodimethylsiloxane13-block-PEOn-OCH3 when n=8 and 16 but not when n=3. In this work, their efficacy was evaluated in terms of optimal PEO-segment length and minimum concentration required in silicone. For each PEO-silane amphiphile (n=3, 8, and 16), five concentrations (5, 10, 25, 50, and 100µmol per 1g silicone) were evaluated. Efficacy was quantified in terms of the modified silicones' abilities to undergo rapid, water-driven surface restructuring to form hydrophilic surfaces as well as resistance to fibrinogen adsorption. Only n=8 and 16 were effective, with a lower minimum concentration in silicone required for n=8 (10µmol per 1g silicone) versus n=16 (25µmol per 1g silicone). STATEMENT OF SIGNIFICANCE: Silicone is commonly used for implantable medical devices, but its hydrophobic surface promotes protein adsorption which leads to thrombosis and infection. Typical methods to incorporate poly(ethylene oxide) (PEO) into silicones have not been effective due to the poor migration of PEO to the surface-biological interface. In this work, PEO-silane amphiphiles - comprised of a siloxane tether (m=13) and variable PEO segment lengths (n=3, 8, 16) - were blended into silicone to improve its protein resistance. The efficacy of the amphiphiles was determined to be dependent on PEO length. With the intermediate PEO length (n=8), water-driven surface restructuring and resulting protein resistance was achieved with a concentration of only 1.7wt%.