The Effect of Extender Particle Size on the Glass Transition Temperature of Model Epoxy Coatings.

Inorganic extenders are important constituents of 2K thermosetting epoxy-amine coatings and their physical properties play an important role in the final properties of the organic coatings. The effects of extender particle size and loading (i.e., the amount of extender in component A or in the total formulation) on the glass transition temperature (Tg) of model epoxy-amine coatings were studied in this work with differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA). The obtained results show that the particle size and loading of feldspar particles (from 25 wt% to 70 wt%) do not influence the glass transition temperature of the model epoxy-amine coating significantly. In general, the smaller the particle size the lower the glass transition temperature of the coating but this depression in Tg seems negligible when seen relative to the change in extender particle size. Similar observations are reported for two model coatings having the same lamda (Λ) value but with silica of very different particle sizes (i.e., nanosilica and micron sized silica).

The design of a bipodal bis(pentafluorophenoxy)aluminate supported on silica as an activator for ethylene polymerization using surface organometallic chemistry.

A new class of well-defined activating supports for olefin polymerization was obtained via the surface organometallic chemistry approach. High activities in slurry polymerization of ethylene along with industrial-grade physical properties of the resulting polyethylene were obtained when these activators were combined with metallocene complexes in the presence of triisobutylaluminium.