Temperature and external strain sensing with metal-embedded optical fiber sensors for structural health monitoring.

An optical fiber with both temperature and strain fiber Bragg grating sensors were embedded into an aluminum cast structure during the casting process. Temperature and strain calibrations were carried out respectively for the metal-embedded sensors. Temperature and external strain decoupling was further demonstrated in a temperature range from 25 to 80 °C and an external strain range from 0 to ∼110 µÉ›. With the interpolated temperature measured by two temperature sensors at different positions, the external strain could be decoupled from temperature and thermal strain at the strain sensor. The temperature and external strain values obtained from our embedded optical fiber sensors agreed well with reference values, revealing the good performance of the metal-embedded optical fiber sensors. The difference between the measured values and the reference values are within ±5 µÉ› for external strain and ±1 °C for temperature. With only a single fiber, the in-situ temperature and external strain information in the aluminum structure can be monitored in real time, representing an important step towards fiber-optic smart casts. Our investigation demonstrates that embedded optical fiber sensors can be a promising method for structural health monitoring of metallic structures.

Fiber Bragg Sensors Embedded in Cast Aluminum Parts: Axial Strain and Temperature Response.

In this study, the response of fiber Bragg gratings (FBGs) embedded in cast aluminum parts under thermal and mechanical load were investigated. Several types of FBGs in different types of fibers were used in order to verify general applicability. To monitor a temperature-induced strain, an embedded regenerated FBG (RFBG) in a cast part was placed in a climatic chamber and heated up to 120 ∘C within several cycles. The results show good agreement with a theoretical model, which consists of a shrink-fit model and temperature-dependent material parameters. Several cast parts with different types of FBGs were machined into tensile test specimens and tensile tests were executed. For the tensile tests, a cyclic procedure was chosen, which allowed us to distinguish between the elastic and plastic deformation of the specimen. An analytical model, which described the elastic part of the tensile test, was introduced and showed good agreement with the measurements. Embedded FBGs - integrated during the casting process - showed under all mechanical and thermal load conditions no hysteresis, a reproducible sensor response, and a high reliable operation, which is very important to create metallic smart structures and packaged fiber optic sensors for harsh environments.

Evaluation of Strain Transition Properties between Cast-In Fibre Bragg Gratings and Cast Aluminium during Uniaxial Straining.

Current testing methods are capable of measuring strain near the surface on structural parts, for example by using strain gauges. However, stress peaks often occur within the material and can only be approximated. An alternative strain measurement incorporates fibre-optical strain sensors (Fiber Bragg Gratings, FBG) which are able to determine strains within the material. The principle has already been verified by using embedded FBGs in tensile specimens. The transition area between fibre and aluminium, however, is not yet properly investigated. Therefore, strains in tensile specimens containing FBGs were measured by neutron diffraction in gauge volumes of two different sizes around the Bragg grating. As a result, it is possible to identify and decouple elastic and plastic strains affecting the FBGs and to transfer the findings into a fully descriptive FE-model of the strain transition area.We thus accomplished closing the gap between the external load and internal straining obtained from cast-in FBG and generating valuable information about the mechanisms within the strain transition area.It was found that the porosity within the casting has a significant impact on the stiffness of the tensile specimen, the generation of excess microscopic tensions and thus the formation of permanent plastic strains, which are well recognized by the FBG. The knowledge that FBG as internal strain sensors function just as well as common external strain sensors will now allow for the application of FBG in actual structural parts and measurements under real load conditions. In the future, applications for long-term monitoring of cast parts will also be enabled and are currently under development.